Friction stir welding was used to join two AA2060-T8 plates,and then the effect of precipitate evolution on microstructure and corrosion behavior of the joint was investigated.The evolution of precipitates on the top ...Friction stir welding was used to join two AA2060-T8 plates,and then the effect of precipitate evolution on microstructure and corrosion behavior of the joint was investigated.The evolution of precipitates on the top surface of the joint was characterized by scanning electron microscopy and transmission electron microscopy.The corrosion behaviors of different regions in the joint were investigated by an electrochemistry method and an alternating salt spray exposure.The corrosion was mainly dependent on the nature of precipitates in each region of the joint.The shoulder affected zone had the worst corrosion resistance as a result of the re-dissolved ofθ′(Al2Cu),T1(Al2CuLi)andδ′(Al3Li)phases,the formation of intergranular precipitates and precipitate-free zones.However,the thermomechanically affected zone had a slightly improved corrosion resistance because it had no intergranular precipitates.The heat affected zone and base metal had the best corrosion resistance.展开更多
The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,t...The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,the volume fraction ofαphase decreased with increasing strain rate.At 600 and 650°C,the volume fraction ofαphase firstly increased to a maximum value with increasing strain rate from 1×10-3 to 1×10-2 s-1,and then decreased.At 700°C,the microstructure consisted of singleβphase.At a given strain rate,the volume fraction ofαphase decreased with increasing deformation temperature.With decreasing strain rate and increasing deformation temperature,the volume fraction and size of globularαphase increased.At 650°C and 1×10-3 s-1,the lamellarαphase was fully globularized.The variation in the volume fraction and morphology ofαphase with strain rate and deformation temperature significantly affected the hardness of 47Zr-45Ti-5Al-3V alloy.展开更多
基金Beijing Natural Science Foundation (Grant No. 3194048)China Friction Stir Welding Center and to Beijing Key Laboratory of Pipeline Critical Technology and Equipment for Deepwater Oil & Gas Development (Grant No. BIPT2018006) for the financial support
文摘Friction stir welding was used to join two AA2060-T8 plates,and then the effect of precipitate evolution on microstructure and corrosion behavior of the joint was investigated.The evolution of precipitates on the top surface of the joint was characterized by scanning electron microscopy and transmission electron microscopy.The corrosion behaviors of different regions in the joint were investigated by an electrochemistry method and an alternating salt spray exposure.The corrosion was mainly dependent on the nature of precipitates in each region of the joint.The shoulder affected zone had the worst corrosion resistance as a result of the re-dissolved ofθ′(Al2Cu),T1(Al2CuLi)andδ′(Al3Li)phases,the formation of intergranular precipitates and precipitate-free zones.However,the thermomechanically affected zone had a slightly improved corrosion resistance because it had no intergranular precipitates.The heat affected zone and base metal had the best corrosion resistance.
基金Project(201629) supported by the Scientific Research Foundation for Introduced Talent of Guizhou University,ChinaProjects(20164014,20165654) supported by the Hundred-level Innovative Talents Project of Guizhou Province,ChinaProject(20146013) supported by the Science and Technology of Guizhou Province,China
文摘The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,the volume fraction ofαphase decreased with increasing strain rate.At 600 and 650°C,the volume fraction ofαphase firstly increased to a maximum value with increasing strain rate from 1×10-3 to 1×10-2 s-1,and then decreased.At 700°C,the microstructure consisted of singleβphase.At a given strain rate,the volume fraction ofαphase decreased with increasing deformation temperature.With decreasing strain rate and increasing deformation temperature,the volume fraction and size of globularαphase increased.At 650°C and 1×10-3 s-1,the lamellarαphase was fully globularized.The variation in the volume fraction and morphology ofαphase with strain rate and deformation temperature significantly affected the hardness of 47Zr-45Ti-5Al-3V alloy.