A coupled thermodynamic model of inclusions precipitation both in liquid and solid phase and microseg- regation of solute elements during solidification of heat-resistant steel containing cerium was established. Then ...A coupled thermodynamic model of inclusions precipitation both in liquid and solid phase and microseg- regation of solute elements during solidification of heat-resistant steel containing cerium was established. Then the model was validated by the SEM analysis of the industrial products. The type and amount of inclusions in solidifica- tion structure of 253MA heat-resistant steel were predicted by the model, and the valuable results for the inclusions controlling in 253MA steel were obtained. When the cerium addition increases, the types of inclusions transform from SiO2 and MnS to Ce2 O3 and Ce2O2 S in 253MA steel and the precipitation temperature of SiO2 and MnS decrea- ses. The inclusions CeS and CeN convert to Ce2 O3 and Ce2 O2 S as the oxygen content increases and Ce2 O3 and CeN convert to Ce2 O2 S, Ce3 S4, and MnS as the sulfur content increases. The formation temperature of SiO2 increases when the oxygen content increases and the MnS precipitation temperature increases when the sulfur content increa ses. There is only a small quantity of inclusions containing cerium in 253MA steel with high cleanliness, i. e. , low oxygen and sulfur contents. By contrast, a mass of SiO2 , MnS and Ce2 O2 S are formed in steel when the oxygen and sulfur contents are high enough. The condition that MnS precipitates in 253MA steel is 1.2wEo[O] ＋W[s]〉0. 01% and SiO2 precipitates when 2w[O] ＋wrs[S]〉0. 017% （W[S]0. 005%） and w[O]〉0. 006% （w[S]〉0. 005%）.展开更多
基金Sponsored by National Key Basic Research Program of China(2012CB626812)National Natural Science Foundation of China(51104039)Program for New Century Excellent Talents in University of Ministry of Education of China(NCET-11-0077)
文摘A coupled thermodynamic model of inclusions precipitation both in liquid and solid phase and microseg- regation of solute elements during solidification of heat-resistant steel containing cerium was established. Then the model was validated by the SEM analysis of the industrial products. The type and amount of inclusions in solidifica- tion structure of 253MA heat-resistant steel were predicted by the model, and the valuable results for the inclusions controlling in 253MA steel were obtained. When the cerium addition increases, the types of inclusions transform from SiO2 and MnS to Ce2 O3 and Ce2O2 S in 253MA steel and the precipitation temperature of SiO2 and MnS decrea- ses. The inclusions CeS and CeN convert to Ce2 O3 and Ce2 O2 S as the oxygen content increases and Ce2 O3 and CeN convert to Ce2 O2 S, Ce3 S4, and MnS as the sulfur content increases. The formation temperature of SiO2 increases when the oxygen content increases and the MnS precipitation temperature increases when the sulfur content increa ses. There is only a small quantity of inclusions containing cerium in 253MA steel with high cleanliness, i. e. , low oxygen and sulfur contents. By contrast, a mass of SiO2 , MnS and Ce2 O2 S are formed in steel when the oxygen and sulfur contents are high enough. The condition that MnS precipitates in 253MA steel is 1.2wEo[O] ＋W[s]〉0. 01% and SiO2 precipitates when 2w[O] ＋wrs[S]〉0. 017% （W[S]0. 005%） and w[O]〉0. 006% （w[S]〉0. 005%）.
