Y/Bi co-doped silicate glasses were prepared,and the effects of Y 2 O 3 on the absorption and emission properties were investigated by spectrum measurement.It was found that the absorption intensity in visible region ...Y/Bi co-doped silicate glasses were prepared,and the effects of Y 2 O 3 on the absorption and emission properties were investigated by spectrum measurement.It was found that the absorption intensity in visible region decreases with increase of Y 3＋ concentration in（70-x）SiO 2 xY 2 O 3-30CaO-1.5Bi 2 O 3（x=0 mol.%,1 mol.%,3 mol.%,5 mol.%,7 mol.%） glasses.The emissions centered at 410,630,1200 and 1290 nm were observed under 280,470,514 and 808 nm excitation,respectively.The emission intensity had the similar change tendency in the visible and near infrared region.We also discussed the actual role of Y 3＋ ions playing in the visible and near infrared emissions of the silicate glasses.展开更多
基金supported by Science and Technology Project of Guangdong (2009A090100044)National High-Technology Research and Development Program of China ("863"Program) (2011AA030201)
文摘Y/Bi co-doped silicate glasses were prepared,and the effects of Y 2 O 3 on the absorption and emission properties were investigated by spectrum measurement.It was found that the absorption intensity in visible region decreases with increase of Y 3＋ concentration in（70-x）SiO 2 xY 2 O 3-30CaO-1.5Bi 2 O 3（x=0 mol.%,1 mol.%,3 mol.%,5 mol.%,7 mol.%） glasses.The emissions centered at 410,630,1200 and 1290 nm were observed under 280,470,514 and 808 nm excitation,respectively.The emission intensity had the similar change tendency in the visible and near infrared region.We also discussed the actual role of Y 3＋ ions playing in the visible and near infrared emissions of the silicate glasses.