Bonding enhancement of cold rolling TA1 P-Ti/AA6061 composite plates via surface oxidation treatment

TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.

液体静压导轨定压供油式油腔承载力的超静定力学模型

在机床液体静压导轨的设计计算中,准确计算各油腔的承载力是正确设计液体静压导轨系统的前提。目前液体静压导轨的油腔承载力的计算一般采用'平移外负载'的方法。不同的油腔布置形式对应不同的力学模型,使'平移外负载'的通用性较差。根据叠加原理,利用逆向思维,将定压供油式油腔的承载力分为6部分,分别承受外载荷的6个分量。导轨上油腔的布置较复杂时,油腔承载力的计算变成超静定问题。借鉴'弹性体'的求解方法,列出油膜的变形协调方程,将超静定问题转化成静定问题,进而求解出各油腔的承载力。将油腔承载力的6部分进行矢量叠加,推导出油腔承载力的最终求解方程。以工程中的回转工作台为范例进行计算,与实际的已测结果进行比较,验证了该方法的正确可行性。所做研究提供了定压供油式液体静压导轨油腔承载力的通用计算方法,并能借助计算机编程求解,提高了设计效率和精度。

铝合金微弧氧化陶瓷层石墨相的形成及作用

在ZL10 8微弧氧化过程中 ,实现了石墨相的沉积。陶瓷层中的石墨相具有明显的减摩作用 。

盒形件固体颗粒介质板材成形工艺研究

固体颗粒介质板材成形工艺是采用固体颗粒微珠代替刚性凸(凹)模(或弹性体、液体)的作用对板材拉深成形的新工艺。选用非金属固体颗粒介质——GM颗粒作为研究对象,以固体颗粒介质在高应力水平下的体积压缩试验和摩擦强度试验为基础,应用散体力学理论中扩展的Drucker-Prager线性模型构建固体颗粒介质有限元材料模型。以具有非轴对称性的方盒形件为代表,进行固体颗粒介质成形工艺的有限元模拟,研究成形过程中板材的流动特征和壁厚分布规律。工艺试验成功得到方盒形零件,将加载曲线、成形过程变形特征和壁厚分布曲线与数值模拟结果比对较为吻合。分析表明,采用以散体力学为基础建立的固体颗粒介质材料模型进行工艺模拟,能够得到与试验较为接近的变形特征和力能参数,可以应用于制定工艺方案的依据,为该技术在板材成形中的应用起到指导和借鉴作用。

高压水除鳞喷嘴结构参数对喷嘴射流性能的影响

为了进一步研究高压水除鳞喷嘴的射流性能,优化喷嘴的结构参数,选取出口扩张角、锥孔深度、入口收缩角作为参考因素,以喷射角和射流流量作为评价指标,对喷嘴各参考因素对射流性能的影响进行了仿真分析。结合正交试验的方法,对喷嘴各结构参数及其交互作用对其性能影响的显著性及重要性次序进行分析,获得最优的参数组合并对其进行了实验验证。结果表明:出口扩张角的增大会使喷射角减小但会使射流流量增加,锥孔深度的增加可以较为全面地提升喷嘴的射流性能,收缩角的增大会使得喷嘴的射流性能减弱,喷嘴的除鳞效果变差;3个参考因素中锥孔深度是对射流性能影响最大的因素;当出口扩张角为80°、锥孔深度为8mm、入口收缩角为65°时喷嘴的射流性能最优。通过将参数优化后的喷嘴的实验结果与原始喷嘴的实验结果对比发现,优化后喷嘴的喷射角由原始值35.7°提升至44.1°,射流流量的大小由原始值10.17L/min提升至28.3L/min。

Cast-rolling force model in solid-liquid cast-rolling bonding(SLCRB) process for fabricating bimetal clad strips

Based on twin-roll casting, a cast-rolling force model was proposed to predict the rolling force in the bimetal solid-liquid cast-rolling bonding(SLCRB) process. The solid-liquid bonding zone was assumed to be below the kiss point(KP). The deformation resistance of the liquid zone was ignored. Then, the calculation model was derived. A 2D thermal-flow coupled simulation was established to provide a basis for the parameters in the model, and then the rolling forces of the Cu/Al clad strip at different rolling speeds were calculated. Meanwhile, through measurement experiments, the accuracy of the model was verified. The influence of the rolling speed, the substrate strip thickness, and the material on the rolling force was obtained. The results indicate that the rolling force decreases with the increase of the rolling speed and increases with the increase of the thickness and thermal conductivity of the substrate strip. The rolling force is closely related to the KP height. Therefore, the formulation of reasonable process parameters to control the KP height is of great significance to the stability of cast-rolling forming.

Three-roller continuous setting round process for longitudinally submerged arc welding pipes

In order to solve the problems of excess ovality and cross-section distortion of longitudinally submerged arc welding pipes after forming,a new three-roller continuous setting round process was proposed.This process can be divided into three stages:loading stage,roll bending stage and unloading stage.Based on the discretization idea,the mechanical model of the primary statically indeterminate problem of the longitudinally submerged arc welding pipes at the roll bending stage was established,and the deformation response was obtained.The simulation and theoretical results show that there are three positive bending regions and three reverse bending regions along the circumference of the pipe.The loading force of each roller shows growth,stability and downward trend with time.The error between the theoretical fitting curve and the simulated data point is very small,and the simulation results verify the reliability of the theoretical calculation.The experimental results show that the residual ovality decreases with the increase of the reduction,and the reduction of the turning point is the optimum reduction.In addition,the residual ovality of the pipe is less than 0.7%without cross-section distortion,which verifies the feasibility of this process.

Bonding strength of Invar/Cu clad strips fabricated by twin-roll casting process

Based on traditional twin-roll casting process,Invar/Cu clad strips were successfully fabricated by using solid Invar alloy strip and molten Cu under conditions of high temperature,high pressure and plastic deformation.A series of tests including tensile test,bending test,T-type peeling test and scanning electron microscope(SEM)and energy dispersive spectrometer(EDS)measurements were carried out to analyze the mechanical properties of Invar/Cu clad strips and the micro-morphology of tensile fracture surfaces and bonding interfaces.The results indicate that no delamination phenomenon occurs during the compatible deformation of Invar/Cu in bending test and only one stress platform exists in the tensile stress-strain curve when the bonding strength is large.On the contrary,different mechanical properties of Invar and Cu lead to delamination phenomenon during the uniaxial tensile test,which determines that two stress platforms occur on the stress-strain curve of Invar/Cu clad strips when two elements experience necking.The average peeling strength can be increased from13.85to42.31N/mm after heat treatment at800℃for1h,and the observation of the Cu side at peeling interface shows that more Fe is adhered on the Cu side after the heat treatment.All above illustrate that heat treatment can improve the strength of the bonding interface of Invar/Cu clad strips.

Multi-point flexible straightening process by reciprocating bending for metal profiles

A multi-point flexible straightening process characterized by reciprocating bending is proposed.Specifically,the process is analyzed in terms of deformation mechanism and verified by numerical simulations and physical experiments of the straightening of a series of metal profiles with different materials and initial shapes.Further,the relationship between the bending radius and the times of reciprocating bending required to unify the curvature is discussed,and the distribution of residual stress after straightening is analyzed.The results show that the reciprocating bending process can eliminate the difference of the initial curvature,make the curvature of each section tend to be uniform;the times of reciprocating bending to reach the uniform curvature decreases with the decrease of bending radius.The straightness of the straightened profile obtained from the experiment and simulation is less than 0.2%,demonstrating a good feasibility of this method.

Instability analysis of free deformation zone of cylindrical parts based on hot-granule medium-pressure forming technology

The cylindrical part of sheet metal based on hot-granule medium-pressure forming (HGMF) technology was investigated.The stress functions of the free deformation zone and the fracture instability theory were combined to establish the analytical expression of the critical pressure of punch. The results show that the active friction between the granule medium and the sheet metal, as well as the non-uniform internal pressure presented by the solid granule medium, can obviously improve the forming performance of the sheet metal. The critical pressure of punch increases with the increment of the friction coefficient between the granule medium and sheet metal, as well as the plastic strain ratio, whereas it decreases with the increase of the material-hardening exponent. Furthermore, the impact on the critical pressure from high to low order is the plastic strain ratio, the friction coefficient,and material-hardening exponent. The deep-drawing experiment with HGMF technology on AZ31B magnesium alloy sheet verified the instability theory.Key words: hot-granule

Interfacial pressure distribution and bonding characteristics in twin-roll casting of Cu/Al clad strip

The mechanical properties and product thickness specifications of bimetallic clad strip prepared by twin-roll casting are tightly related to the mechanical behavior of bonding interface interaction.The thermal−flow coupled simulation and the interface pressure calculation models are established with the cast-rolling velocity as the variable.The results show that the interface temperature decreases,the interface pressure and the proportion of the thickness of the Al side increase with the decrease in cast-rolling velocity.The thinning of Cu strip mainly occurs in the backward slip zone.The higher pressure and longer solid/semi-solid contact time make the interface bonded fully,which provides favorable conditions for atomic diffusion.The inter-diffusion zone with a width of 4.9μm is attained at a cast-rolling velocity of 2.4 m/min,and the Cu side surface is nearly completely covered by aluminum.Therefore,the ductile fracture occurs on the Al side,which prevents the propagation of interface delamination cracks effectively.Meanwhile,shear effect becomes more significant at high interfacial pressure and large plastic strain,and the microstructure on Al side is composed of slender columnar crystals.Thus,the metallurgical bonding and refinement of grains on the Al side can result in higher bonding strength and tensile properties of the clad strip.

Microstructure homogeneity regulation of 7050 aluminum forgings by surface cumulative plastic deformation

To regulate the microstructure homogeneity of large aluminum structural forgings for aircraft,the surface cumulative plastic deformation was proposed.The microstructure of 7050 aluminum forgings after the surface cumulative plastic deformation was investigated by electron backscatter diffraction(EBSD),transmission electron microscopy(TEM),and X-ray diffraction(XRD).The results showed that the microstructure evolution of 7050 aluminum forgings was more sensitive to the deformation temperature than the strain rate.The dislocation density continued to increase with the decrease of the deformation temperature and the increase of the strain rate.Dislocation density and stored energy were accumulated by the surface cumulative plastic deformation.Besides,a static recrystallization(SRX)model of 7050 aluminum forgings was established.The SRX volume fraction calculated by this model was in good agreement with the experimental results,which indicated that the model could accurately describe the SRX behavior of 7050 aluminum forgings during the surface cumulative plastic deformation.

High temperature stress–strain curves of MnS and their applications in finite element simulation

A novel method for testing stress–strain curves of non-metallic materials was presented.The high temperature stress-strain curves of MnS were preliminarily obtained and corrected to account for the influence of friction.Using the finite element method,the influence of deformation parameters on the deformation evolution of MnS inclusions was investigated based on the experimental reference data.The corresponding physical experiment was designed for comparative analysis.The results indicate that the experimental high-temperature deformation data of MnS are highly reliable.In the process of matrix deformation,the shapes of MnS inclusions change from spherical to ellipsoidal and even to lamellar.There are some differences in the morphological deformation of MnS inclusions located at different positions.With the increase in the initial size of MnS inclusions,the risk of failing the inclusion-flaw inspection increases and the forging quality further deteriorates.