High-nitrogen nickel-free stainless steels were fabricated by the metal injection molding technique using high nitrogen alloying powders and a mixture of three polymers as binders.Mixtures of metal powders and binders...High-nitrogen nickel-free stainless steels were fabricated by the metal injection molding technique using high nitrogen alloying powders and a mixture of three polymers as binders.Mixtures of metal powders and binders with various proportions were also investigated, and an optimum powder loading capacity was determined as 64vol%.Intact injection molded compacts were successfully obtained by regulating the processing parameters.The debinding process for molded compacts was optimized with a combination of thermo-gravimetric analysis and differential scanning calorimetry analysis.An optimum relative density and nitrogen content of the specimens are obtained at 1360℃,which are 97.8%and 0.79wt%,respectively.展开更多
Polycrystalline CuInS2 （CIS） films were prepared by sulphurization of Cu-In films. The surface morphology and phase composition of the as-grown film, the KCN-etched film, and the annealed KCN-etched film were invest...Polycrystalline CuInS2 （CIS） films were prepared by sulphurization of Cu-In films. The surface morphology and phase composition of the as-grown film, the KCN-etched film, and the annealed KCN-etched film were investigated. During the sulphurization, the secondary CuxS phase segregated on the surface of the as-grown films. To improve the crystalline quality of CuInS2 films, a series of post-grown treatments, such as KCN-etching and vacuum annealing KCN-etched films, were performed on the as-grown films. Both as-grown and post-treated films were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. The results indicated that a CuxS secondary phase segregated on the surface of the as-grown film, which could be removed effectively by KCN etching. After the vacuum annealing treatment, the KCN-etched film had a sphalerite structure with （112） preferred orientation. Meanwhile, the crystalline quality of the CIS film was significantly improved, which provided a novel method to improve the performance of thin film solar cells.展开更多
γ-CuI thin films were prepared by a spraying method using acetonitrile as a solvent,CuI and iodine as reagents.The influences of substrate temperature on the structure,topography,and optical properties of CuI films w...γ-CuI thin films were prepared by a spraying method using acetonitrile as a solvent,CuI and iodine as reagents.The influences of substrate temperature on the structure,topography,and optical properties of CuI films were investigated.Scanning electron microscope（SEM） photos revealed that the shape and grain size of CuI grains were related to substrate temperature.X-ray diffraction results showed that substrate temperature affected the crystalline quality of CuI films.When the substrate temperature was 110°C,CuI thin films showed γ-phase zinkblende structure with（111） preferred orientation.The dimension of the globular CuI crystallite was approximately 35 nm,the energy band gap was 2.97 eV,the maximum transmittance was 87.3% in the part of the visible region,and the open circuit voltage was close to 380 mV.This opened a route for a cadmium-free buffer layer for CuInS2 solar cells.展开更多
A novel method was reported to measure the remnant magnetic field in Lorentz mode in a FEI Tecnai F20 transmission electron microscope equipped with a Lorentz lens. The movement of the circle Bloch line of the cross-t...A novel method was reported to measure the remnant magnetic field in Lorentz mode in a FEI Tecnai F20 transmission electron microscope equipped with a Lorentz lens. The movement of the circle Bloch line of the cross-tie wall in Permalloy is used to measure the remnant magnetic field by tilting the specimen and adjusting the objective lens current. The remnant magnetic field is estimated to be about 17 Oe, in a direction opposite to that of the objective lens magnetic field. The remnant magnetic field can be compensated by adjusting the value of the objective lens current.展开更多
基金supported by the National High-Tech Research and Development Program of China(No.2006AA03Z502)
文摘High-nitrogen nickel-free stainless steels were fabricated by the metal injection molding technique using high nitrogen alloying powders and a mixture of three polymers as binders.Mixtures of metal powders and binders with various proportions were also investigated, and an optimum powder loading capacity was determined as 64vol%.Intact injection molded compacts were successfully obtained by regulating the processing parameters.The debinding process for molded compacts was optimized with a combination of thermo-gravimetric analysis and differential scanning calorimetry analysis.An optimum relative density and nitrogen content of the specimens are obtained at 1360℃,which are 97.8%and 0.79wt%,respectively.
基金the National High-Tech Research and Development Program of China (No. 2006AA03Z2370)
文摘Polycrystalline CuInS2 （CIS） films were prepared by sulphurization of Cu-In films. The surface morphology and phase composition of the as-grown film, the KCN-etched film, and the annealed KCN-etched film were investigated. During the sulphurization, the secondary CuxS phase segregated on the surface of the as-grown films. To improve the crystalline quality of CuInS2 films, a series of post-grown treatments, such as KCN-etching and vacuum annealing KCN-etched films, were performed on the as-grown films. Both as-grown and post-treated films were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. The results indicated that a CuxS secondary phase segregated on the surface of the as-grown film, which could be removed effectively by KCN etching. After the vacuum annealing treatment, the KCN-etched film had a sphalerite structure with （112） preferred orientation. Meanwhile, the crystalline quality of the CIS film was significantly improved, which provided a novel method to improve the performance of thin film solar cells.
基金supported by Beijing Municipal Natural Science Foundation (No.2091003)
文摘γ-CuI thin films were prepared by a spraying method using acetonitrile as a solvent,CuI and iodine as reagents.The influences of substrate temperature on the structure,topography,and optical properties of CuI films were investigated.Scanning electron microscope（SEM） photos revealed that the shape and grain size of CuI grains were related to substrate temperature.X-ray diffraction results showed that substrate temperature affected the crystalline quality of CuI films.When the substrate temperature was 110°C,CuI thin films showed γ-phase zinkblende structure with（111） preferred orientation.The dimension of the globular CuI crystallite was approximately 35 nm,the energy band gap was 2.97 eV,the maximum transmittance was 87.3% in the part of the visible region,and the open circuit voltage was close to 380 mV.This opened a route for a cadmium-free buffer layer for CuInS2 solar cells.
基金supported by National Natural Science Foundation of China(No.10776037)
文摘A novel method was reported to measure the remnant magnetic field in Lorentz mode in a FEI Tecnai F20 transmission electron microscope equipped with a Lorentz lens. The movement of the circle Bloch line of the cross-tie wall in Permalloy is used to measure the remnant magnetic field by tilting the specimen and adjusting the objective lens current. The remnant magnetic field is estimated to be about 17 Oe, in a direction opposite to that of the objective lens magnetic field. The remnant magnetic field can be compensated by adjusting the value of the objective lens current.