Photoinduced synthesis of CO2 and CH4 was investigated using a batch reaction system on several photoactive materials supported on silicon dioxide. Single semiconductor showed higher selectivity to C1 compounds. The p...Photoinduced synthesis of CO2 and CH4 was investigated using a batch reaction system on several photoactive materials supported on silicon dioxide. Single semiconductor showed higher selectivity to C1 compounds. The production of C2-C3 oxygenates took place preferentially on composite semiconductor photocatalysts. In particular, it was found that acetone was the primary product over Cu / CdS –TiO2 / SiO2.展开更多
Microporous polyvinylidene fluoride(PVDF)hollow fibre membranes were spun using the dry-wet phaseinversion method.By means of dip-coating technique,a uniform coating with thickness of around 5-12 μm of polyvinyldimet...Microporous polyvinylidene fluoride(PVDF)hollow fibre membranes were spun using the dry-wet phaseinversion method.By means of dip-coating technique,a uniform coating with thickness of around 5-12 μm of polyvinyldimethylsiloxane(PVDMS)was formed on the surface of porous PVDF hollow fibers.The structural parameters of PVDFsubstrate membrane were estimated by gas permeation test.Using N_2/O_2 as the medium,the separation properties ofPVDMS-PVDF composite hollow fiber membranes were also evaluated experimentally.The experimental data of bothpermeability and selectivity are in good agreement with the theoretical results predicted by the presented pore-distributionmodel.In order to obtain the compact composite membrane free of defects by the dip-coating technique,the thickness ofPVDMS skin must be higher than 5 μm.展开更多
文摘Photoinduced synthesis of CO2 and CH4 was investigated using a batch reaction system on several photoactive materials supported on silicon dioxide. Single semiconductor showed higher selectivity to C1 compounds. The production of C2-C3 oxygenates took place preferentially on composite semiconductor photocatalysts. In particular, it was found that acetone was the primary product over Cu / CdS –TiO2 / SiO2.
基金This work was supported by the National Natural Science Foundation of China(No.20076025).
文摘Microporous polyvinylidene fluoride(PVDF)hollow fibre membranes were spun using the dry-wet phaseinversion method.By means of dip-coating technique,a uniform coating with thickness of around 5-12 μm of polyvinyldimethylsiloxane(PVDMS)was formed on the surface of porous PVDF hollow fibers.The structural parameters of PVDFsubstrate membrane were estimated by gas permeation test.Using N_2/O_2 as the medium,the separation properties ofPVDMS-PVDF composite hollow fiber membranes were also evaluated experimentally.The experimental data of bothpermeability and selectivity are in good agreement with the theoretical results predicted by the presented pore-distributionmodel.In order to obtain the compact composite membrane free of defects by the dip-coating technique,the thickness ofPVDMS skin must be higher than 5 μm.