Novel hydrophilic NaYF4:Yb^3+,Tm^3+@NaGdF4:Ce^3+,Eu^3+double-jacket microtubes(DJMTs)with upconversion/downconversion dual-mode luminescence were designed and prepared through epitaxial growth of NaGdF4:Ce^3+,Eu^3+she...Novel hydrophilic NaYF4:Yb^3+,Tm^3+@NaGdF4:Ce^3+,Eu^3+double-jacket microtubes(DJMTs)with upconversion/downconversion dual-mode luminescence were designed and prepared through epitaxial growth of NaGdF4:Ce^3+,Eu^3+shell onto the NaYF4:Yb^3+,Tm^3+microtube via poly(acrylic acid)(PAA)mediated hydrothermal method.It is demonstrated that PAA ligand played an important role in guiding the direct growth of NaGdF4:Ce^3+,Eu^3+shell onto the surface of NaYF4:Yb^3+,Tm^3+parent microtubes.The growth of NaGdF4:Ce^3+,Eu^3+shell experienced a crystal phase transition fromβ-NaGdF4 andβ-NaYF4 mixture toβ-NaYF4@NaGdF4 composite crystal,and morphology evolution from mixture ofβ-NaGdF4:Ce^3+,Eu^3+nanorods andβ-NaYF4:Yb^3+,Tm^3+microtubes to NaYF4:Yb^3+,Tm^3+@NaGdF4:Ce^3+,Eu^3+DJMTs.The formation mechanism of DJMTs was the dissolution−renucleation ofβ-NaGdF4:Ce^3+,Eu^3+nanorods and the growth ofβ-NaGdF4:Ce^3+,Eu^3+shell via the classical Ostwald ripening mechanism.The as-prepared DJMTs could exhibit blue upconversion and red downconversion luminescence,which was further made into environmentally benign luminescent inks for creating highly secured and fluorescent-based anti-counterfeiting patterns via inkjet printing.展开更多
Palladium-supported cobalt hydroxide(Co(OH)_(2)-Pd) nanoplates were fabricated in an aqueous solution and employed as a catalyst for the reduction of 4-nitrophenol.For the preparation of Co(OH)2-Pd,Pd nanoparticles we...Palladium-supported cobalt hydroxide(Co(OH)_(2)-Pd) nanoplates were fabricated in an aqueous solution and employed as a catalyst for the reduction of 4-nitrophenol.For the preparation of Co(OH)2-Pd,Pd nanoparticles were anchored on the Co(OH)_(2) nanoplates after the reduction of Na;PdCl;by ascorbic acid in the absence of a stabilizer at room temperature.The observations under transmission and scanning electron microscopy reveal that Pd nanoparticles with a size of 2-5 nm are uniformly dispersed on the surface of the Co(OH)_(2) nanoplates.In catalytic test,the conversion of 4-nitrophenol to 4-aminophenol is completed within 6 min in the presence of Co(OH)_(2)-Pd(1000) nanoplates with2.18 at.% Pd,and the corresponding kinetic constant is 0.0089 s;in the first test.The catalyst retains relatively high activity after several cycles.The results demonstrate that the Co(OH)_(2)-Pd(1000) nanoplates exhibit high catalytic activity toward the reduction of 4-nitrophenol in the presence of NaBH;.展开更多
基金Project(51874129)supported by the National Natural Science Foundation of ChinaProjects(2018JJ3115,2019JJ60049)supported by the Science Foundation of Hunan Province,ChinaProjects(19B153,19B158)supported by the Scientific Research Fund of Hunan Provincial Education Department,China。
文摘Novel hydrophilic NaYF4:Yb^3+,Tm^3+@NaGdF4:Ce^3+,Eu^3+double-jacket microtubes(DJMTs)with upconversion/downconversion dual-mode luminescence were designed and prepared through epitaxial growth of NaGdF4:Ce^3+,Eu^3+shell onto the NaYF4:Yb^3+,Tm^3+microtube via poly(acrylic acid)(PAA)mediated hydrothermal method.It is demonstrated that PAA ligand played an important role in guiding the direct growth of NaGdF4:Ce^3+,Eu^3+shell onto the surface of NaYF4:Yb^3+,Tm^3+parent microtubes.The growth of NaGdF4:Ce^3+,Eu^3+shell experienced a crystal phase transition fromβ-NaGdF4 andβ-NaYF4 mixture toβ-NaYF4@NaGdF4 composite crystal,and morphology evolution from mixture ofβ-NaGdF4:Ce^3+,Eu^3+nanorods andβ-NaYF4:Yb^3+,Tm^3+microtubes to NaYF4:Yb^3+,Tm^3+@NaGdF4:Ce^3+,Eu^3+DJMTs.The formation mechanism of DJMTs was the dissolution−renucleation ofβ-NaGdF4:Ce^3+,Eu^3+nanorods and the growth ofβ-NaGdF4:Ce^3+,Eu^3+shell via the classical Ostwald ripening mechanism.The as-prepared DJMTs could exhibit blue upconversion and red downconversion luminescence,which was further made into environmentally benign luminescent inks for creating highly secured and fluorescent-based anti-counterfeiting patterns via inkjet printing.
基金the financial supports from the National Natural Science Foundation of China (Nos. 51974116, 51874128)the Science Foundation of Hunan Province, China (Nos. 2020JJ4273, 2020JJ5130)。
文摘Palladium-supported cobalt hydroxide(Co(OH)_(2)-Pd) nanoplates were fabricated in an aqueous solution and employed as a catalyst for the reduction of 4-nitrophenol.For the preparation of Co(OH)2-Pd,Pd nanoparticles were anchored on the Co(OH)_(2) nanoplates after the reduction of Na;PdCl;by ascorbic acid in the absence of a stabilizer at room temperature.The observations under transmission and scanning electron microscopy reveal that Pd nanoparticles with a size of 2-5 nm are uniformly dispersed on the surface of the Co(OH)_(2) nanoplates.In catalytic test,the conversion of 4-nitrophenol to 4-aminophenol is completed within 6 min in the presence of Co(OH)_(2)-Pd(1000) nanoplates with2.18 at.% Pd,and the corresponding kinetic constant is 0.0089 s;in the first test.The catalyst retains relatively high activity after several cycles.The results demonstrate that the Co(OH)_(2)-Pd(1000) nanoplates exhibit high catalytic activity toward the reduction of 4-nitrophenol in the presence of NaBH;.