Stereolithography(SLA)combined with a two-step post-processing method“oxidation−reduction”was developed to fabricate pure copper with high complexity.The copper slurries for SLA were prepared,and particularly the in...Stereolithography(SLA)combined with a two-step post-processing method“oxidation−reduction”was developed to fabricate pure copper with high complexity.The copper slurries for SLA were prepared,and particularly the influence of volume fraction of copper on the properties of copper slurries was investigated.In the two-step post-treatment process,organics were removed by oxidation and copper powder was oxidized simultaneously,and then the oxidized copper was reduced into highly reactive copper particles,improving the sintering activity of the copper green body and enhancing the relative density of the sintered part.The results show that curing depth of the copper slurries decreased with the increase of volume fraction of copper.The viscosity of the pure copper slurry rises exponentially as the volume fraction of copper exceeded 50%.The highest volume fraction of pure copper slurry for SLA is 55%.The specimens exhibited an increase in hardness and electrical conductivity with the increase of volume fraction of copper.Specifically,the maximum values of hardness and conductivity of samples with 55 vol.%copper were HV 52.7 and 57.1%(IACS),respectively.展开更多
基金supported by the Major Science and Technology Projects in Fujian Province,China(No.2023HZ021005)the State Key Laboratory of Powder Metallurgy,Central South University,China,and Fujian Key Laboratory of Rare-earth Functional Materials,China.
文摘Stereolithography(SLA)combined with a two-step post-processing method“oxidation−reduction”was developed to fabricate pure copper with high complexity.The copper slurries for SLA were prepared,and particularly the influence of volume fraction of copper on the properties of copper slurries was investigated.In the two-step post-treatment process,organics were removed by oxidation and copper powder was oxidized simultaneously,and then the oxidized copper was reduced into highly reactive copper particles,improving the sintering activity of the copper green body and enhancing the relative density of the sintered part.The results show that curing depth of the copper slurries decreased with the increase of volume fraction of copper.The viscosity of the pure copper slurry rises exponentially as the volume fraction of copper exceeded 50%.The highest volume fraction of pure copper slurry for SLA is 55%.The specimens exhibited an increase in hardness and electrical conductivity with the increase of volume fraction of copper.Specifically,the maximum values of hardness and conductivity of samples with 55 vol.%copper were HV 52.7 and 57.1%(IACS),respectively.