Two heat treatments of A356 alloys with combined addition of rare earth and strontium were conducted.T6 treatment is a long time treatment（solution at 535 ℃ for 4 h ＋ aging at 150 ℃ for 15 h）.The other treatment ...Two heat treatments of A356 alloys with combined addition of rare earth and strontium were conducted.T6 treatment is a long time treatment（solution at 535 ℃ for 4 h ＋ aging at 150 ℃ for 15 h）.The other treatment is a short time treatment（solution at 550 ℃ for 2 h ＋ aging at 170 ℃ for 2 h）.The effects of heat treatment on microstructure and tensile properties of the Al-7%Si-0.3%Mg alloys were investigated by optical microscopy,scanning electronic microscopy and tension test.It is found that a 2 h solution at 550 ℃ is sufficient to make homogenization and saturation of magnesium and silicon in α（Al） phase,spheroid of eutectic Si phase.Followed by solution,a 2 h artificial aging at 170 ℃ is almost enough to produce hardening precipitates.Those samples treated with T6 achieve the maximum tensile strength and fracture elongation.With short time treatment（ST）,samples can reach 90% of the maximum yield strength,95% of the maximum strength,and 80% of the maximum elongation.展开更多
基金Project(2008B80703001) supported by Guangdong Provincial Department of Science and Technology,ChinaProject(09A45031160) supported by Guangzhou Science and Technology Commission,ChinaProject(ZC2009015) supported by Zengcheng Science and Technology Bureau,China
文摘Two heat treatments of A356 alloys with combined addition of rare earth and strontium were conducted.T6 treatment is a long time treatment（solution at 535 ℃ for 4 h ＋ aging at 150 ℃ for 15 h）.The other treatment is a short time treatment（solution at 550 ℃ for 2 h ＋ aging at 170 ℃ for 2 h）.The effects of heat treatment on microstructure and tensile properties of the Al-7%Si-0.3%Mg alloys were investigated by optical microscopy,scanning electronic microscopy and tension test.It is found that a 2 h solution at 550 ℃ is sufficient to make homogenization and saturation of magnesium and silicon in α（Al） phase,spheroid of eutectic Si phase.Followed by solution,a 2 h artificial aging at 170 ℃ is almost enough to produce hardening precipitates.Those samples treated with T6 achieve the maximum tensile strength and fracture elongation.With short time treatment（ST）,samples can reach 90% of the maximum yield strength,95% of the maximum strength,and 80% of the maximum elongation.