Nano SiO2 was filled into gypsum particleboard. Effect of the amount of nano SiO2 particles filled, ultrasonic dissipating duration and treating the nano particles with different coupling agents on the mechanical prop...Nano SiO2 was filled into gypsum particleboard. Effect of the amount of nano SiO2 particles filled, ultrasonic dissipating duration and treating the nano particles with different coupling agents on the mechanical properties of the board were studied respectively. The results show that nano SiO2 is helpful for the improvement of the properties. Adding 3%(mass fraction) nano SiO2 is the best for the improvement of both modulus of rupture(MOR) and modulus of elasticity(MOE) of the boards formed at 30 ℃ or 40 ℃. For the boards formed at 30 ℃, their MOR and MOE can be improved by 8.77% and 12.24%, and MOR and MOE of the boards formed at 40 ℃ can be improved by 44.44% and 108.38%.3% is also the best addition proportion to improve internal bond(IB) of the boards formed at 30 ℃, while 5% is the best for that of the boards formed at 40 ℃. At room temperature, dissipating nano SiO2 into flake by ultrasonic has better effect on the properties of the final products. Through ultrasonic treating for 1 h and the best treating duration, the MOR and MOE can be increased by 41.99% and 47.80%. In addition, different coupling agents have different effects on the final properties too, and silane coupling agent KH570 is better for the improvement of properties of the boards formed at room temperature.展开更多
The corrosion resistance of Zr-Al-Ni-Cu(Nb) bulk amorphous alloys was systematically investigated. The experimental results show that the corrosion resistance of Zr-based bulk amorphous alloys can not be considered to...The corrosion resistance of Zr-Al-Ni-Cu(Nb) bulk amorphous alloys was systematically investigated. The experimental results show that the corrosion resistance of Zr-based bulk amorphous alloys can not be considered to be excellent at any situation, whereas it is affected by many factors such as the kind of corrosive medium, solution concentration and the alloy composition. It is found that Zr-Al-Ni-Cu bulk amorphous alloys are seriously corroded in HCl solution in comparison with their excellent corrosion resistance at other acid, alkali and salt circumstances for passivating. Its resistance ability against the chlorine ion induced pitting corrosion can be greatly improved by the addition of Nb element.展开更多
In manufacture of precise optical products, it is important to inspect and classify the potential defects existing on the products’ surfaces after precise machining in order to obtain high quality in both functionali...In manufacture of precise optical products, it is important to inspect and classify the potential defects existing on the products’ surfaces after precise machining in order to obtain high quality in both functionality and aesthetics. The existing methods for detecting and classifying defects all are low accuracy or efficiency or high cost in inspection process. In this paper, a new inspection system based on machine vision has been introduced, which uses automatic focusing and image mosaic technologies to rapidly acquire distinct surface image, and employs Case-Based Reasoning(CBR)method in defects classification. A modificatory fuzzy similarity algorithm in CBR has been adopted for more quick and robust need of pattern recognition in practice inspection. Experiments show that the system can inspect surface diameter of 500mm in half an hour with resolving power of 0.8μm diameter according to digs or 0.5μm transverse width according to scratches. The proposed inspection principles and methods not only have meet manufacturing requirements of precise optical products, but also have great potential applications in other fields of precise surface inspection.展开更多
基金Project (30371130) supported by the National Natural Science Foundation of China
文摘Nano SiO2 was filled into gypsum particleboard. Effect of the amount of nano SiO2 particles filled, ultrasonic dissipating duration and treating the nano particles with different coupling agents on the mechanical properties of the board were studied respectively. The results show that nano SiO2 is helpful for the improvement of the properties. Adding 3%(mass fraction) nano SiO2 is the best for the improvement of both modulus of rupture(MOR) and modulus of elasticity(MOE) of the boards formed at 30 ℃ or 40 ℃. For the boards formed at 30 ℃, their MOR and MOE can be improved by 8.77% and 12.24%, and MOR and MOE of the boards formed at 40 ℃ can be improved by 44.44% and 108.38%.3% is also the best addition proportion to improve internal bond(IB) of the boards formed at 30 ℃, while 5% is the best for that of the boards formed at 40 ℃. At room temperature, dissipating nano SiO2 into flake by ultrasonic has better effect on the properties of the final products. Through ultrasonic treating for 1 h and the best treating duration, the MOR and MOE can be increased by 41.99% and 47.80%. In addition, different coupling agents have different effects on the final properties too, and silane coupling agent KH570 is better for the improvement of properties of the boards formed at room temperature.
文摘The corrosion resistance of Zr-Al-Ni-Cu(Nb) bulk amorphous alloys was systematically investigated. The experimental results show that the corrosion resistance of Zr-based bulk amorphous alloys can not be considered to be excellent at any situation, whereas it is affected by many factors such as the kind of corrosive medium, solution concentration and the alloy composition. It is found that Zr-Al-Ni-Cu bulk amorphous alloys are seriously corroded in HCl solution in comparison with their excellent corrosion resistance at other acid, alkali and salt circumstances for passivating. Its resistance ability against the chlorine ion induced pitting corrosion can be greatly improved by the addition of Nb element.
文摘In manufacture of precise optical products, it is important to inspect and classify the potential defects existing on the products’ surfaces after precise machining in order to obtain high quality in both functionality and aesthetics. The existing methods for detecting and classifying defects all are low accuracy or efficiency or high cost in inspection process. In this paper, a new inspection system based on machine vision has been introduced, which uses automatic focusing and image mosaic technologies to rapidly acquire distinct surface image, and employs Case-Based Reasoning(CBR)method in defects classification. A modificatory fuzzy similarity algorithm in CBR has been adopted for more quick and robust need of pattern recognition in practice inspection. Experiments show that the system can inspect surface diameter of 500mm in half an hour with resolving power of 0.8μm diameter according to digs or 0.5μm transverse width according to scratches. The proposed inspection principles and methods not only have meet manufacturing requirements of precise optical products, but also have great potential applications in other fields of precise surface inspection.