Ag–CdO composites are still one of the most commonly used electrical contact materials in low-voltage applications owing to their excellent electrical and mechanical properties.Nevertheless,considering the restrictio...Ag–CdO composites are still one of the most commonly used electrical contact materials in low-voltage applications owing to their excellent electrical and mechanical properties.Nevertheless,considering the restriction on using Cd due to its toxicity,it is necessary to find alternative materials that can replace these composites.In this study,the synthesis of Ag-ZnO alloys from Ag-Zn solid solutions was investigated by hot mechanochemical processing.The hot mechanochemical processing was conducted in a modified attritor mill at 138℃under flowing O2 at 1200 cm3/min for 3.0 h.The microstructure and phase evolution were investigated using X-ray diffractometry,field emission gun scanning electron microscopy and transmission electron microscopy.The results suggest that it is possible to complete the oxidation of Ag-Zn solid solution by hot mechanochemical processing at a low temperature and short time.This novel synthesis route can produce Ag-ZnO composites with a homogeneous distribution of nanoscale ZnO precipitates,which is impossible to achieve using the conventional material processing methods.Considering the fact that the fundamental approach to improving electric contact material performance resides in obtaining uniform dispersion of the second-phase in the Ag matrix,this new processing route could open the possibility for Ag-ZnO composites to replace non-environmentally friendly Ag-CdO.展开更多
The effect of the amount of Sn on the formation of fcc phase in Ti-13 Ta-x Sn(x=3,6,9 and 12,at.%)alloys was studied.The alloys were synthesized by mechanical alloying using a planetary mill,jar and balls of stabilize...The effect of the amount of Sn on the formation of fcc phase in Ti-13 Ta-x Sn(x=3,6,9 and 12,at.%)alloys was studied.The alloys were synthesized by mechanical alloying using a planetary mill,jar and balls of stabilized yttrium.Using Rietveld refinement,it was found that the obtained fcc phase has crystallite size smaller than 10 nm and microstrain larger than 10-3.Both conditions are required to form an fcc phase in Ti-based alloys.For all samples,the microstructure of the fcc phase consists of equiaxial crystallites with sizes smaller than 10 nm.The largest presence of fcc phase in the studied Ti alloy was found with 6 at.%Sn,because this alloy exhibits the largest microstrain(1.5×10-2)and crystallite size of 6.5 nm.Experimental data reveal that a solid solution and an amorphous phase were formed during milling.The necessary conditions to promote the formation of solid solution and amorphous phases were determined using thermodynamic calculations.When the amount of Sn increases,the energy required to form an amorphous phase varies from approximately 10 to approximately-5 k J/mol for 3 and 12 at.%Sn,respectively.The thermodynamic calculations are in agreement with XRD patterns analysis and HRTEM results.展开更多
基金financially supported by the FONDECYT(Project No.11100284)the Metallurgy Department of University of Atacama for the XRD and SEM analysis(Projects EQM130125 and EQUV 003)
文摘Ag–CdO composites are still one of the most commonly used electrical contact materials in low-voltage applications owing to their excellent electrical and mechanical properties.Nevertheless,considering the restriction on using Cd due to its toxicity,it is necessary to find alternative materials that can replace these composites.In this study,the synthesis of Ag-ZnO alloys from Ag-Zn solid solutions was investigated by hot mechanochemical processing.The hot mechanochemical processing was conducted in a modified attritor mill at 138℃under flowing O2 at 1200 cm3/min for 3.0 h.The microstructure and phase evolution were investigated using X-ray diffractometry,field emission gun scanning electron microscopy and transmission electron microscopy.The results suggest that it is possible to complete the oxidation of Ag-Zn solid solution by hot mechanochemical processing at a low temperature and short time.This novel synthesis route can produce Ag-ZnO composites with a homogeneous distribution of nanoscale ZnO precipitates,which is impossible to achieve using the conventional material processing methods.Considering the fact that the fundamental approach to improving electric contact material performance resides in obtaining uniform dispersion of the second-phase in the Ag matrix,this new processing route could open the possibility for Ag-ZnO composites to replace non-environmentally friendly Ag-CdO.
基金financial support from FONDECYT Project No.1190797FONDEQUIP/EQM Project No.140095。
文摘The effect of the amount of Sn on the formation of fcc phase in Ti-13 Ta-x Sn(x=3,6,9 and 12,at.%)alloys was studied.The alloys were synthesized by mechanical alloying using a planetary mill,jar and balls of stabilized yttrium.Using Rietveld refinement,it was found that the obtained fcc phase has crystallite size smaller than 10 nm and microstrain larger than 10-3.Both conditions are required to form an fcc phase in Ti-based alloys.For all samples,the microstructure of the fcc phase consists of equiaxial crystallites with sizes smaller than 10 nm.The largest presence of fcc phase in the studied Ti alloy was found with 6 at.%Sn,because this alloy exhibits the largest microstrain(1.5×10-2)and crystallite size of 6.5 nm.Experimental data reveal that a solid solution and an amorphous phase were formed during milling.The necessary conditions to promote the formation of solid solution and amorphous phases were determined using thermodynamic calculations.When the amount of Sn increases,the energy required to form an amorphous phase varies from approximately 10 to approximately-5 k J/mol for 3 and 12 at.%Sn,respectively.The thermodynamic calculations are in agreement with XRD patterns analysis and HRTEM results.