The oxidation behaviors of fused zirconium diboride and chemosynthetic zirconium diboride as well as morphology and composition of their oxidation products were researched by FESEM-EDS and XRD.The two kinds of zirconi...The oxidation behaviors of fused zirconium diboride and chemosynthetic zirconium diboride as well as morphology and composition of their oxidation products were researched by FESEM-EDS and XRD.The two kinds of zirconium diboride were heated at 700℃,900℃,1100℃and 1300℃for 3 h in air,respectively.The results show that Zr02 and B203(Ⅰ)are generated from the chemosynthetic zirconium diboride oxidized at 700℃for 3 h or the fused zirconium diboride oxidized at 800℃for 24 h;B203(Ⅰ)dissolves into water and then H3B03 crystallizes.展开更多
Three groups of cylinder specimens(φ10 mm×10 mm)with 20%,30%and 40%(by mass,the same hereinafter)of ZrO2,were prepared using analytically pure MgO,Al2O3 and ZrO2 powders as the starting materials.The specimens w...Three groups of cylinder specimens(φ10 mm×10 mm)with 20%,30%and 40%(by mass,the same hereinafter)of ZrO2,were prepared using analytically pure MgO,Al2O3 and ZrO2 powders as the starting materials.The specimens were fired at 1600℃for 5 h,1700℃for 0 h and 1800℃for 7 h,respectively.The microstructure of the MgO-MgAl2O4-ZrO2 subsystem was studied by FESEM.The results show that(1)in the temperature range of 1600-1700℃,solid phase reactions happen in the MgO-MgAl2O4-ZrO2 subsystem,leaving three phases:periclase,spinel and ZrO2(solid dissolving with Mg2+)co-existing;spinellization affects the densification;(2)the specimen with 40%ZrO2 fired at 1800℃has heterogeneous melting microstructure;some areas form typical ternary eutectic MgO-MgAl2O4-ZrO2 with composition of MgO 35.2%-37.2%,Al2O324.2%-26.6%,and ZrO237.2%-39.8%.展开更多
文摘The oxidation behaviors of fused zirconium diboride and chemosynthetic zirconium diboride as well as morphology and composition of their oxidation products were researched by FESEM-EDS and XRD.The two kinds of zirconium diboride were heated at 700℃,900℃,1100℃and 1300℃for 3 h in air,respectively.The results show that Zr02 and B203(Ⅰ)are generated from the chemosynthetic zirconium diboride oxidized at 700℃for 3 h or the fused zirconium diboride oxidized at 800℃for 24 h;B203(Ⅰ)dissolves into water and then H3B03 crystallizes.
基金The author would like to thank Fu Qiuhua,Zhang Wei and Fan Qingsong for their surport to this work.
文摘Three groups of cylinder specimens(φ10 mm×10 mm)with 20%,30%and 40%(by mass,the same hereinafter)of ZrO2,were prepared using analytically pure MgO,Al2O3 and ZrO2 powders as the starting materials.The specimens were fired at 1600℃for 5 h,1700℃for 0 h and 1800℃for 7 h,respectively.The microstructure of the MgO-MgAl2O4-ZrO2 subsystem was studied by FESEM.The results show that(1)in the temperature range of 1600-1700℃,solid phase reactions happen in the MgO-MgAl2O4-ZrO2 subsystem,leaving three phases:periclase,spinel and ZrO2(solid dissolving with Mg2+)co-existing;spinellization affects the densification;(2)the specimen with 40%ZrO2 fired at 1800℃has heterogeneous melting microstructure;some areas form typical ternary eutectic MgO-MgAl2O4-ZrO2 with composition of MgO 35.2%-37.2%,Al2O324.2%-26.6%,and ZrO237.2%-39.8%.