Low carbon microalloyed steel containing 0.062 percent C, 2.34 percent Mn,0.044 percent Nb, 0.029 percent Ti, 0.032 percent V in mass fraction and small amount of B wasprepared in laboratory. Slabs of the steel were r...Low carbon microalloyed steel containing 0.062 percent C, 2.34 percent Mn,0.044 percent Nb, 0.029 percent Ti, 0.032 percent V in mass fraction and small amount of B wasprepared in laboratory. Slabs of the steel were rolled into plates of 6mm in thickness followed byaccelerated cooling. The plates possess very high yield strength and reasonable ductility, and theyield ratio is about 0.8. Ultra-fine ferrite structure with micrometer dimension was observed in thesurface layer of the plates. Moreover, the effect of the finishing rolling temperature on the finalmicrostructure and formation mechanism of ultra-fine ferrite as well as the gamma->alphatransformation behavior of the steel was discussed.展开更多
基金This work was financially supported by the State Foundation of China for Fundamental Research(No.G1998061500).
文摘Low carbon microalloyed steel containing 0.062 percent C, 2.34 percent Mn,0.044 percent Nb, 0.029 percent Ti, 0.032 percent V in mass fraction and small amount of B wasprepared in laboratory. Slabs of the steel were rolled into plates of 6mm in thickness followed byaccelerated cooling. The plates possess very high yield strength and reasonable ductility, and theyield ratio is about 0.8. Ultra-fine ferrite structure with micrometer dimension was observed in thesurface layer of the plates. Moreover, the effect of the finishing rolling temperature on the finalmicrostructure and formation mechanism of ultra-fine ferrite as well as the gamma->alphatransformation behavior of the steel was discussed.