To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated usi...To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated using X-ray photoelectron spectroscopy(XPS).The hydroxylation process did not affect the crystal size,specific surface area,pore volume,average pore diameter,and thermal stability of the g-C_(3)N_(4)nanoplates.After incorporating pristine and hydroxylated g-C_(3)N_(4)nanoplates,dense sol-gel coatings were obtained.Transmission electron microscopy(TEM)revealed the uniform distribution of the modified g-C_(3)N_(4)in the coating.The average roughness of the coating was also reduced after adding the modified nanoplates due to the decreased aggregation tendency.Electrochemical impedance spectroscopy(EIS)examinations in simulated acid rain revealed a significant improvement in the anticorrosion properties of the sol-gel film after the addition of the modified g-C_(3)N_(4)due to the chemical bonding of the coating to the nanoplates.展开更多
文摘To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated using X-ray photoelectron spectroscopy(XPS).The hydroxylation process did not affect the crystal size,specific surface area,pore volume,average pore diameter,and thermal stability of the g-C_(3)N_(4)nanoplates.After incorporating pristine and hydroxylated g-C_(3)N_(4)nanoplates,dense sol-gel coatings were obtained.Transmission electron microscopy(TEM)revealed the uniform distribution of the modified g-C_(3)N_(4)in the coating.The average roughness of the coating was also reduced after adding the modified nanoplates due to the decreased aggregation tendency.Electrochemical impedance spectroscopy(EIS)examinations in simulated acid rain revealed a significant improvement in the anticorrosion properties of the sol-gel film after the addition of the modified g-C_(3)N_(4)due to the chemical bonding of the coating to the nanoplates.