Zinc(Zn)and its biocompatible and biodegradable alloys have substantial potential for use in orthopedic implants.Nevertheless,pure Zn with a hexagonal close-packed crystal structure has only two independent slip syste...Zinc(Zn)and its biocompatible and biodegradable alloys have substantial potential for use in orthopedic implants.Nevertheless,pure Zn with a hexagonal close-packed crystal structure has only two independent slip systems,therefore exhibiting extremely low elongation and yield strength in its ascast condition,which restricts its clinical applications.In this study,as-cast Zn–xTi(titanium)(x=0.05,0.10,0.20,and 0.30 wt.%)binary alloys were hot-rolled and their microstructures,mechanical properties,wear resistance,and cytocompatibility were comprehensively investigated for orthopedic implant applications.The microstructures of both as-cast and hot-rolled Zn–xTi alloys consisted of anα-Zn matrix phase and a TiZn16 phase,while Zn–0.2 Ti and Zn–0.3 Ti exhibited a finerα-Zn phase due to the grainrefining effect of Ti.The hot-rolled Zn–0.2 Ti alloy exhibited the highest yield strength(144.5 MPa),ultimate strength(218.7 MPa),and elongation(54.2%)among all the Zn–x Ti alloys.The corrosion resistance of Zn–xTi alloys in Hanks’solution decreased with increasing addition of Ti,and the hot-rolled Zn–0.3 Ti alloy exhibited the highest corrosion rates of 432μm/y as measured by electrochemical testing and 57.9μm/y as measured by immersion testing.The as-cast Zn–xTi alloys showed lower wear losses than their hot-rolled counterparts.The extracts of hot-rolled Zn–x Ti alloys at concentrations of≤25%showed no cytotoxicity to MG-63 osteosarcoma cells and the extracts of Zn–xTi alloys exhibited enhanced cytocompatibility with increasing Ti content.展开更多
基金the Wenzhou Science and Technology Bureau through the project ZG2019022 and 2018ZG008financial support for this research by the Australian Research Council(ARC)through the Discovery Project DP170102557+1 种基金Future Fellowship FT160100252the support of the ARC Research Hub for Advanced Manufacturing of Medical Devices(IH150100024)。
文摘Zinc(Zn)and its biocompatible and biodegradable alloys have substantial potential for use in orthopedic implants.Nevertheless,pure Zn with a hexagonal close-packed crystal structure has only two independent slip systems,therefore exhibiting extremely low elongation and yield strength in its ascast condition,which restricts its clinical applications.In this study,as-cast Zn–xTi(titanium)(x=0.05,0.10,0.20,and 0.30 wt.%)binary alloys were hot-rolled and their microstructures,mechanical properties,wear resistance,and cytocompatibility were comprehensively investigated for orthopedic implant applications.The microstructures of both as-cast and hot-rolled Zn–xTi alloys consisted of anα-Zn matrix phase and a TiZn16 phase,while Zn–0.2 Ti and Zn–0.3 Ti exhibited a finerα-Zn phase due to the grainrefining effect of Ti.The hot-rolled Zn–0.2 Ti alloy exhibited the highest yield strength(144.5 MPa),ultimate strength(218.7 MPa),and elongation(54.2%)among all the Zn–x Ti alloys.The corrosion resistance of Zn–xTi alloys in Hanks’solution decreased with increasing addition of Ti,and the hot-rolled Zn–0.3 Ti alloy exhibited the highest corrosion rates of 432μm/y as measured by electrochemical testing and 57.9μm/y as measured by immersion testing.The as-cast Zn–xTi alloys showed lower wear losses than their hot-rolled counterparts.The extracts of hot-rolled Zn–x Ti alloys at concentrations of≤25%showed no cytotoxicity to MG-63 osteosarcoma cells and the extracts of Zn–xTi alloys exhibited enhanced cytocompatibility with increasing Ti content.
