Geopolymer composites containing woven cotton fabric(0-8.3 wt%)were fabricated using the hand lay-up technique,and were exposed to elevated temperatures of 200℃,400℃,600℃,800℃and 1000℃.With an increase in tempera...Geopolymer composites containing woven cotton fabric(0-8.3 wt%)were fabricated using the hand lay-up technique,and were exposed to elevated temperatures of 200℃,400℃,600℃,800℃and 1000℃.With an increase in temperature,the geopolymer composites exhibited a reduction in compressive strength,flexural strength and fracture toughness.When heated above 600℃,the composites exhibited a significant reduction in mechanical properties.They also exhibited brittle behavior due to severe degradation of cotton fibres and the creation of additional porosity in the composites.Microstructural images verified the existence of voids and small channels in the composites due to fibre degradation.展开更多
This paper presents the mechanical and thermal properties of flax fabric reinforced fly ash based geopolymer composites.Geopolymer composites reinforced with 2.4,3.0 and 4.1 wt%woven flax fabric in various layers were...This paper presents the mechanical and thermal properties of flax fabric reinforced fly ash based geopolymer composites.Geopolymer composites reinforced with 2.4,3.0 and 4.1 wt%woven flax fabric in various layers were fabricated using a hand lay-up technique and tested for mechanical properties such as flexural strength,flexural modulus,compressive strength,hardness,and fracture toughness.All mechanical properties were improved by increasing the flax fibre contents,and showed superior mechanical properties over a pure geopolymer matrix.Fourier transform infrared spectroscopy(FTIR)and scanning electron microscopy(SEM)studies were carried out to evaluate the composition and fracture surfaces of geopolymer and geopolymer/flax composites.The thermal behaviour of composites was studied by thermogravimetric analysis(TGA)and the results showed significant degradation of flax fibres at 300℃.展开更多
文摘Geopolymer composites containing woven cotton fabric(0-8.3 wt%)were fabricated using the hand lay-up technique,and were exposed to elevated temperatures of 200℃,400℃,600℃,800℃and 1000℃.With an increase in temperature,the geopolymer composites exhibited a reduction in compressive strength,flexural strength and fracture toughness.When heated above 600℃,the composites exhibited a significant reduction in mechanical properties.They also exhibited brittle behavior due to severe degradation of cotton fibres and the creation of additional porosity in the composites.Microstructural images verified the existence of voids and small channels in the composites due to fibre degradation.
文摘This paper presents the mechanical and thermal properties of flax fabric reinforced fly ash based geopolymer composites.Geopolymer composites reinforced with 2.4,3.0 and 4.1 wt%woven flax fabric in various layers were fabricated using a hand lay-up technique and tested for mechanical properties such as flexural strength,flexural modulus,compressive strength,hardness,and fracture toughness.All mechanical properties were improved by increasing the flax fibre contents,and showed superior mechanical properties over a pure geopolymer matrix.Fourier transform infrared spectroscopy(FTIR)and scanning electron microscopy(SEM)studies were carried out to evaluate the composition and fracture surfaces of geopolymer and geopolymer/flax composites.The thermal behaviour of composites was studied by thermogravimetric analysis(TGA)and the results showed significant degradation of flax fibres at 300℃.