Antibacterial ceramic was prepared by doping enamel slurry with composite phosphate inorganic antibacterial materials containing rare earth (inorganic antibacterial additives), and then the mechanisms for activating w...Antibacterial ceramic was prepared by doping enamel slurry with composite phosphate inorganic antibacterial materials containing rare earth (inorganic antibacterial additives), and then the mechanisms for activating water and improving seed germinative property were tested by nuclear magnetic resonance (NMR) and the method of testing oxygen dissolved in activated water. Results show that the half peak width of (()^(17)O-NMR) for tap water activated by the antibacterial ceramic drops from 115.36 to 99.15 Hz, and oxygen concentrations of activated water increase by 20%, germinate rate of horsebean and earthnut seeds increases by 12.5% and 7.5%, respectively. Therefore antibacterial ceramic doped enamel slurry with inorganic antibacterial additives containing rare earth can reduce the volume of clusters of water molecules, improve activation of tap water, and promote plant seeds germinate.展开更多
Conventionally, an experimentally determined phase diagram requires studies of phase formation at a range of temperatures for each composition, which takes years of effort from multiple research groups. Combinatorial ...Conventionally, an experimentally determined phase diagram requires studies of phase formation at a range of temperatures for each composition, which takes years of effort from multiple research groups. Combinatorial materials chip technology, featuring high-throughput synthesis and characterization, is able to determine the phase diagram of an entire composition spread of a binary or ternary system at a single temperature on one materials library, which, though significantly increasing efficiency, still requires many libraries processed at a series of temperatures in order to complete a phase diagram. In this paper, we propose a "one-chip method" to construct a complete phase diagram by individually synthesizing each pixel step by step with a progressive pulse of energy to heat at different temperatures while monitoring the phase evolution on the pixel in situ in real time. Repeating this process pixel by pixel throughout the whole chip allows the entire binary or ternary phase diagram to be mapped on one chip in a single experiment. The feasibility of this methodology is demonstrated in a study of a Ge-Sb-Te ternary alloy system, on which the amorphouscrystalline phase boundary is determined.展开更多
The fused cast alumina-zirconia-silica(AZS)refractory is an indispensable material of the glass melting furnace,because of its outstanding corrosion resistance and low pollution to glass production.The exudation is on...The fused cast alumina-zirconia-silica(AZS)refractory is an indispensable material of the glass melting furnace,because of its outstanding corrosion resistance and low pollution to glass production.The exudation is one important index to evaluate the performance of fused cast AZS refractory products.In order to study the effects of chemical composition and microstructure on the exudation of fused cast AZS refractory materials,three types of fused-cast AZS refractory bricks(AZS33#,AZS36#and AZS41#)were selected from several companies as the research object,and their composition,bulk density,apparent porosity,the value of exudation,static corrosion rate and microstructure were discussed.The results show that the chemical composition,especially the content of SiO2 and Na2O,and the distribution of zirconia would greatly affect the content and viscosity of glass phase,thus affecting the glass exudation.This work will provide technical reference for the development of low exudation AZS refractories.展开更多
Based on the principle of ENV 196-4 "Methods of testing cement - Part 4 Quantitative determination of constituents or Chinese Standard GB/12960-2007 Quantitative measurement of mineral admixtures in cement, methods w...Based on the principle of ENV 196-4 "Methods of testing cement - Part 4 Quantitative determination of constituents or Chinese Standard GB/12960-2007 Quantitative measurement of mineral admixtures in cement, methods were developed for quantitative determination of fly ash, slag and limestone powder in fresh cement pastes, mortars and concretes. Limestone powder was determined using thermal analysis method. The residue content of fly ash on an 80um sieve, and silt contents of aggregate were also considered during the quantitative determination of mineral composition of quaternary cementitious system. With the developed methods, the deviations between the measured and the actual mineral contents of the constituent in the eemantitious material in fresh cement paste, mortar and concrete, were within 3%.展开更多
Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland c...Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland cement,which are applied during the hot-stage pretreatment with simulated gas for raw steel slag or the accelerated carbonation curing of slurry.The mechanical strengths,carbonate products,microstructures and CO_(2) uptakes were quantitatively investigated.Results manifest that accelerated carbonation curing increases the compressive strengths of steel slag slurry,from 17.1 MPa (binder of 80 wt% EAF and 20 wt%cement under standard moisture curing) to 36.0 MPa (binder of 80 wt%EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 52%.In contrast,hot-stage carbonation applied during the pretreatment of steel slag increases the compressive strengths to 43.7 MPa (binder of 80 wt%carbonated EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 67%.Hotstage carbonation of steel slag is found for particle agglomeration,minerals remodeling and calcite formed,thus causing an activated steel slag with a dense structure and more active components.Accelerated carbonation curing of steel slag slurry paste results in the newly formed amorphous CaCO_(3),calcite crystalline and silica gels that covered the pores of the matrix,facilitating microstructure densification and strength improvement.Adopting the combinative methods of the hot-stage CO_(2) pretreatment and accelerated carbonation curing creates a promising high-volume steel slag-based binder with high strengths and CO_(2) storage.展开更多
Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service li...Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service life of the regenerator checker body,the slag chemical composition and alkali-sulfur ratio of glass tanks after using petrol coke and the damage mechanism of the residual magnesia bricks in the regenerator checker body were studied,as well as the corrosion resistance of three magnesia based bricks(direct bonded magnesia chrome bricks,fused rebonded magnesia chrome bricks,and fused rebonded high-purity magnesium aluminate spinel bricks).On this basis,a series of targeted countermeasures were adopted to optimize the configuration of refractories,significantly improving the service life of checker bricks and meeting the requirements of glass industry development.展开更多
Zirconium-based metal-organic framework UiO-66 was successfully prepared by solvothermal method,and UiO-66 was modified by adding regulators such as formic acid,acetic acid,and hydrochloric acid.The NH_(3)-SCR reactiv...Zirconium-based metal-organic framework UiO-66 was successfully prepared by solvothermal method,and UiO-66 was modified by adding regulators such as formic acid,acetic acid,and hydrochloric acid.The NH_(3)-SCR reactivity of the samples was evaluated by the denitration activity evaluation system,and the UiO-66 and the regulator-modified UiO-66 were characterized by XRD,SEM,BET,FTIR,TG,NH_(3)-TPD,etc.,the effects of regulator types on the structure and properties of UiO-66 were investigated.The experimental results show that,after adding the modifier,the morphology of UiO-66 changes from irregular quadrilateral with serious agglomeration to particles with regular crystal shape and good dispersibility,and the crystal morphology of the catalyst is improved.In addition,after adding the modifier,UiO-66 has a larger specific surface area and stronger surface acidity,which optimizes the catalytic performance of UiO-66.The catalytic performance test results of NH_(3)-SCR show that the low-temperature activity of UiO-66 is poor,and it only shows a certain catalytic activity at higher temperatures.The catalytic activity of UiO-66 was significantly improved after adding the regulator.Among them,the UiO-66-HCl modified with hydrochloric acid had the best catalytic activity,and the denitration rate reached 70%when the denitration temperature was 380℃.展开更多
To study the effect of atmospheric pressure on the properties of fresh and hardened airentrained concrete, three kinds of air entraining agents were used for preparing air-entrained concrete in the plateaus(Lhasa, 61 ...To study the effect of atmospheric pressure on the properties of fresh and hardened airentrained concrete, three kinds of air entraining agents were used for preparing air-entrained concrete in the plateaus(Lhasa, 61 kPa) and the plains(Beijing, 101 kPa). Air content, slump, compressive strength and pore structure of the three air-entrained concretes were tested in these two places. It is found that the air content of concrete under low atmospheric pressure(LAP) is 4%-36% lower than that of concrete under normal atmospheric pressure(NAP), which explaines the decrease of slump for air-entrained concrete under LAP. Pore number of hardened concrete under LAP is reduced by 48%-69%. While, the proportion of big pores(pore diameter >1 200 μm) and air void spacing factor are increased by 1.5%-7.3% and 51%-92%, respectively. The deterioration of pore structure results in a 3%-9% reduction in the compressive strength of concrete. From the results we have obtained, it can be concluded that the increase of critical nucleation energy of air bubbles and the decrease of volumetric compressibility coefficient of air in the concrete are responsible for the variation of air content and pore structure of concrete under LAP.展开更多
The effects of activated coal gangue on compressive strength, porosity and pore size distribution of hardened cement pastes were investigated. Activated coal gangue with two different kaolin contents, one higher and o...The effects of activated coal gangue on compressive strength, porosity and pore size distribution of hardened cement pastes were investigated. Activated coal gangue with two different kaolin contents, one higher and one lower, were used to partially replace Portland cement at 0%, 10%, and 30% by weight. The water to binder ratio(w/b) of 0.5 was used for all the blended cement paste mixes. Experimental results indicate that the blended cement of activated coal gangue mortar with higher kaolin mineral content has a higher compressive strength than that with lower kaolin mineral content. The porosity and pore size of blended cement mortar were significantly affected by the replacement of activated coal gangue.展开更多
The split Hopkinson pressure bar (SHPB) testing with diameter 40 mm was used to investigate the dynamic mechanical properties of engineered cementitious composites (ECCs) with different fly ash content. The basic ...The split Hopkinson pressure bar (SHPB) testing with diameter 40 mm was used to investigate the dynamic mechanical properties of engineered cementitious composites (ECCs) with different fly ash content. The basic properties including deformation, energy absorption capacity, strain-stress relationship and failure patterns were discussed. The ECCs showed strain-rate dependency and kept better plastic flow during impact process compared with reactive powder concrete (RPC) and concrete, but the critical compressive strength was lower than that of RPC and concrete. The bridging effect of PVA fiber and addition of fly ash can significantly improve the deformation and energy absorption capacities of ECCs. With the increase of fly ash content in ECCs, the static and dynamic compressive strength lowered and the dynamic increase factor enhanced. Therefore, to meet different engineering needs, the content of fly ash can be an important index to control the static and dynamic mechanical properties of ECCs.展开更多
In order to improve the mechanical properties and Greenness of engineered cementitious composites (ECC),four-point bending test,compressive strength and flexural strength test were employed to analyze the effects of f...In order to improve the mechanical properties and Greenness of engineered cementitious composites (ECC),four-point bending test,compressive strength and flexural strength test were employed to analyze the effects of fly ash content on the mechanical properties of.ECC.The replacement ratio of cement with fly ash was 50%,60%,70% and 80%,respectively.The experimental results indicate that ECCs with high volume fly ash still remained the characteristic of pseudo-strain hardening and the mid-span deflection in four-point bending test increase remarkably by adding more fly ash.The observations of ECCs indicate that the multiple cracks are saturated and the crack width is relatively smaller for higher volume fly ash ECC,owing to the lower strength of matrix and the improvement ofinterface bonding.Fly ash reduces the compressive strength and flexural strength of ECC at all ages.Therefore,as the compressive strength could meet the requirement of practical engineering,employing the higher volume fly ash ECCs would benefit to obtain relatively high ductility.展开更多
The internal curing effect of superabsorbent polymer(SAP) on the properties of high performance concrete(HPC) under marine wetting and drying cycles(WD cycles) was investigated. Compressive strength, hydration and chl...The internal curing effect of superabsorbent polymer(SAP) on the properties of high performance concrete(HPC) under marine wetting and drying cycles(WD cycles) was investigated. Compressive strength, hydration and chloride migration were experimentally investigated and the results were evaluated by compasison with those under fresh water curing(FW). Water absorption and porosity were also evaluated only under WD cycles. The results showed the important influence of wetting and drying cycles on the properties of SAP modified HPC properties. Carefully designed, SAP minimized the long-term compressive strength of HPC under marine WD cycles. The hydration rate was faster in the initial curing, but became lower as compared with that cured in FW. In addition, SAP improved the long-term water absorption resistance and chloride migration resistance of HPC under marine WD cycles. The examination of the porosity showed a lower increase of the volume of capillary pores in SAP modified HPC under long term WD cycles compared with that without SAP. Therefore, internal curing by SAP could improve the durability properties of HPC under marine WD cycles.展开更多
The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry (MIP),X-ray diffraction (XRD) and diff...The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry (MIP),X-ray diffraction (XRD) and differential thermal analysis (DTA).Results show that ground steel-making slag is a kind of high activity mineral additives and it can raise the longer-age strength of OPC mortar.The total porosity and average pore diameter of OPC paste with ground steel-making slag increase with the increase of the amount of ground steel-making slag replacing OPC at various ages,while after 28 days most pores in OPC paste with ground steel-making slag do not influence the strength because the diameter of those pores is in the rang of 20 to 50nm.The hydration mechanism of ground steel-making slag is similar to that of OPC but different from that of fly ash and blast furnace slag.The hydration products of ground steel-making slag contain quite a lot of Ca(OH) 2 in long age.展开更多
ITO thin films were grown on PC(polycarbonate), PMMA(polymethyl methacrylate) and glass substrates by r.f. magnetron sputtering. The electrical, structural and chemical characteristics of ITO films were analyzed b...ITO thin films were grown on PC(polycarbonate), PMMA(polymethyl methacrylate) and glass substrates by r.f. magnetron sputtering. The electrical, structural and chemical characteristics of ITO films were analyzed by the Hall Technique, X-ray diffraction, and X-ray photoelectron spectroscopy. XPS studies suggest that all the ITO films consist of crystalline and amorphous phases. The degree of crystallinity increases from less than 45% to more than 90% when the substrate temperature increases from 80 to 300 ℃. The In and Sn exist in the chemical state of In^3+ and Sn^4+, respectively, independent of substrate type and temperature. The enrichment of Sn on surface and In in body of ITO films are also revealed. And, the oxygen deficient regions exist both in surface layer and film body. For ITO films deposited under 180 ℃ , the carrier concentration are mainly provided by oxygen vacancies, and the dominant electron carrier scattering mechanism is grain boundary scattering between the crystal and the amorphous grain. For ITO films deposited over 180 ℃, the carrier concentration are provided by tin doping, and the dominant scattering mechanism transforms from grain boundary scattering between the crystal grains to ionized impurity scattering with increasing deposition temperature.展开更多
Workability and mechanical properties of steel slag green concrete with different types of steel slag and different dosages of admixtures were investigated. The effectiveness of steel slag powder on suppressing alkali...Workability and mechanical properties of steel slag green concrete with different types of steel slag and different dosages of admixtures were investigated. The effectiveness of steel slag powder on suppressing alkali aggregate reaction(AAR) expansion was assessed using the method of ASTM C441 and accelerated test method. Experimental results show that mechanical properties can be improved further due to the synergistic effect and mutual activation when compound mineral admixtures with steel slag powder and blast-furnace slag powder are mixed into concrete. In addition,about 50% decrease in expansion rate of mortar bars with mineral admixtures can be achieved in AAR tests. Mineral admixtures with steel slag powder as partial replacement for Portland cement in concrete is an effective means for controlling expansion due to AAR.展开更多
The effects of water/binder ratio (w/b) on the toughness behavior, compressive strength and flexural strength of engineered cementitious composites (ECC) were investigated. The w/b ratios of 0.25, 0.31, 0.33 and 0...The effects of water/binder ratio (w/b) on the toughness behavior, compressive strength and flexural strength of engineered cementitious composites (ECC) were investigated. The w/b ratios of 0.25, 0.31, 0.33 and 0.37 were selected and the specimens were tested at the ages of 7 d and 28 d. The experimental results showed that there was a corresponding increase in first cracking strength, modulus of rupture, compressive strength and flexural strength with the decrease of w/b. Within the w/b range of 0.25-0.37, higher w/b was found to have improved effects on deflection, strain hardening index and toughness index of ECC. In the permission of meeting the requirement of compressive strength grade, selecting higher w/b in mix design will help to obtain robust ECC.展开更多
Developing high-performance non-precious metal electrocatalysts for oxygen reduction reaction(ORR)is crucial for the commercialization of fuel cells and metal-air batteries.However,doped carbon-based materials only sh...Developing high-performance non-precious metal electrocatalysts for oxygen reduction reaction(ORR)is crucial for the commercialization of fuel cells and metal-air batteries.However,doped carbon-based materials only show good ORR activity in alkaline medium,and become less effective in acidic environment.We believe that an appropriate combination of both ionic and electronic transport path,and well dopant distribution of doped carbon-based materials would help to realize high ORR performance un-der both acidic and alkaline cond让ions.Accordingly,a nitrogen and sulfur co-doped carbon framework with hierarchical through-hole structure is fabricated by morphology-controlled solid-state pyrolysis of poly(aniline-co-2-ami no thiophenol)foam.The uniform high concentrations of nitrogen and sulfur,high intrinsic conductivity,and integrated three dimensional ionic and electronic transfer passageways of the 3D porous structure lead to synergistic effects in catalyzing ORR.As a result,the limiting current density of the carbonized poly(aniline-co-2-aminothiophenol)foam is equivalent to commercial Pt/C in acidic environment,and twice the latter in alkaline medium.展开更多
Zirconia aqueous slurry was prepared with fine zirconia powder. Injection process for making zirconia fiber was demonstrated, including preparation of aqueous slurry, injection of slurry, fiber setting in acetone, and...Zirconia aqueous slurry was prepared with fine zirconia powder. Injection process for making zirconia fiber was demonstrated, including preparation of aqueous slurry, injection of slurry, fiber setting in acetone, and fiber firing. The principle of the process was discussed. The effects of solid loading in the zirconia slurry, addition of dispersant in the slurry, and ball milling time on the rheological properties of the slurry, especially yield stress, were illustrated. The role of acetone as curing agent was discussed. Zirconia poly-crystalline fiber with its density of 6. 05 g · cm^-3 was obtained after sintering at 1 530 ℃ for 5 h. Microstructure of the sintered zirconia fiber was investigated.展开更多
文摘Antibacterial ceramic was prepared by doping enamel slurry with composite phosphate inorganic antibacterial materials containing rare earth (inorganic antibacterial additives), and then the mechanisms for activating water and improving seed germinative property were tested by nuclear magnetic resonance (NMR) and the method of testing oxygen dissolved in activated water. Results show that the half peak width of (()^(17)O-NMR) for tap water activated by the antibacterial ceramic drops from 115.36 to 99.15 Hz, and oxygen concentrations of activated water increase by 20%, germinate rate of horsebean and earthnut seeds increases by 12.5% and 7.5%, respectively. Therefore antibacterial ceramic doped enamel slurry with inorganic antibacterial additives containing rare earth can reduce the volume of clusters of water molecules, improve activation of tap water, and promote plant seeds germinate.
基金supported in part by National High Technology Research and Development Program (2015AA034204)the National Natural Science Foundation of China (51472044)
文摘Conventionally, an experimentally determined phase diagram requires studies of phase formation at a range of temperatures for each composition, which takes years of effort from multiple research groups. Combinatorial materials chip technology, featuring high-throughput synthesis and characterization, is able to determine the phase diagram of an entire composition spread of a binary or ternary system at a single temperature on one materials library, which, though significantly increasing efficiency, still requires many libraries processed at a series of temperatures in order to complete a phase diagram. In this paper, we propose a "one-chip method" to construct a complete phase diagram by individually synthesizing each pixel step by step with a progressive pulse of energy to heat at different temperatures while monitoring the phase evolution on the pixel in situ in real time. Repeating this process pixel by pixel throughout the whole chip allows the entire binary or ternary phase diagram to be mapped on one chip in a single experiment. The feasibility of this methodology is demonstrated in a study of a Ge-Sb-Te ternary alloy system, on which the amorphouscrystalline phase boundary is determined.
文摘The fused cast alumina-zirconia-silica(AZS)refractory is an indispensable material of the glass melting furnace,because of its outstanding corrosion resistance and low pollution to glass production.The exudation is one important index to evaluate the performance of fused cast AZS refractory products.In order to study the effects of chemical composition and microstructure on the exudation of fused cast AZS refractory materials,three types of fused-cast AZS refractory bricks(AZS33#,AZS36#and AZS41#)were selected from several companies as the research object,and their composition,bulk density,apparent porosity,the value of exudation,static corrosion rate and microstructure were discussed.The results show that the chemical composition,especially the content of SiO2 and Na2O,and the distribution of zirconia would greatly affect the content and viscosity of glass phase,thus affecting the glass exudation.This work will provide technical reference for the development of low exudation AZS refractories.
基金Funded by the National Natural Science Foundation of China(50978093 and 51072050)the National Key Research Program(973 Project)(No.2009CB6231001)
文摘Based on the principle of ENV 196-4 "Methods of testing cement - Part 4 Quantitative determination of constituents or Chinese Standard GB/12960-2007 Quantitative measurement of mineral admixtures in cement, methods were developed for quantitative determination of fly ash, slag and limestone powder in fresh cement pastes, mortars and concretes. Limestone powder was determined using thermal analysis method. The residue content of fly ash on an 80um sieve, and silt contents of aggregate were also considered during the quantitative determination of mineral composition of quaternary cementitious system. With the developed methods, the deviations between the measured and the actual mineral contents of the constituent in the eemantitious material in fresh cement paste, mortar and concrete, were within 3%.
基金Funded by the National Key Research and Development Program of China-Intergovernmental International Cooperation in Scientific and Technological Innovation MOST,China (No.2018YFE0107300)。
文摘Two carbonation approaches are considered for studying the effects on the hardening mechanisms of slurries made of 100 wt%electric arc furnace steel slag (EAF) slag or 80 wt%EAF slag incorporating 20 wt% of Portland cement,which are applied during the hot-stage pretreatment with simulated gas for raw steel slag or the accelerated carbonation curing of slurry.The mechanical strengths,carbonate products,microstructures and CO_(2) uptakes were quantitatively investigated.Results manifest that accelerated carbonation curing increases the compressive strengths of steel slag slurry,from 17.1 MPa (binder of 80 wt% EAF and 20 wt%cement under standard moisture curing) to 36.0 MPa (binder of 80 wt%EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 52%.In contrast,hot-stage carbonation applied during the pretreatment of steel slag increases the compressive strengths to 43.7 MPa (binder of 80 wt%carbonated EAF and 20 wt%cement under accelerated carbonation curing),with a CO_(2) uptake of 67%.Hotstage carbonation of steel slag is found for particle agglomeration,minerals remodeling and calcite formed,thus causing an activated steel slag with a dense structure and more active components.Accelerated carbonation curing of steel slag slurry paste results in the newly formed amorphous CaCO_(3),calcite crystalline and silica gels that covered the pores of the matrix,facilitating microstructure densification and strength improvement.Adopting the combinative methods of the hot-stage CO_(2) pretreatment and accelerated carbonation curing creates a promising high-volume steel slag-based binder with high strengths and CO_(2) storage.
文摘Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service life of the regenerator checker body,the slag chemical composition and alkali-sulfur ratio of glass tanks after using petrol coke and the damage mechanism of the residual magnesia bricks in the regenerator checker body were studied,as well as the corrosion resistance of three magnesia based bricks(direct bonded magnesia chrome bricks,fused rebonded magnesia chrome bricks,and fused rebonded high-purity magnesium aluminate spinel bricks).On this basis,a series of targeted countermeasures were adopted to optimize the configuration of refractories,significantly improving the service life of checker bricks and meeting the requirements of glass industry development.
基金Funded by the National Key Research and Development Program of China(No.2016YFC0209302)。
文摘Zirconium-based metal-organic framework UiO-66 was successfully prepared by solvothermal method,and UiO-66 was modified by adding regulators such as formic acid,acetic acid,and hydrochloric acid.The NH_(3)-SCR reactivity of the samples was evaluated by the denitration activity evaluation system,and the UiO-66 and the regulator-modified UiO-66 were characterized by XRD,SEM,BET,FTIR,TG,NH_(3)-TPD,etc.,the effects of regulator types on the structure and properties of UiO-66 were investigated.The experimental results show that,after adding the modifier,the morphology of UiO-66 changes from irregular quadrilateral with serious agglomeration to particles with regular crystal shape and good dispersibility,and the crystal morphology of the catalyst is improved.In addition,after adding the modifier,UiO-66 has a larger specific surface area and stronger surface acidity,which optimizes the catalytic performance of UiO-66.The catalytic performance test results of NH_(3)-SCR show that the low-temperature activity of UiO-66 is poor,and it only shows a certain catalytic activity at higher temperatures.The catalytic activity of UiO-66 was significantly improved after adding the regulator.Among them,the UiO-66-HCl modified with hydrochloric acid had the best catalytic activity,and the denitration rate reached 70%when the denitration temperature was 380℃.
基金Funed by the National Key R&D Program of China(No.2017YFB0309903)
文摘To study the effect of atmospheric pressure on the properties of fresh and hardened airentrained concrete, three kinds of air entraining agents were used for preparing air-entrained concrete in the plateaus(Lhasa, 61 kPa) and the plains(Beijing, 101 kPa). Air content, slump, compressive strength and pore structure of the three air-entrained concretes were tested in these two places. It is found that the air content of concrete under low atmospheric pressure(LAP) is 4%-36% lower than that of concrete under normal atmospheric pressure(NAP), which explaines the decrease of slump for air-entrained concrete under LAP. Pore number of hardened concrete under LAP is reduced by 48%-69%. While, the proportion of big pores(pore diameter >1 200 μm) and air void spacing factor are increased by 1.5%-7.3% and 51%-92%, respectively. The deterioration of pore structure results in a 3%-9% reduction in the compressive strength of concrete. From the results we have obtained, it can be concluded that the increase of critical nucleation energy of air bubbles and the decrease of volumetric compressibility coefficient of air in the concrete are responsible for the variation of air content and pore structure of concrete under LAP.
基金the National Basic Research Program of China(No.2001CB610703)the Basic Research of Preparation and Application of High Performance Cement
文摘The effects of activated coal gangue on compressive strength, porosity and pore size distribution of hardened cement pastes were investigated. Activated coal gangue with two different kaolin contents, one higher and one lower, were used to partially replace Portland cement at 0%, 10%, and 30% by weight. The water to binder ratio(w/b) of 0.5 was used for all the blended cement paste mixes. Experimental results indicate that the blended cement of activated coal gangue mortar with higher kaolin mineral content has a higher compressive strength than that with lower kaolin mineral content. The porosity and pore size of blended cement mortar were significantly affected by the replacement of activated coal gangue.
文摘The split Hopkinson pressure bar (SHPB) testing with diameter 40 mm was used to investigate the dynamic mechanical properties of engineered cementitious composites (ECCs) with different fly ash content. The basic properties including deformation, energy absorption capacity, strain-stress relationship and failure patterns were discussed. The ECCs showed strain-rate dependency and kept better plastic flow during impact process compared with reactive powder concrete (RPC) and concrete, but the critical compressive strength was lower than that of RPC and concrete. The bridging effect of PVA fiber and addition of fly ash can significantly improve the deformation and energy absorption capacities of ECCs. With the increase of fly ash content in ECCs, the static and dynamic compressive strength lowered and the dynamic increase factor enhanced. Therefore, to meet different engineering needs, the content of fly ash can be an important index to control the static and dynamic mechanical properties of ECCs.
基金Funded by the National Natural Science Foundation of China(No. 50872127)the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education Ministry
文摘In order to improve the mechanical properties and Greenness of engineered cementitious composites (ECC),four-point bending test,compressive strength and flexural strength test were employed to analyze the effects of fly ash content on the mechanical properties of.ECC.The replacement ratio of cement with fly ash was 50%,60%,70% and 80%,respectively.The experimental results indicate that ECCs with high volume fly ash still remained the characteristic of pseudo-strain hardening and the mid-span deflection in four-point bending test increase remarkably by adding more fly ash.The observations of ECCs indicate that the multiple cracks are saturated and the crack width is relatively smaller for higher volume fly ash ECC,owing to the lower strength of matrix and the improvement ofinterface bonding.Fly ash reduces the compressive strength and flexural strength of ECC at all ages.Therefore,as the compressive strength could meet the requirement of practical engineering,employing the higher volume fly ash ECCs would benefit to obtain relatively high ductility.
基金Funded by National Key Research and Development Program of China(No.2017YFB0310000)Opening Project of State Key Laboratory of Green Building Materials(No.YA-584)the Key Technology Innovation Program from the Ministry of Science and Technology(Hubei Province)(No.2018AAA004)
文摘The internal curing effect of superabsorbent polymer(SAP) on the properties of high performance concrete(HPC) under marine wetting and drying cycles(WD cycles) was investigated. Compressive strength, hydration and chloride migration were experimentally investigated and the results were evaluated by compasison with those under fresh water curing(FW). Water absorption and porosity were also evaluated only under WD cycles. The results showed the important influence of wetting and drying cycles on the properties of SAP modified HPC properties. Carefully designed, SAP minimized the long-term compressive strength of HPC under marine WD cycles. The hydration rate was faster in the initial curing, but became lower as compared with that cured in FW. In addition, SAP improved the long-term water absorption resistance and chloride migration resistance of HPC under marine WD cycles. The examination of the porosity showed a lower increase of the volume of capillary pores in SAP modified HPC under long term WD cycles compared with that without SAP. Therefore, internal curing by SAP could improve the durability properties of HPC under marine WD cycles.
文摘The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry (MIP),X-ray diffraction (XRD) and differential thermal analysis (DTA).Results show that ground steel-making slag is a kind of high activity mineral additives and it can raise the longer-age strength of OPC mortar.The total porosity and average pore diameter of OPC paste with ground steel-making slag increase with the increase of the amount of ground steel-making slag replacing OPC at various ages,while after 28 days most pores in OPC paste with ground steel-making slag do not influence the strength because the diameter of those pores is in the rang of 20 to 50nm.The hydration mechanism of ground steel-making slag is similar to that of OPC but different from that of fly ash and blast furnace slag.The hydration products of ground steel-making slag contain quite a lot of Ca(OH) 2 in long age.
文摘ITO thin films were grown on PC(polycarbonate), PMMA(polymethyl methacrylate) and glass substrates by r.f. magnetron sputtering. The electrical, structural and chemical characteristics of ITO films were analyzed by the Hall Technique, X-ray diffraction, and X-ray photoelectron spectroscopy. XPS studies suggest that all the ITO films consist of crystalline and amorphous phases. The degree of crystallinity increases from less than 45% to more than 90% when the substrate temperature increases from 80 to 300 ℃. The In and Sn exist in the chemical state of In^3+ and Sn^4+, respectively, independent of substrate type and temperature. The enrichment of Sn on surface and In in body of ITO films are also revealed. And, the oxygen deficient regions exist both in surface layer and film body. For ITO films deposited under 180 ℃ , the carrier concentration are mainly provided by oxygen vacancies, and the dominant electron carrier scattering mechanism is grain boundary scattering between the crystal and the amorphous grain. For ITO films deposited over 180 ℃, the carrier concentration are provided by tin doping, and the dominant scattering mechanism transforms from grain boundary scattering between the crystal grains to ionized impurity scattering with increasing deposition temperature.
基金Project(2006BAF02A00) supported by the National Science and Technology Pillar Program during the 11th Five-Year Plan Period of ChinaProject(08-2-1-18-nsh) supported by the Science and Technology Program of Qingdao City, China
文摘Workability and mechanical properties of steel slag green concrete with different types of steel slag and different dosages of admixtures were investigated. The effectiveness of steel slag powder on suppressing alkali aggregate reaction(AAR) expansion was assessed using the method of ASTM C441 and accelerated test method. Experimental results show that mechanical properties can be improved further due to the synergistic effect and mutual activation when compound mineral admixtures with steel slag powder and blast-furnace slag powder are mixed into concrete. In addition,about 50% decrease in expansion rate of mortar bars with mineral admixtures can be achieved in AAR tests. Mineral admixtures with steel slag powder as partial replacement for Portland cement in concrete is an effective means for controlling expansion due to AAR.
基金Funded by the National Natural Science Foundation of China (No.50872127)the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry
文摘The effects of water/binder ratio (w/b) on the toughness behavior, compressive strength and flexural strength of engineered cementitious composites (ECC) were investigated. The w/b ratios of 0.25, 0.31, 0.33 and 0.37 were selected and the specimens were tested at the ages of 7 d and 28 d. The experimental results showed that there was a corresponding increase in first cracking strength, modulus of rupture, compressive strength and flexural strength with the decrease of w/b. Within the w/b range of 0.25-0.37, higher w/b was found to have improved effects on deflection, strain hardening index and toughness index of ECC. In the permission of meeting the requirement of compressive strength grade, selecting higher w/b in mix design will help to obtain robust ECC.
基金financial support by the National Natural Science Foundation of China (Grant: 51333008)Young Teacher Training Program of Sun Yat-sen University (Grant: 17lgpy86)
文摘Developing high-performance non-precious metal electrocatalysts for oxygen reduction reaction(ORR)is crucial for the commercialization of fuel cells and metal-air batteries.However,doped carbon-based materials only show good ORR activity in alkaline medium,and become less effective in acidic environment.We believe that an appropriate combination of both ionic and electronic transport path,and well dopant distribution of doped carbon-based materials would help to realize high ORR performance un-der both acidic and alkaline cond让ions.Accordingly,a nitrogen and sulfur co-doped carbon framework with hierarchical through-hole structure is fabricated by morphology-controlled solid-state pyrolysis of poly(aniline-co-2-ami no thiophenol)foam.The uniform high concentrations of nitrogen and sulfur,high intrinsic conductivity,and integrated three dimensional ionic and electronic transfer passageways of the 3D porous structure lead to synergistic effects in catalyzing ORR.As a result,the limiting current density of the carbonized poly(aniline-co-2-aminothiophenol)foam is equivalent to commercial Pt/C in acidic environment,and twice the latter in alkaline medium.
文摘Zirconia aqueous slurry was prepared with fine zirconia powder. Injection process for making zirconia fiber was demonstrated, including preparation of aqueous slurry, injection of slurry, fiber setting in acetone, and fiber firing. The principle of the process was discussed. The effects of solid loading in the zirconia slurry, addition of dispersant in the slurry, and ball milling time on the rheological properties of the slurry, especially yield stress, were illustrated. The role of acetone as curing agent was discussed. Zirconia poly-crystalline fiber with its density of 6. 05 g · cm^-3 was obtained after sintering at 1 530 ℃ for 5 h. Microstructure of the sintered zirconia fiber was investigated.