Using H 2 diluted silane,series of μc Si∶H films are fabricated at low temperature with VHF PECVD.The thickness measurements reveal that the deposition rates are obviously enhanced with higher plasma excitation ...Using H 2 diluted silane,series of μc Si∶H films are fabricated at low temperature with VHF PECVD.The thickness measurements reveal that the deposition rates are obviously enhanced with higher plasma excitation frequency or working pressure,but increase firstly and then decrease with the increase of plasma power density.Raman spectra show that the crystallinity and the average grain sizes of the films strongly depend on the temperature of substrate and the concentration of silane.However,the plasma excitation frequency only has effect on the crystallinity,and a maximum occurs during the further increase of plasma excitation frequency.From XRD and TEM experiments,three preferential crystalline orientations (111),(220) and (311) are observed,and the average grain sizes are different for every crystalline orientation.展开更多
文摘Using H 2 diluted silane,series of μc Si∶H films are fabricated at low temperature with VHF PECVD.The thickness measurements reveal that the deposition rates are obviously enhanced with higher plasma excitation frequency or working pressure,but increase firstly and then decrease with the increase of plasma power density.Raman spectra show that the crystallinity and the average grain sizes of the films strongly depend on the temperature of substrate and the concentration of silane.However,the plasma excitation frequency only has effect on the crystallinity,and a maximum occurs during the further increase of plasma excitation frequency.From XRD and TEM experiments,three preferential crystalline orientations (111),(220) and (311) are observed,and the average grain sizes are different for every crystalline orientation.