Pre-reduction of WO_(3)-Co_(3)O_(4)by H_(2)-C_(2)H_4 in a fluidized bed

In order to avoid the formation ofηphase(W_(6)Co_(6)C or W_(3)Co_(3)C)that adversely affects the sintering process and its products in the preparation process of ultra-fine WC-Co powder,a technical route of prereduction of WO_(3)-Co_(3)O_(4)to WO_(2)-Co and then deep reduction carbonization to WC-Co powder has been proposed.This study mainly investigates the influence of gas partial pressure on the pre-reduction process of WO_(3)-Co_(3)O_(4)under a mixed atmosphere of H_(2)-C_(2)H_(4)-Ar at 600℃and establishes the kinetic equations of pre-reduction and carbon evolution.The results indicate that increasing the partial pressure of hydrogen is conducive to the rapid and complete conversion of WO_(3) to WO_(2).High carbon content can be generated by the deposition of C_(2)H_(4),and it hinders the diffusion of the reducing gas;WO_(3)still cannot be completely reduced to WO_(2)as the partial pressure of C_(2)H_(4) increases to 60%.For the carbon evolution of C_(2)H_(4),the carbon amount is positively related to the H_(2)partial pressure,but it shows the highest amount and evolution rate when the ethylene partial pressure is 20%.Based on the reduction rate curves of WO_(3) and carbon evolution rate curves of C_(2)H_(4),the rate equations of pre-reduction and carbon evolution of WO_(3)-Co_(3)O_(4)system at 600℃are established.The pre-reduction reaction belongs to the first-order reaction,and its equation is expressed as follows:r=-(dw_(WO_(3)))/dt=(9±0.15)×10^(-2)×P_(H_(2))^(0.44)P_(C_(2)H_(4))&(0.57)The carbon deposition rate equation of C_(2)H_(4) can be expressed as follows:r=-(dc_C)/dt=r_f-r_b≌7.35×10^(-2)×P_(C_(2)H_(4))^(0.31)

Preparation of ultrafine WC-Co powder via fluidized bed

In this study,the effects of reaction parameters on the deep-reduction and carbonization process of WO_(2)-Co to WC-Co were studied.The results indicate that the oxygen loss rate of WO_(2) is positively correlated with temperature and methane partial pressure.The partial pressure of methane has no significant effect on the formation rate of WC.The carbon content and particle size of the product increase with the increase of CH_(4) partial pressure.By synergistically regulating the reaction temperature to 950℃,the CH_(4) partial pressure to 1.25%,and the reaction time to 60 min,ultrafine WC-Co powder without h phase can be obtained.The particle size of the composite powder is 128 nm,with total carbon content of 6.16%,free carbon content of 0.4%,and residual oxygen content of 0.05%,respectively.The growth rate relationship of tungsten carbide is as follows:δ(t)=1.21×10^(-13)exp(-12809.72/T)√t.