Purpose: This study was aimed to evaluate the effect of restorative materials and glass fiber post on the fracture resistance of endodontically treated premolars. Material and Methods: Fifty extracted single rooted lo...Purpose: This study was aimed to evaluate the effect of restorative materials and glass fiber post on the fracture resistance of endodontically treated premolars. Material and Methods: Fifty extracted single rooted lower premolars were used in this in vitro study and divided into 5 groups: sound teeth (control group);mesial-occlusal-distal (MOD) preparation + endodontic treatment + composite restoration;MOD preparation + endodontic treatment + glass fiber post + composite restoration;MOD preparation + endodontic treatment + amalgam restoration;MOD preparation + endodontic treatment + glass fiber post + amalgam restoration. The specimens were loaded on a universal testing machine at the crosshead speed of1 mm/min until fracture. The data were analyzed using two-way ANOVA test. Results: The mean loads at fracture were 860.11 N, 801.79 N, 761.39 N, 737.14 N and 707.85 N respectively. There were no statistically significant differences (P > 0.05) in the fracture resistance of teeth restored with composite and amalgam, as well as restored with or without glass fiber post. Conclusions: The type of restorative material and the usage of glass fiber post do not have visible influence on the fracture resistance of the endodontically treated mandibular premolars.展开更多
文摘Purpose: This study was aimed to evaluate the effect of restorative materials and glass fiber post on the fracture resistance of endodontically treated premolars. Material and Methods: Fifty extracted single rooted lower premolars were used in this in vitro study and divided into 5 groups: sound teeth (control group);mesial-occlusal-distal (MOD) preparation + endodontic treatment + composite restoration;MOD preparation + endodontic treatment + glass fiber post + composite restoration;MOD preparation + endodontic treatment + amalgam restoration;MOD preparation + endodontic treatment + glass fiber post + amalgam restoration. The specimens were loaded on a universal testing machine at the crosshead speed of1 mm/min until fracture. The data were analyzed using two-way ANOVA test. Results: The mean loads at fracture were 860.11 N, 801.79 N, 761.39 N, 737.14 N and 707.85 N respectively. There were no statistically significant differences (P > 0.05) in the fracture resistance of teeth restored with composite and amalgam, as well as restored with or without glass fiber post. Conclusions: The type of restorative material and the usage of glass fiber post do not have visible influence on the fracture resistance of the endodontically treated mandibular premolars.