A new kind of laminar metal matrix nanocomposite（MMC） was fabricated by an electrodeposition process with copper and superaligned carbon nanotubes film（SACNT film）.The SACNT film was put on a titanium plate and th...A new kind of laminar metal matrix nanocomposite（MMC） was fabricated by an electrodeposition process with copper and superaligned carbon nanotubes film（SACNT film）.The SACNT film was put on a titanium plate and then a layer of copper was electrodeposited on it.By repeating the above process,the laminar Cu/SACNT composite which contains dozens or hundreds of layers of copper and SACNT films was obtained.The thickness of a single copper layer was controlled by adjusting the process parameter easily and the thinnest layer is less than 2 μm.The microscopic observation shows that the directional alignment structure of SACNT is retained in the composite perfectly.The mechanical and electrical properties testing results show that the tensile and yield strengths of composites are improved obviously compared with those of pure copper,and the high conductivity is retained.This technology is a potential method to make applicable MMC which characterizes high volume fraction and directional alignment of carbon nanotubes.展开更多
The super-aligned carbon nanotube(SACNT)films reinforced copper(Cu)laminar composites with different orientationsof CNT ply were fabricated by electrodeposition.The results show that the tensile strength and yield str...The super-aligned carbon nanotube(SACNT)films reinforced copper(Cu)laminar composites with different orientationsof CNT ply were fabricated by electrodeposition.The results show that the tensile strength and yield strength of cross-ply compositewith5.0%(volume fraction)of SACNT reach maximum of336.3MPa and246.0MPa respectively,increased by74.0%and124.5%compared with pure Cu prepared with the same method.Moreover,the electrical conductivities of all the prepared composites areover75%IACS.The result of TEM analysis shows that the size of Cu grain and the thickness of twin lamellae can be reduced byadding SACNT,and the refining effect in cross-ply composites is more significant than that in unidirectional ply composites.Theenhanced strength of the Cu/SACNT composites comes from not only the reinforcing effect of SACNT films but also the additionalstrengthening of the Cu grain refinement caused by CNT orientation.展开更多
基金Project(20111080980)supported by the Initiative Scientific Research Program,Tsinghua University,China
文摘A new kind of laminar metal matrix nanocomposite（MMC） was fabricated by an electrodeposition process with copper and superaligned carbon nanotubes film（SACNT film）.The SACNT film was put on a titanium plate and then a layer of copper was electrodeposited on it.By repeating the above process,the laminar Cu/SACNT composite which contains dozens or hundreds of layers of copper and SACNT films was obtained.The thickness of a single copper layer was controlled by adjusting the process parameter easily and the thinnest layer is less than 2 μm.The microscopic observation shows that the directional alignment structure of SACNT is retained in the composite perfectly.The mechanical and electrical properties testing results show that the tensile and yield strengths of composites are improved obviously compared with those of pure copper,and the high conductivity is retained.This technology is a potential method to make applicable MMC which characterizes high volume fraction and directional alignment of carbon nanotubes.
基金Project(20111080980) supported by the Initiative Scientific Research Program,Tsinghua University,ChinaProject(2013AA031201) supported by the High Technology Research and Development Program of China
文摘The super-aligned carbon nanotube(SACNT)films reinforced copper(Cu)laminar composites with different orientationsof CNT ply were fabricated by electrodeposition.The results show that the tensile strength and yield strength of cross-ply compositewith5.0%(volume fraction)of SACNT reach maximum of336.3MPa and246.0MPa respectively,increased by74.0%and124.5%compared with pure Cu prepared with the same method.Moreover,the electrical conductivities of all the prepared composites areover75%IACS.The result of TEM analysis shows that the size of Cu grain and the thickness of twin lamellae can be reduced byadding SACNT,and the refining effect in cross-ply composites is more significant than that in unidirectional ply composites.Theenhanced strength of the Cu/SACNT composites comes from not only the reinforcing effect of SACNT films but also the additionalstrengthening of the Cu grain refinement caused by CNT orientation.