IZO films were deposited onto PET substrate at room temperature with the inclined opposite target type DC magnetron sputtering equipment,in which a sintered oxide IZO target(doped with 10% ZnO,packing density of 99.99...IZO films were deposited onto PET substrate at room temperature with the inclined opposite target type DC magnetron sputtering equipment,in which a sintered oxide IZO target(doped with 10% ZnO,packing density of 99.99%) was used.The effects of total sputtering pressure and film thickness on IZO films properties were studied.All the films produced at room temperature have a amorphous structure,irrespective of the total sputtering pressure and film thickness.A resistivity of the order of 10-4 Ωcm was obtained for IZO films deposited at lower pressure(film thickness of 190 nm).The resistivity of IZO films deposited at room temperature depends on film thickness and shows a minimum at a thickness of 530 nm.展开更多
基金supported by the Ministry of Education,Science Technology (MEST) and Korea Industrial Technology Foundation (KOTEF) through the Human Resource Training Project for Regional Innovation
文摘IZO films were deposited onto PET substrate at room temperature with the inclined opposite target type DC magnetron sputtering equipment,in which a sintered oxide IZO target(doped with 10% ZnO,packing density of 99.99%) was used.The effects of total sputtering pressure and film thickness on IZO films properties were studied.All the films produced at room temperature have a amorphous structure,irrespective of the total sputtering pressure and film thickness.A resistivity of the order of 10-4 Ωcm was obtained for IZO films deposited at lower pressure(film thickness of 190 nm).The resistivity of IZO films deposited at room temperature depends on film thickness and shows a minimum at a thickness of 530 nm.