For 308L and 347L weld metals of austenitc stainless steels (ASS), hydrogen induced cracking (HIC) occurred during dynamically charging under constant load. The threshold stress intensity for HIC, Km, decreased linear...For 308L and 347L weld metals of austenitc stainless steels (ASS), hydrogen induced cracking (HIC) occurred during dynamically charging under constant load. The threshold stress intensity for HIC, Km, decreased linearly with the logarithm of the concentration of diffusible hydrogen C0 in the weld metals and the rolled plate of type 304L ASS, i.e., KIH=85.2-10.71nC0 (308L), KIH=76.1-9.31n C0(347L), and KIH=91.7-10.11nC0(304L). The fracture mode for HIC in the three type of ASS changed from ductile to brittle with the decrease in the applied stress intensity KI or/and the increase in C0. The boundary line between ductile and brittle fracture surfaces was KI-54+25exp(-C0/153)=0.展开更多
Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires...Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires are studied. The results show that with theincrease of Fe_2O_3 in the mix, the melting point of the pretreated mix is increased. LiBaF_3 andBaFe_(12)O_(19), which are very low in inherent moisture, are formed after the pretreatment. Themechanical properties are evaluated to the weld metals. The low temperature notch toughness of theweld metals is increased linearly with the Fe_2O_3 content in the flux due to the balance betweenFe_2O_3 and residual Al in the weld metal. The optimum Fe_2O_3 content in flux is 2.5 percent approx3.5 percent.展开更多
基金This project was supported by the Special Fund for the MajorState Basic Research projects(No. G19990650).
文摘For 308L and 347L weld metals of austenitc stainless steels (ASS), hydrogen induced cracking (HIC) occurred during dynamically charging under constant load. The threshold stress intensity for HIC, Km, decreased linearly with the logarithm of the concentration of diffusible hydrogen C0 in the weld metals and the rolled plate of type 304L ASS, i.e., KIH=85.2-10.71nC0 (308L), KIH=76.1-9.31n C0(347L), and KIH=91.7-10.11nC0(304L). The fracture mode for HIC in the three type of ASS changed from ductile to brittle with the decrease in the applied stress intensity KI or/and the increase in C0. The boundary line between ductile and brittle fracture surfaces was KI-54+25exp(-C0/153)=0.
文摘Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires are studied. The results show that with theincrease of Fe_2O_3 in the mix, the melting point of the pretreated mix is increased. LiBaF_3 andBaFe_(12)O_(19), which are very low in inherent moisture, are formed after the pretreatment. Themechanical properties are evaluated to the weld metals. The low temperature notch toughness of theweld metals is increased linearly with the Fe_2O_3 content in the flux due to the balance betweenFe_2O_3 and residual Al in the weld metal. The optimum Fe_2O_3 content in flux is 2.5 percent approx3.5 percent.