Multilayered Pt/Ru modified aluminide coating for thermal barrier coating （TBC） systems has been investi- gated. 2μm Pt＋2 μm Ru＋2 μm Pt was first deposited on nickel-base superalloy DZ125 by electrodeposition, ...Multilayered Pt/Ru modified aluminide coating for thermal barrier coating （TBC） systems has been investi- gated. 2μm Pt＋2 μm Ru＋2 μm Pt was first deposited on nickel-base superalloy DZ125 by electrodeposition, and then the coating was treated by annealing and a conventional pack-cementation aluminizing process. The cyclic oxidation tests were carried out at 1423 K in air. It was found that the thermal cyclic oxidation resistance of Pt/Ru-modified aluminide coating was comparable to that of Pt-modified aluminide coating, which was much better than simply aluminized DZ125. The addition of Ru to Pt-modified aluminide coating increased the resistance to rumpling. The microstructures and phase constitutions of the coating before and after oxidation were investigated.展开更多
In the present investigation,Pt/Ru-modified bond coating consisted of 2 μm Pt＋2 μm Ru was deposited on a nickel-based superalloy by electroplating method and followed by conventional Al pack cementation.The cyclic ...In the present investigation,Pt/Ru-modified bond coating consisted of 2 μm Pt＋2 μm Ru was deposited on a nickel-based superalloy by electroplating method and followed by conventional Al pack cementation.The cyclic corrosion behavior of Pt/Ru-modified bond coating exposed to NaCl plus water vapor has been investigated under atmospheric pressure at 1050℃.The result shows that the cyclic corrosion life of Pt/Ru-modified bond coating is longer than that of the conventional Pt-modified aluminide coating in the presence of NaCl plus water vapor.The addition of Ru makes the coating possess the increased strength and suppress the rumpling behavior.The absence of rumpling may be responsible for the improved corrosion resistance of Pt/Ru-modified aluminide coating.展开更多
基金sponsored by the Program for New Century Excellent Talents in University (NCET)the National Natural Science Foundation of China (NSFC,Nos.50731001 and 50971013)the National Institute for Materials Science (NIMS) internship program
文摘Multilayered Pt/Ru modified aluminide coating for thermal barrier coating （TBC） systems has been investi- gated. 2μm Pt＋2 μm Ru＋2 μm Pt was first deposited on nickel-base superalloy DZ125 by electrodeposition, and then the coating was treated by annealing and a conventional pack-cementation aluminizing process. The cyclic oxidation tests were carried out at 1423 K in air. It was found that the thermal cyclic oxidation resistance of Pt/Ru-modified aluminide coating was comparable to that of Pt-modified aluminide coating, which was much better than simply aluminized DZ125. The addition of Ru to Pt-modified aluminide coating increased the resistance to rumpling. The microstructures and phase constitutions of the coating before and after oxidation were investigated.
基金supported by the Program for Changjiang Scholars and Innovative Research Team in University(PCSIRT)(IRT0512)the Program for New Century Excellent Talents in University(NCET)+1 种基金the National Natural Science Foundation of China(Nos.50671002and50971013)the National Institute for Materials Science (NIMS) internship program
文摘In the present investigation,Pt/Ru-modified bond coating consisted of 2 μm Pt＋2 μm Ru was deposited on a nickel-based superalloy by electroplating method and followed by conventional Al pack cementation.The cyclic corrosion behavior of Pt/Ru-modified bond coating exposed to NaCl plus water vapor has been investigated under atmospheric pressure at 1050℃.The result shows that the cyclic corrosion life of Pt/Ru-modified bond coating is longer than that of the conventional Pt-modified aluminide coating in the presence of NaCl plus water vapor.The addition of Ru makes the coating possess the increased strength and suppress the rumpling behavior.The absence of rumpling may be responsible for the improved corrosion resistance of Pt/Ru-modified aluminide coating.