The influence of multipass high rotating speed friction stir processing(FSP)on the microstructure evolution,corrosion behavior,and tensile properties of the stirred zone(SZ)was investigated by EBSD,TEM,SEM,electrochem...The influence of multipass high rotating speed friction stir processing(FSP)on the microstructure evolution,corrosion behavior,and tensile properties of the stirred zone(SZ)was investigated by EBSD,TEM,SEM,electrochemical workstation and electronic universal testing machine.The mean grain size of the SZ is significantly refined,and it increases with the increase of the processing pass.In addition to an obvious increase in the number,the distribution ofβ-Al12Mg17 precipitates also becomes more uniform and dispersed with increasing the processing pass.Compared with the as-received AZ31 alloy,the tensile properties of the SZ are hardly improved,but the corrosion resistances are significantly enhanced.The corrosion potential of the SZ prepared by 4-pass FSP is increased from−1.56 V for the unprocessed AZ31 alloy to−1.19 V,while the corrosion current is decreased from 1.55×10^−4 to 5.47×10^−5 A.展开更多
基金Projects(51861034,51601167)supported by the National Natural Science Foundation of ChinaProject(2020GY-262)supported by the Science and Technology Department of Shaanxi Province,China+1 种基金Project(2019-86-1)supported by the Technology Bureau of Yulin,ChinaProject(20GK06)supported by the High-level Talent Program of Yulin University,China。
文摘The influence of multipass high rotating speed friction stir processing(FSP)on the microstructure evolution,corrosion behavior,and tensile properties of the stirred zone(SZ)was investigated by EBSD,TEM,SEM,electrochemical workstation and electronic universal testing machine.The mean grain size of the SZ is significantly refined,and it increases with the increase of the processing pass.In addition to an obvious increase in the number,the distribution ofβ-Al12Mg17 precipitates also becomes more uniform and dispersed with increasing the processing pass.Compared with the as-received AZ31 alloy,the tensile properties of the SZ are hardly improved,but the corrosion resistances are significantly enhanced.The corrosion potential of the SZ prepared by 4-pass FSP is increased from−1.56 V for the unprocessed AZ31 alloy to−1.19 V,while the corrosion current is decreased from 1.55×10^−4 to 5.47×10^−5 A.