The cooling rate sensitivities of A1TiB, RE and A1TiB-RE refiners were investigated using laboratory experiments and the actual industrial applications of A356 automotive wheel via low pressure die casting technology....The cooling rate sensitivities of A1TiB, RE and A1TiB-RE refiners were investigated using laboratory experiments and the actual industrial applications of A356 automotive wheel via low pressure die casting technology. Their impact mechanisms on the microstructure and mechanical properties of the A356 alloy were discussed. The results demonstrated that the AITiB-RE refiner possessed most effective and synergetic refinement effects compared to the individual A1TiB or RE refiners. The A1TiB-RE refiner exhibited the least sensitivity to the cooling rate changes than the other refiners. The comprehensive properties of alloy wheel refined by the A1TiB-RE refiner were improved significantly. The tensile strength, yield strength, and elongation of wheel spoke improved by approximately 11.3%, 10.8% and 44.1%, respectively. The property difference values of the tensile strength, yield strength, and elongation in different positions of the wheel decreased from 14.8%, 31.2% and 47.7% to 8.6%, 27.1% and 30.9%, respectively.展开更多
The effect of open porosity of Y2O3ceramic on the apparent contact angle and interaction between molten Ti47 Al alloy and Y2O3ceramic substrates under pure Ar was investigated by using a sessile drop method at 1600 &#...The effect of open porosity of Y2O3ceramic on the apparent contact angle and interaction between molten Ti47 Al alloy and Y2O3ceramic substrates under pure Ar was investigated by using a sessile drop method at 1600 °C. As the open porosity increased from 9.6% to 30.3%, the spreading rate of molten Ti47 Al alloys on Y2O3ceramic substrates reduced from 2.3 to 1.1°/s; meanwhile, the final equilibrium contact angles increased from 55.8° to 63.6°. The microstructure observations revealed that with increasing the open porosity of the Y2O3substrates, the thickness of sand adhesion at the interfaces of the alloy droplets increased from 5.4 to 15.7 lm, and ceramic particles in the alloy matrix increased as well. The increasing contact area between the molten alloy and the substrate played a dominant role in determining the interaction on Ti Al/Y2O3interface.展开更多
基金financially supported by the National High Technology Research and Development Program(No.2013AA031002)
文摘The cooling rate sensitivities of A1TiB, RE and A1TiB-RE refiners were investigated using laboratory experiments and the actual industrial applications of A356 automotive wheel via low pressure die casting technology. Their impact mechanisms on the microstructure and mechanical properties of the A356 alloy were discussed. The results demonstrated that the AITiB-RE refiner possessed most effective and synergetic refinement effects compared to the individual A1TiB or RE refiners. The A1TiB-RE refiner exhibited the least sensitivity to the cooling rate changes than the other refiners. The comprehensive properties of alloy wheel refined by the A1TiB-RE refiner were improved significantly. The tensile strength, yield strength, and elongation of wheel spoke improved by approximately 11.3%, 10.8% and 44.1%, respectively. The property difference values of the tensile strength, yield strength, and elongation in different positions of the wheel decreased from 14.8%, 31.2% and 47.7% to 8.6%, 27.1% and 30.9%, respectively.
基金support of the‘‘National Science&Technology Pillar Program of China’’project of PR China(No.2013BAB11B04)the National Natural Science Foundation of China(Grant No.51404017)the State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technolog
文摘The effect of open porosity of Y2O3ceramic on the apparent contact angle and interaction between molten Ti47 Al alloy and Y2O3ceramic substrates under pure Ar was investigated by using a sessile drop method at 1600 °C. As the open porosity increased from 9.6% to 30.3%, the spreading rate of molten Ti47 Al alloys on Y2O3ceramic substrates reduced from 2.3 to 1.1°/s; meanwhile, the final equilibrium contact angles increased from 55.8° to 63.6°. The microstructure observations revealed that with increasing the open porosity of the Y2O3substrates, the thickness of sand adhesion at the interfaces of the alloy droplets increased from 5.4 to 15.7 lm, and ceramic particles in the alloy matrix increased as well. The increasing contact area between the molten alloy and the substrate played a dominant role in determining the interaction on Ti Al/Y2O3interface.