The morphologies and formation process of Ni-pool defects in WC?8Ni cemented carbides were studied. The SEM images show that Ni-pool generally has two kinds of morphologies: “island” in isolation and “ring” around...The morphologies and formation process of Ni-pool defects in WC?8Ni cemented carbides were studied. The SEM images show that Ni-pool generally has two kinds of morphologies: “island” in isolation and “ring” around a new phase. In the obtained samples with “ring-like Ni-pool”, WC, Ni and Ni2W4C (η phase) phases were detected in XRD patterns. Combined with SEM, EDX and XRD results, it is found that the phase in the center of the “ring-like Ni-pool” is Ni2W4C (η phase) and the main chemical components of Ni-pool are Ni, W and C. In addition, the relationships among large size Ni (agglomerated) particles, volatile impurities, pores and carbon content vs forming process of the Ni-pool defects for WC?8Ni cemented carbides are also presented and discussed.展开更多
文摘The morphologies and formation process of Ni-pool defects in WC?8Ni cemented carbides were studied. The SEM images show that Ni-pool generally has two kinds of morphologies: “island” in isolation and “ring” around a new phase. In the obtained samples with “ring-like Ni-pool”, WC, Ni and Ni2W4C (η phase) phases were detected in XRD patterns. Combined with SEM, EDX and XRD results, it is found that the phase in the center of the “ring-like Ni-pool” is Ni2W4C (η phase) and the main chemical components of Ni-pool are Ni, W and C. In addition, the relationships among large size Ni (agglomerated) particles, volatile impurities, pores and carbon content vs forming process of the Ni-pool defects for WC?8Ni cemented carbides are also presented and discussed.