Octahedral Mn_(3)O_(4)nanoparticles with an Ag-doping and nanoporous Ag(NPS)framework was simply fabricated through an alloying-etching engineering.The dual-modified Mn_(3)O_(4)(denoted as Ag−Mn_(3)O_(4)/NPS)consists ...Octahedral Mn_(3)O_(4)nanoparticles with an Ag-doping and nanoporous Ag(NPS)framework was simply fabricated through an alloying-etching engineering.The dual-modified Mn_(3)O_(4)(denoted as Ag−Mn_(3)O_(4)/NPS)consists of Ag-doped Mn_(3)O_(4)nanoparticles crosslinked with three dimensional nanoporous Ag framework.The incorporated Ag dopant is effective in improving the intrinsic ionic and electronic conductivities of Mn_(3)O_(4),while the NPS framework is introduced to improve the electron/mass transfer across the entire electrode.Profiting from the dual-modification strategy,the Ag−Mn_(3)O_(4)/NPS exhibits admirable rate capability and cycling stability.A high reversible capacity of 88.7 mA·h/g can still be retained for over 1000 cycles at a current density of 1 A/g.Moreover,a series of ex-situ experimental techniques indicate that for Ag−Mn_(3)O_(4)/NPS electrode during the zinc ion storage,Mn_(3)O_(4)is electrochemically oxidized into various MnOx(e.g.,Mn_(2)O_(3),MnO2)species in the initial charging,and the subsequent battery reaction is actually the intercalation/deintercalation of H+and Zn2+into MnOx.展开更多
基金financially supported by the Natural Science Foundation of Shandong Province,China (Nos.ZR2023ME155,ZR2023ME085)the National Natural Science Foundation of China (No.52201254)+1 种基金the Project of“20 Items of University”of Jinan,China (No.202228046)the Taishan Scholar Project of Shandong Province,China (No.tsqn202306226)。
文摘Octahedral Mn_(3)O_(4)nanoparticles with an Ag-doping and nanoporous Ag(NPS)framework was simply fabricated through an alloying-etching engineering.The dual-modified Mn_(3)O_(4)(denoted as Ag−Mn_(3)O_(4)/NPS)consists of Ag-doped Mn_(3)O_(4)nanoparticles crosslinked with three dimensional nanoporous Ag framework.The incorporated Ag dopant is effective in improving the intrinsic ionic and electronic conductivities of Mn_(3)O_(4),while the NPS framework is introduced to improve the electron/mass transfer across the entire electrode.Profiting from the dual-modification strategy,the Ag−Mn_(3)O_(4)/NPS exhibits admirable rate capability and cycling stability.A high reversible capacity of 88.7 mA·h/g can still be retained for over 1000 cycles at a current density of 1 A/g.Moreover,a series of ex-situ experimental techniques indicate that for Ag−Mn_(3)O_(4)/NPS electrode during the zinc ion storage,Mn_(3)O_(4)is electrochemically oxidized into various MnOx(e.g.,Mn_(2)O_(3),MnO2)species in the initial charging,and the subsequent battery reaction is actually the intercalation/deintercalation of H+and Zn2+into MnOx.