Advanced uniform LiNi0.7Co0.15Mn0.15O2 microspheres were successfully synthesized and examined as cathode materials for lithium-ion batteries. The structure,morphology, and electrochemical performance of LiNi0.7-Co0.1...Advanced uniform LiNi0.7Co0.15Mn0.15O2 microspheres were successfully synthesized and examined as cathode materials for lithium-ion batteries. The structure,morphology, and electrochemical performance of LiNi0.7-Co0.15Mn0.15O2 calcined at different temperatures ranging from 650 to 900 °C were systematically investigated. The XRD results show that the material has a well-ordered layered structure with small amount of cation mixing. A distinct spherical morphology of the obtained powders prepared at different temperatures can be seen from the SEM images. The as-synthesized LiNi0.7Co0.15Mn0.15O2 powders have a very high-tap density of about 2.37 g·cm^-3. Among all the samples,the sample calcined at 750 °C exhibits the best electrochemical performance with an initial discharge capacity of185.2 mAh·g^-1（3.0–4.3 V, 0.2C rate） and capacity retention〉94.77 %after50cycles.Moreover,thismaterialshowshighspecific capacity and good cycling stability. The LiNi0.7-Co0.15Mn0.15O2 microspheres with high-specific capacity and high-tap density are promising to use as cathode materials for next-generation high-energy-density lithium-ion batteries.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 21001117)the National Science Foundation for Post-Doctoral Scientists of China (No. 2011M501286)
文摘Advanced uniform LiNi0.7Co0.15Mn0.15O2 microspheres were successfully synthesized and examined as cathode materials for lithium-ion batteries. The structure,morphology, and electrochemical performance of LiNi0.7-Co0.15Mn0.15O2 calcined at different temperatures ranging from 650 to 900 °C were systematically investigated. The XRD results show that the material has a well-ordered layered structure with small amount of cation mixing. A distinct spherical morphology of the obtained powders prepared at different temperatures can be seen from the SEM images. The as-synthesized LiNi0.7Co0.15Mn0.15O2 powders have a very high-tap density of about 2.37 g·cm^-3. Among all the samples,the sample calcined at 750 °C exhibits the best electrochemical performance with an initial discharge capacity of185.2 mAh·g^-1（3.0–4.3 V, 0.2C rate） and capacity retention〉94.77 %after50cycles.Moreover,thismaterialshowshighspecific capacity and good cycling stability. The LiNi0.7-Co0.15Mn0.15O2 microspheres with high-specific capacity and high-tap density are promising to use as cathode materials for next-generation high-energy-density lithium-ion batteries.