Defect-free dissimilar Al/zinc coated steel and Al/AlSi coated steel welds were successfully fabricated by refill friction stir spot welding. However, Al alloy and uncoated steel could not be welded under the same wel...Defect-free dissimilar Al/zinc coated steel and Al/AlSi coated steel welds were successfully fabricated by refill friction stir spot welding. However, Al alloy and uncoated steel could not be welded under the same welding condition. Al-Zn eutectic layer formed at the Al/zinc coated steel interface showed nonuniformity in thickness and nanoscale intermetallic(IMC) produced was discontinuous. The bonding formation between the Al-Zn layer and the surrounding materials was attributed to a liquid/solid reaction mechanism. Bonding formation at Al alloy and AlSi coated steel interface was attributed to a solid/solid reaction mechanism, as the joining process did not involve with melting of base metals or AlSi coating materials. Kissing bond formed at the weld boundary acted as a crack initiation and propagation site,and the present study showed that weld strength of Al 5754/AlSi coated steel was greatly influenced by properties of original IMC layer.展开更多
基金supported by the Natural Science and Engineering Council(NSERC)of Canada,the Canadian Foundation for Innovation
文摘Defect-free dissimilar Al/zinc coated steel and Al/AlSi coated steel welds were successfully fabricated by refill friction stir spot welding. However, Al alloy and uncoated steel could not be welded under the same welding condition. Al-Zn eutectic layer formed at the Al/zinc coated steel interface showed nonuniformity in thickness and nanoscale intermetallic(IMC) produced was discontinuous. The bonding formation between the Al-Zn layer and the surrounding materials was attributed to a liquid/solid reaction mechanism. Bonding formation at Al alloy and AlSi coated steel interface was attributed to a solid/solid reaction mechanism, as the joining process did not involve with melting of base metals or AlSi coating materials. Kissing bond formed at the weld boundary acted as a crack initiation and propagation site,and the present study showed that weld strength of Al 5754/AlSi coated steel was greatly influenced by properties of original IMC layer.