Phase Transformation of Amorphous Calcium Carbonate to Single-Crystalline Aragonite with Macroscopic Layered Structure in the Presence of Egg White Protein and Zinc Ion

Highly oriented calcium carbonate lamellas are exquisite structure produced by biomineralization. Strategies mimicking nature have been developed to synthesize inorganic materials with excellent structures and optimal properties. In our strategy, egg white protein and zinc ion were employed in the solution to induce the crystallization of calcium carbonate, resulting in the macroscopic aragonite laminate with an average length of 1.5 mm, which was comprised of single-crystalline tablets. During the crystallization at initial stage, it was found that the particles displayed the characteristics of amorphous calcium carbonate, which was then transformed into the sophisticated structured aragonite through a multistage assembly process. The rebuilt nacre structure in vitro was achieved owing to the synergistic effects of egg white protein and zinc ion.

锌白铜带材表面高温发黄问题的研究

锌白铜具有优良的电磁屏蔽性能,被广泛应用于电磁屏蔽罩,但在实际使用过程中,需要通过高温钎焊实现与其他部件的连接,在钎焊过程中往往会出现高温发黄现象,影响产品的美观及使用特性。通过研究锌白铜高温发黄机理和清洗工艺、研磨工艺、工作辊表面粗糙度以及成品退火工艺对高温发黄的影响,解决了锌白铜高温发黄问题。结果表明,采用合适的清洗介质浓度和研磨刷转速、较低的工作辊表面粗糙度及合适的成品退火工艺,可以保证锌白铜在300℃保温5 min后不发黄;将该技术推广应用于铜镍锡、铜镍硅和铜锡磷等需要高温钎焊的合金中,同样也可解决高温钎焊发黄问题。

热镀锌镀层白条缺陷研究及控制

针对热镀锌产品镀层白条缺陷,研究了其形成机理、影响因素和控制措施。结果表明,白条缺陷由炉鼻子内锌灰黏附于带钢表面而形成,其成分是Zn和ZnO。白条缺陷影响因素主要有炉鼻子密封性、露点、带钢入锌锅温度、锌锅温度和排锌灰效果。通过对上述因素进行控制及优化,有效地消除白条缺陷,达到家电用钢表面质量需求。

铜铅锌冶炼固废协同处理及有价金属综合回收

针对我国铜、铅和锌冶炼所产工业固废产量高、存量大、种类繁杂、成分复杂、难处理等突出问题,详细介绍了我国铜、铅和锌冶炼所产工业固废的种类及处置情况,包括铜冶炼渣、渣选尾矿、白烟尘、烟化炉渣、镉烟尘、锌浸出渣、锌挥发窑渣等标志性大宗工业固废的处理工艺及新技术,并提出了铜、铅、锌冶炼固废协同处理的新技术路线。结合铜、铅和锌冶炼所产工业固废的种类及处置特点,建立铜、铅、锌综合冶炼基地或产业园,协同处理铜、铅和锌冶炼所产工业固废,可有效提高有价金属元素的综合回收率与利用效率,降低综合冶炼成本。

C7701锌白铜卷对卷连续高速镀镍前阴极电化学除油工艺研究

为了解决传统的C7701锌白铜卷材除油、去污前处理工艺存在的环境污染、过程管控困难等缺点,开发了一种不含磷的弱碱性除油液来对C7701锌白铜板材进行阴极电化学除油。研究了阴极电流密度、温度、波美度和处理时间对除油效果的影响,得到较佳的工艺条件为:阴极电流密度2.2 A/dm2,温度65°C,波美度10°Bé,时间42 s。在最佳工艺条件下可有效去除C7701锌白铜板材表面的油污,而且不腐蚀基材。该工艺的废水中不含磷,锌含量低于1 mg/L。

铜冶炼高砷烟尘有价金属综合回收试验研究

对铜冶炼高砷烟尘进行多段逆流低酸浸出,实现有价金属分向、梯级综合回收,其中铅、铋、锡富集于浸出渣中回收,在浸出液中梯级回收铜、砷、锌。结果表明:探明了高砷烟尘湿法回收工艺过程中有价金属的元素分布情况以及浸出液中有价金属以硫化铜、白砷、硫酸锌形式回收的可行性;通过两段逆流氧化浸出,铜、锌、砷的浸出率分别为:91%、98%、88%。

氧化锌矿废渣制备白炭黑的研究

以氧化锌矿硫酸铵焙烧、水溶、转化提取铅锶后的废渣为原料,氢氧化钠为溶出剂,碱溶得到提硅渣和硅酸钠溶液,适宜的溶出条件为氢氧化钠与废渣的质量比1∶1、溶出温度85℃、溶出时间2 h。分步碳分硅酸钠溶液制备白炭黑产品:第一步碳分终点pH值10.8,溶液中的Al、Zn、Ca等杂质沉淀或包覆除去;第二步碳分硅酸钠精制液终点pH值9.0,得到沉淀白炭黑产品和碳酸钠溶液,结晶得到碳酸钠产品,所得白炭黑为无定形白色球形颗粒,粒度均匀,各项指标符合国家行业标准。也可用活性石灰乳直接苛化硅酸钠溶液制取硅酸盐产品和氢氧化钠溶液,实现循环利用。

白烟尘两段逆流浸出工艺研究

针对白烟尘既富含铜、铅、锌、铋等多种有价金属,又含有砷、镉等有害元素的特点,提出一种两段逆流浸出工艺。采用该工艺进行实验处理某铜冶炼厂生产的白烟尘,分别考察了酸浸方式、初始硫酸质量浓度、酸浸液固比、酸浸温度、酸浸时间对铜砷浸出的影响。探索出最佳工艺条件液固比为4∶1,初始硫酸质量浓度80g/L,反应温度为80℃,反应时间为2 h。二次浸出液返回继续浸出白烟尘,此时白烟尘铜、锌、砷浸出率分别为95.7%、98.5%、92.2%,而浸出渣中铜、锌、砷品位降至0.42%、0.50%、1.28%。铅、铋的品位实现有效富集,二次酸浸渣中品位分别为47.73%和9.72%,相比原料分别富集约2.6倍和4.5倍。

Zn(BTZ)_2白色有机电致发光材料的合成及其器件制备

以PCl3为脱水剂 ,将邻氨基硫酚与水杨酸脱水环化合成出 2 (2 羟基苯基 )苯并噻唑 ,并进一步将所得产物与乙酸锌反应合成出 2 (2 羟基苯基 )苯并噻唑螯合锌 (Zn (BTZ) 2 )材料。以该配合物作为发光层制备出结构为ITO PVK∶TPD Zn(BTZ) 2 Al近白色电致发光器件 ,其色坐标位于白场之内 (x =0 .2 4 2 ,y =0 .35 9) ,在驱动电压为 1 6V时 ,亮度达 32 0 0cd m2 ,对应的量子效率为 0 .32 %。进一步在Zn (BTZ) 2 中掺入橙红色染料Ru brene ,制成ITO PVK∶TPD Zn(BTZ) 2 ∶Rubrene Al结构器件 ,实现了纯白色发光 (色坐标值 :x =0 .32 4 ,y =0 .343) ,非常接近于白色等能点 ,且量子效率达 0 .4 7%。

氮锌复合作用对白三叶草根瘤超显微结构的影响

采用砂培试验和电子显微技术,研究了不同水平氮锌配施对白三叶草根瘤发育和超显微结构的影响。结果表明,随施氮水平增加,根瘤数量、根瘤固氮酶活性、单瘤重量、根瘤细胞内类菌体数量显著下降,类菌体周膜空间增大。与缺锌条件相比,足量供锌显著增加了根瘤数量、单瘤重量、根瘤固氮酶活性、根瘤细胞内类菌体数量和类菌体体积,减小了类菌体周膜空间,类菌体周膜、细胞壁、细胞膜完整性和均匀性增加。与其它处理相比较,低氮和足量供锌处理显著增加了根瘤数量、单瘤重量、根瘤固氮酶活性、根瘤细胞内类菌体数量,显著减小了类菌体周膜空间。

亚微细锌-钇抗菌白炭黑的制备及性能研究

通过溶胶-凝胶法制备了锌-钇抗菌白炭黑,并通过单因素实验分别探究了Zn2+浓度、钇离子浓度及反应时间对锌-钇抗菌白炭黑粒径大小的影响,从而得出此种抗菌材料最佳粒径的制备条件。运用激光粒度分析仪、红外光谱(FT-IR)、X射线衍射(XRD)对产品进行表征;抗菌性能的研究采用涂布平板法,菌种采用大肠杆菌。结果表明:当Zn2+浓度为0.01mol/L、钇离子浓度为0.005mol/L、反应时间为1.5h时,产品分散性较好,粒径小且均一,并且锌-钇抗菌白炭黑对大肠杆菌具有较好的抑菌效果,杀菌率可达到90%以上。FT-IR分析表明添加抗菌离子后,并没有改变载体白炭黑的结构;XRD分析发现锌-钇抗菌白炭黑产品为无定形态。

镀锌层三价铬高耐蚀蓝白钝化工艺研究

三价铬钝化环境污染小,但钝化膜的耐蚀性不及六价铬钝化。为此,深入研究了三价铬钝化的耐蚀性。基于钝化液的基本组成配方,用正交试验法优化了镀锌层三价铬蓝白钝化工艺的最佳工艺参数和工艺范围:4.8g/LCrCl3,1.0mL/LH2SO4,1.0mL/LHNO3,2.5mL/L醇类添加剂,2.5mL/LHAc,钝化液温度25℃,浸渍时间15s,钝化液pH值1.8。研究了工艺参数与钝化层外观和耐蚀性的关系,在最佳工艺参数的条件下,进行镀锌层三价铬蓝白钝化处理,所得膜层经76h的中性盐雾试验不产生白锈,已超过了国家标准的48h。

水热法合成Zn_(0.85)Mn_(0.15)O纳米晶体及其光性能

目的目前,最重要的问题是难以合成高质量均匀掺杂的样品,原因之一就是影响样品结构和性能的因素很多,比如前驱物浓度、pH值、温度、时间,现在还没有搞清楚,不同的制备方法也得出不同的结论.方法采用水热法,在正交实验研究的基础上,设计了不同前驱物浓度的实验,用X射线衍射仪,扫描电镜对其样品的结构和晶粒的形貌进行了研究,最后测试了不同前驱物浓度样品的室温拉曼光谱.结果采用水热法合成了Zn0.85Mn0.15O纳米晶体,得出了各因素影响实验响应的大小;观察到ZnMn2+3O4这种杂相,同时不同前驱物浓度样品的拉曼光谱显示,E2模及A1模均向低频方向移动,而且不同的前驱物浓度,其E2模及A1模向低频方向移动的幅度不同.结论虽然用水热法可以合成出比较均匀的纳米体,但其制备的技术现在不够成熟,尤其是前驱物浓度等因素影响晶粒形貌的本质,也就是生长机理还不太清楚,依然需要深入的研究.

氮锌复合作用对白三叶叶片叶绿体超微结构的影响

在砂培条件下,研究了不同水平氮锌配施对白三叶生长、叶片叶绿素含量和叶绿体超微结构的影响。结果表明,在缺锌条件下,随供氮水平增加,植株干物重、叶片叶绿素含量显著下降,氮锌配施表现为拮抗效应。在足量供锌条件下,中量供氮,植株干物重、叶片叶绿素含量高于低量供氮,氮锌配施表现为协同效应;与低水平供氮相比,当高水平供氮时,白三叶各组分干物重、叶片叶绿素含量显著下降,氮锌配施表现为拮抗效应。白三叶叶片超显微结构表明,低锌条件下,随供氮水平增加,叶绿体结构变差,基粒及基粒片层、基质片层数量下降甚至解体,光合能力显著下降。足量供锌时,以中量供氮叶绿体基粒及基粒片层、基质片层数量最多,内部结构有序性最高,光合能力最强。叶绿体超显微结构变化与白三叶干物重、叶绿素含量变化趋势相一致。

钛白废酸的综合利用

研究了钛白废酸浸出含锌氧化物料的湿法冶金过程。在此基础上 ,制得了高品位钛黄、氧化铁红、碱式碳酸锌、活性氧化锌和含锌镁硫酸铵复合肥。最大限度地从含锌氧化物料和钛白废酸中回收了锌、钛和铁 ,硫酸得到利用 。

白烟灰浸出液砷与锌的分离与回收

对硫化法共沉淀浸出液中的锌和砷的工艺进行了研究,在优化条件下,锌和砷的沉淀率分别为100%和99%;进一步研究了加铁盐氧化脱砷并分离锌和砷,分别得到砷酸铁及硫化锌产品。浸出液用氢氧化钠调节pH可分离出90%以上的砷,再加入硫化物可将锌沉淀完全。而采用氢氧化钙调节pH为1左右,加入硫酸铁,可将95%以上砷分离。再调节脱砷液pH为4以上,控制Na2S/Zn摩尔比为1.5,可将Zn2+沉淀完全。在沉锌后的滤液中未检测出砷。

锌合金工业白烟治理的实验研究

填料塔洗涤吸收净化工艺在化工领域和低浓度工业废气净化方面均能很好地发挥作用。以水为吸收剂,应用填料塔对锌合金白烟进行吸收操作,试验结果显示:锌白烟的主要成分是氯化铵烟尘,其粒径在1μm以下,极不易溶于水,导致该工艺对氯化铵烟尘的处理效率仅在70%左右。烟气中氯化氢和氨气的浓度较低,经过处理已经达到排放标准。尽管氯化铵烟尘的处理效率低于预期,但实验研究对锌合金白烟的治理仍有重要的指导意义。

分光光度法测定镀锌白色钝化液中的铬(Ⅵ)和铬(Ⅲ)

在硫、磷混酸介质中,以花青为还原剂,采用分光光度法测定镀锌白色钝化液中的铬(Ⅵ),利用过氧化氢氧化铬(Ⅲ)测定钝化液中的铬(Ⅲ)。阐述了该方法的测量步骤,探讨了测量波长、酸度、反应温度、时间、花青用量及共存离子对测量结果的影响。结果表明,当铬(Ⅵ)浓度为0-1 04μg/mL时,所测吸光度与铬(Ⅵ)间的关系遵守比耳定律。与常用的硫酸亚铁铵滴定法相比,该方法准确度更高。

锌-铈无机抗菌材料的制备及应用研究

通过溶胶-凝胶法制备获得一种具有抗菌性能的锌-铈抗菌白炭黑。通过单因素试验分别探究了锌离子浓度、稀土铈离子浓度和反应时间对锌-铈抗菌白炭黑抑菌率的影响。从而得到了较佳制备条件,锌离子浓度是0.8 mol·L^(-1)、稀土铈离子浓度是0.005 mol·L^(-1)、反应时间是1.5 h。实验以大肠杆菌为菌种,采用涂布平板法进行抗菌实验。采用SEM、EDS、BET、FTIR和XRD检测手段对产品进行表征。结果表明,锌-铈抗菌白炭黑结构蓬松,平均粒径较小,为无定形态。锌-铈抗菌白炭黑的比表面积为载体白炭黑的两倍多,更有利于作为添加剂加入到制品中。锌和铈离子的加入,载体白炭黑的原本结构并没有发生改变。此外,本研究还将锌-铈抗菌白炭黑添加到陶瓷中,获得了具有抗菌性能的抗菌陶瓷。

碱性锌镍合金电镀白钝化工艺的研究

研究了不同镍含量的锌镍合金镀层低铬白钝化工艺。通过中性盐雾试验 ,比较了不同钝化工艺对不同镍含量的锌镍合金镀层耐蚀性的影响。结果表明 。