The effects of the process parameters of TIG （tungsten inset gas）-flux welding on the welds morphology, angular distortion, ferrite content and hot cracking in austenitic stainless steel were investigated. Autogenou...The effects of the process parameters of TIG （tungsten inset gas）-flux welding on the welds morphology, angular distortion, ferrite content and hot cracking in austenitic stainless steel were investigated. Autogenous TIG welding process was applied to the type 304 stainless steel through a thin layer of activating flux to produce a bead on plate welded joint. TiO2, SiO2, Fe2O3, Cr2O3, ZnO and MnO2 were used as the activating fluxes. The experimental results indicated that the TIG-flux welding can increase the weld depth/width ratio and reduce the HAZ （heat affected zone） range, and therefore the angular distortion of the weldment can be reduced. It was also found that the retained ferrite content within the TIG-flux welds is increased, and has a beneficial effect in reducing hot cracking tendency for stainless steels of the austenitic type weld metals. A plasma column constriction increases the current density at the anode spot and then a substantial increase in penetration of the TIG-flux welds can be obtained.展开更多
文摘The effects of the process parameters of TIG （tungsten inset gas）-flux welding on the welds morphology, angular distortion, ferrite content and hot cracking in austenitic stainless steel were investigated. Autogenous TIG welding process was applied to the type 304 stainless steel through a thin layer of activating flux to produce a bead on plate welded joint. TiO2, SiO2, Fe2O3, Cr2O3, ZnO and MnO2 were used as the activating fluxes. The experimental results indicated that the TIG-flux welding can increase the weld depth/width ratio and reduce the HAZ （heat affected zone） range, and therefore the angular distortion of the weldment can be reduced. It was also found that the retained ferrite content within the TIG-flux welds is increased, and has a beneficial effect in reducing hot cracking tendency for stainless steels of the austenitic type weld metals. A plasma column constriction increases the current density at the anode spot and then a substantial increase in penetration of the TIG-flux welds can be obtained.