Pure Al coating was deposited on sintered NdFeB magnet by direct current(DC) magnetron sputtering to improve the corrosion resistance of magnet. The influences of coating thickness and sputtering power on microstruc...Pure Al coating was deposited on sintered NdFeB magnet by direct current(DC) magnetron sputtering to improve the corrosion resistance of magnet. The influences of coating thickness and sputtering power on microstructure and corrosion resistance of Al coating were investigated. The surface morphology of Al coating was characterized by scanning electron microscopy(SEM). The corrosion properties were investigated by potentiodynamic polarization curves and neutral salt spray(NSS) test. The formation of the uniform and compact Al coating is a necessary condition to achieve excellent corrosion resistance. And the optimal corrosion resistance can be obtained in the sample with 6.69 μm thick Al coating deposited at 51-82 W.展开更多
The Al−Mg alloy with high Mg addition(Al−9.2Mg−0.8Mn−0.2Zr-0.15Ti,in wt.%)was subjected to different passes(1,2 and 4)of high strain rate rolling(HSRR),with the total thickness reduction of 72%,the rolling temperature...The Al−Mg alloy with high Mg addition(Al−9.2Mg−0.8Mn−0.2Zr-0.15Ti,in wt.%)was subjected to different passes(1,2 and 4)of high strain rate rolling(HSRR),with the total thickness reduction of 72%,the rolling temperature of 400℃and strain rate of 8.6 s^(−1).The microstructure evolution was studied by optical microscope(OM),scanning electron microscope(SEM),electron backscattered diffraction(EBSD)and transmission electron microscope(TEM).The alloy that undergoes 2 passes of HSRR exhibits an obvious bimodal grain structure,in which the average grain sizes of the fine dynamic recrystallization(DRX)grains and the coarse non-DRX regions are 6.4 and 47.7mm,respectively.The high strength((507±9)MPa)and the large ductility((24.9±1.3)%)are obtained in the alloy containing the bimodal grain distribution.The discontinuous dynamic recrystallization(DDRX)mechanism is the prominent grain refinement mechanism in the alloy subjected to 2 passes of HSRR.展开更多
Effects of welding speed on the microstructure evolution in the stir zone(SZ)and mechanical properties of the friction stir welding(FSW)joints were studied by OM,XRD,SEM,TEM,EBSD and tensile testing.Compared with the ...Effects of welding speed on the microstructure evolution in the stir zone(SZ)and mechanical properties of the friction stir welding(FSW)joints were studied by OM,XRD,SEM,TEM,EBSD and tensile testing.Compared with the base metal(BM),an obviously fine dynamic recrystallization(DRX)microstructure occurs in the SZ and the DRX grain size decreases from 5.6 to 4.4μm with the increasing of welding speed.Fine DRX microstructure is mainly achieved by continuous dynamic recrystallization(CDRX)mechanism,strain induced boundary migration(SIBM)mechanism and particle stimulated nucleation(PSN)mechanism.Meanwhile,the geometric coalescence and the Burke−Turnbull mechanism are the main DRX grain growth mechanisms.Among all the welding speeds,the joint welded at rotation speed of 1500 r/min and welding speed of 75 mm/min has the greatest tensile properties,i.e.ultimate tensile strength(UTS)of(509±2)MPa,yield strength(YS)of(282±4)MPa,elongation(El)of(23±1)%,and the joint efficiency of 73%.展开更多
Effects of the sole and the combined addition of Ca and Sr on microstructure and mechanical properties of as-cast and as-rolled Mg-5 Zn alloys were carefully investigated by OM,SEM,hot-compression testing and tensile ...Effects of the sole and the combined addition of Ca and Sr on microstructure and mechanical properties of as-cast and as-rolled Mg-5 Zn alloys were carefully investigated by OM,SEM,hot-compression testing and tensile testing.Ca is more effective than Sr in the microstructural refinement of as-cast alloys.High-strain-rate rolling(HSRR)produces more deformed twins and thus provides more nucleation sites for dynamic recrystallization(DRX).The addition of Ca and Sr can promote dynamic precipitation during HSRR,the precipitation process would consume the storage energy and thus increases the critical strain value of DRX,resulting in the retarded DRX effect by the addition of Ca and/or Sr.The as-rolled Mg-5 Zn-0.4 Ca-0.2 Sr alloy exhibits a good combination of strength and ductility,with the ultimate tensile strength of 317 MPa,the yield strength of 235 MPa and the elongation to rupture of 24%.展开更多
The mechanical behaviors and damping capacities of the binary Mg−Ga alloys with the Ga content ranging from 1 to 5 wt.%were investigated by means of optical microscope(OM),scanning electron microscope(SEM),X-ray diffr...The mechanical behaviors and damping capacities of the binary Mg−Ga alloys with the Ga content ranging from 1 to 5 wt.%were investigated by means of optical microscope(OM),scanning electron microscope(SEM),X-ray diffraction(XRD),hardness test,tensile test and dynamic mechanical analyzer(DMA).The hardness(HV_(0.5))increases with the increase of Ga content,which can be described as HV_(0.5)=41.61+10.35c,and the solid solution strengthening effect∆σ_(s)of the alloy has a linear relationship with c^(n),where c is the molar fraction of solute atoms and n=1/2 or 2/3.Ga exhibits a stronger solid solution strengthening effect than Al,Zn or Sn due to the large atomic radius difference and the modulus mismatch between Ga and Mg atoms.The addition of Ga makes the Mg−Ga alloys have better damping capacity,and this phenomenon can be explained by the Granato−Lücke dislocation model.The lattice distortion and the modulus mismatch generated because of the addition of Ga increase the resistance to motion of the dislocation in the process of swinging or moving,and thus the better damping capacity is acquired.展开更多
基金Project(NCET-11-0127)supported by Program for New Century Excellent Talents in University,ChinaProject(K1306063-11)supported by the Key Project for Science and Technology of Changsha,China
文摘Pure Al coating was deposited on sintered NdFeB magnet by direct current(DC) magnetron sputtering to improve the corrosion resistance of magnet. The influences of coating thickness and sputtering power on microstructure and corrosion resistance of Al coating were investigated. The surface morphology of Al coating was characterized by scanning electron microscopy(SEM). The corrosion properties were investigated by potentiodynamic polarization curves and neutral salt spray(NSS) test. The formation of the uniform and compact Al coating is a necessary condition to achieve excellent corrosion resistance. And the optimal corrosion resistance can be obtained in the sample with 6.69 μm thick Al coating deposited at 51-82 W.
文摘The Al−Mg alloy with high Mg addition(Al−9.2Mg−0.8Mn−0.2Zr-0.15Ti,in wt.%)was subjected to different passes(1,2 and 4)of high strain rate rolling(HSRR),with the total thickness reduction of 72%,the rolling temperature of 400℃and strain rate of 8.6 s^(−1).The microstructure evolution was studied by optical microscope(OM),scanning electron microscope(SEM),electron backscattered diffraction(EBSD)and transmission electron microscope(TEM).The alloy that undergoes 2 passes of HSRR exhibits an obvious bimodal grain structure,in which the average grain sizes of the fine dynamic recrystallization(DRX)grains and the coarse non-DRX regions are 6.4 and 47.7mm,respectively.The high strength((507±9)MPa)and the large ductility((24.9±1.3)%)are obtained in the alloy containing the bimodal grain distribution.The discontinuous dynamic recrystallization(DDRX)mechanism is the prominent grain refinement mechanism in the alloy subjected to 2 passes of HSRR.
文摘Effects of welding speed on the microstructure evolution in the stir zone(SZ)and mechanical properties of the friction stir welding(FSW)joints were studied by OM,XRD,SEM,TEM,EBSD and tensile testing.Compared with the base metal(BM),an obviously fine dynamic recrystallization(DRX)microstructure occurs in the SZ and the DRX grain size decreases from 5.6 to 4.4μm with the increasing of welding speed.Fine DRX microstructure is mainly achieved by continuous dynamic recrystallization(CDRX)mechanism,strain induced boundary migration(SIBM)mechanism and particle stimulated nucleation(PSN)mechanism.Meanwhile,the geometric coalescence and the Burke−Turnbull mechanism are the main DRX grain growth mechanisms.Among all the welding speeds,the joint welded at rotation speed of 1500 r/min and welding speed of 75 mm/min has the greatest tensile properties,i.e.ultimate tensile strength(UTS)of(509±2)MPa,yield strength(YS)of(282±4)MPa,elongation(El)of(23±1)%,and the joint efficiency of 73%.
基金Projects(51471066,51571089) supported by the National Natural Science Foundation of ChinaProject(2019JJ40044) supported by the Natural Science Foundation of Hunan Province,China
文摘Effects of the sole and the combined addition of Ca and Sr on microstructure and mechanical properties of as-cast and as-rolled Mg-5 Zn alloys were carefully investigated by OM,SEM,hot-compression testing and tensile testing.Ca is more effective than Sr in the microstructural refinement of as-cast alloys.High-strain-rate rolling(HSRR)produces more deformed twins and thus provides more nucleation sites for dynamic recrystallization(DRX).The addition of Ca and Sr can promote dynamic precipitation during HSRR,the precipitation process would consume the storage energy and thus increases the critical strain value of DRX,resulting in the retarded DRX effect by the addition of Ca and/or Sr.The as-rolled Mg-5 Zn-0.4 Ca-0.2 Sr alloy exhibits a good combination of strength and ductility,with the ultimate tensile strength of 317 MPa,the yield strength of 235 MPa and the elongation to rupture of 24%.
基金supported by the National Natural Science Foundation of China(Nos.51571089, 51871093)the Natural Science Foundation of Hunan Province, China(No. 2019JJ40044)
文摘The mechanical behaviors and damping capacities of the binary Mg−Ga alloys with the Ga content ranging from 1 to 5 wt.%were investigated by means of optical microscope(OM),scanning electron microscope(SEM),X-ray diffraction(XRD),hardness test,tensile test and dynamic mechanical analyzer(DMA).The hardness(HV_(0.5))increases with the increase of Ga content,which can be described as HV_(0.5)=41.61+10.35c,and the solid solution strengthening effect∆σ_(s)of the alloy has a linear relationship with c^(n),where c is the molar fraction of solute atoms and n=1/2 or 2/3.Ga exhibits a stronger solid solution strengthening effect than Al,Zn or Sn due to the large atomic radius difference and the modulus mismatch between Ga and Mg atoms.The addition of Ga makes the Mg−Ga alloys have better damping capacity,and this phenomenon can be explained by the Granato−Lücke dislocation model.The lattice distortion and the modulus mismatch generated because of the addition of Ga increase the resistance to motion of the dislocation in the process of swinging or moving,and thus the better damping capacity is acquired.