This work focused on the zinc powder coated with Y(OH)3 microparticles by means of ultrasonic immersion for performance improvement of zinc electrodes in alkaline battery systems.Scanning electron microscopy and other...This work focused on the zinc powder coated with Y(OH)3 microparticles by means of ultrasonic immersion for performance improvement of zinc electrodes in alkaline battery systems.Scanning electron microscopy and other characterization techniques were applied to examine the influence of the ultrasonic power on the sonochemical growth of Y(OH)3 microparticles in direct contact with zinc powder.Electrochemical properties of zinc electrodes containing Y(OH)3 microparticles were discussed through the measurement...展开更多
Zinc powder electrodeposited from suspension bath has higher corrosion resistance than that from conventional bath. The results of X ray, SEM and EIS (Electrochem. Impedance Spectrum) indicated that the microstructur...Zinc powder electrodeposited from suspension bath has higher corrosion resistance than that from conventional bath. The results of X ray, SEM and EIS (Electrochem. Impedance Spectrum) indicated that the microstructures of zinc powder could be modified according to the kinds of suspension species. Suspension of TiO 2, SiO 2, In 2O 3, PbO 2 and SnO 2 could obviously improve the polarization resistance of zinc powder anodes in 5 mol/L KOH solution.展开更多
Zinc oxide, which has photocatalytic activity, is used as white pigment for cosmetics. A certain degree of sebum on the skin is decomposed by ultraviolet radiation in sunlight. In this work, zinc oxide was shaken with...Zinc oxide, which has photocatalytic activity, is used as white pigment for cosmetics. A certain degree of sebum on the skin is decomposed by ultraviolet radiation in sunlight. In this work, zinc oxide was shaken with phosphoric acid to synthesize a white pigment for cosmetics. Zinc oxide was set with 0.1 mol/L of phosphoric acid at P/Zn = 1/1 and 1/2, and then shaking in hot water for 1 h. The chemical composition, powder properties, photocatalytic activity, color phase, and smoothness of the obtained powder were studied. The P/Zn ratio in preparation had an effect on the reaction between phosphoric acid and zinc oxide. The photocatalytic activity of zinc oxide was inhibited by phosphoric acid treatment. The obtained samples had enough high reflectance at the visible light region.展开更多
基金supported by the Innovation Foundation of BUAA for Ph. D Graduates Provided by Beihang University in China
文摘This work focused on the zinc powder coated with Y(OH)3 microparticles by means of ultrasonic immersion for performance improvement of zinc electrodes in alkaline battery systems.Scanning electron microscopy and other characterization techniques were applied to examine the influence of the ultrasonic power on the sonochemical growth of Y(OH)3 microparticles in direct contact with zinc powder.Electrochemical properties of zinc electrodes containing Y(OH)3 microparticles were discussed through the measurement...
文摘Zinc powder electrodeposited from suspension bath has higher corrosion resistance than that from conventional bath. The results of X ray, SEM and EIS (Electrochem. Impedance Spectrum) indicated that the microstructures of zinc powder could be modified according to the kinds of suspension species. Suspension of TiO 2, SiO 2, In 2O 3, PbO 2 and SnO 2 could obviously improve the polarization resistance of zinc powder anodes in 5 mol/L KOH solution.
文摘Zinc oxide, which has photocatalytic activity, is used as white pigment for cosmetics. A certain degree of sebum on the skin is decomposed by ultraviolet radiation in sunlight. In this work, zinc oxide was shaken with phosphoric acid to synthesize a white pigment for cosmetics. Zinc oxide was set with 0.1 mol/L of phosphoric acid at P/Zn = 1/1 and 1/2, and then shaking in hot water for 1 h. The chemical composition, powder properties, photocatalytic activity, color phase, and smoothness of the obtained powder were studied. The P/Zn ratio in preparation had an effect on the reaction between phosphoric acid and zinc oxide. The photocatalytic activity of zinc oxide was inhibited by phosphoric acid treatment. The obtained samples had enough high reflectance at the visible light region.