In this work, the joining of aluminum to steel was conducted by ultrasound enhanced friction stir weld- ing （USE-FSW）. The power ultrasound was introduced into one of the metal sheets by an ultrasonic roll seam modu...In this work, the joining of aluminum to steel was conducted by ultrasound enhanced friction stir weld- ing （USE-FSW）. The power ultrasound was introduced into one of the metal sheets by an ultrasonic roll seam module synchronously to the FSW-process. The effect of the ultrasound on the resulting welds, their microstructure and their corrosion properties was investigated by light and scanning electron microscopy and corrosion investigations. The USE-FSW-joints showed less and smaller steel particles in the nugget zone as well as a thinner continuous intermetallic phase of FeAl3 at the interface. The nondestructive testing method of computed laminography proved the observations made by optic microscopy due to non-porous joints for both techniques. Corrosion investigations showed only low corrosion current densities and no enhanced galvanic corrosion for the EN AW-6061/DC04-hybrid joints in sodium chloride solution.展开更多
基金supported by the DFG Priority Program 1640:“Joining by plastic deformation”
文摘In this work, the joining of aluminum to steel was conducted by ultrasound enhanced friction stir weld- ing （USE-FSW）. The power ultrasound was introduced into one of the metal sheets by an ultrasonic roll seam module synchronously to the FSW-process. The effect of the ultrasound on the resulting welds, their microstructure and their corrosion properties was investigated by light and scanning electron microscopy and corrosion investigations. The USE-FSW-joints showed less and smaller steel particles in the nugget zone as well as a thinner continuous intermetallic phase of FeAl3 at the interface. The nondestructive testing method of computed laminography proved the observations made by optic microscopy due to non-porous joints for both techniques. Corrosion investigations showed only low corrosion current densities and no enhanced galvanic corrosion for the EN AW-6061/DC04-hybrid joints in sodium chloride solution.