In this study, Inconel 738 alloy was diffusion bonded to a ferritic stainless steel. The effect of bonding temperature on the microstructural development across the joint region was investigated. Following the diffusi...In this study, Inconel 738 alloy was diffusion bonded to a ferritic stainless steel. The effect of bonding temperature on the microstructural development across the joint region was investigated. Following the diffusion bonding, conventional characterization techniques such as scanning electron microscopy （SEM）, energy dispersive X-ray （EDX） and microhardness were used to examine the interracial microstructure. It was seen that bonding temperature was effective on the diffusion of Ni from Inconel 738 to ferritic stainless steel that affected the microstructure of the interface. Austenite phase was formed at the interface as a result of Ni diffusion from the Inconel 738 to the interface.展开更多
In order to understand the influence of nano-sized B4C additive on ZA27 alloy, mechanical and physical properties of ZA27-B4C nanocomposites were investigated in terms of B4C content. While physical properties were de...In order to understand the influence of nano-sized B4C additive on ZA27 alloy, mechanical and physical properties of ZA27-B4C nanocomposites were investigated in terms of B4C content. While physical properties were determined in terms of microstructural studies, density and porosity tests, mechanical properties were determined in terms of ultimate tensile strength（UTS） and hardness experiments. Morphological and microstructural studies were carried out with scanning electron microscopy（SEM）. The experimental results indicate that nano-sized B4C can be used to enhance the mechanical properties of ZA27 alloy effectively. The highest mechanical performance can be obtained at ZA27-0.5% B4C（in weight） nanocomposite with values of tensile strength（247 MPa） and hardness（141,18 BH） and low partial porosity（0.5%）. After a pick point, increasing B4C ratio may cause the formation of agglomeration in grain boundaries, that＇s why density, tensile strength, and hardness values are declined.展开更多
Friction stir lap welds were produced in 3 mm thick Alclad sheets of Al alloy 2014-T4 using two different tools （with triangular and threaded taper cylindrical pins）. The effects of tool geometry on weld microstruct...Friction stir lap welds were produced in 3 mm thick Alclad sheets of Al alloy 2014-T4 using two different tools （with triangular and threaded taper cylindrical pins）. The effects of tool geometry on weld microstructure, lap-shear performance and failure mode were investigated. The pin profile was found to significantly influence the hook geometry, which in turn strongly influenced the joint strength and the failure mode. Welds produced in alloy 2014-T4 Alclad sheets by using triangular and threaded taper cylindrical tools exhibited an average lap-shear failure load of 16.5 and 19.5 kN, respectively, while the average failure load for standard riveted joints was only 3.4 kN. Welds produced in alloy 2014-T6 Alclad sheets and in alloy 2014-T4 bare sheets （i.e., no Alclad） were comparatively evaluated with those produced in alloy 2014-T4 Alclad sheets. While the welds made （with threaded taper cylindrical tool） in T6 and T4 conditions showed very similar lap-shear failure loads, the joint efficiency of the welds made in T6 condition （43%） was considerably lower （because of the higher base material strength） than those made in T4 condition （51%）. The Alclad layers were found to present no special problems in friction stir lap welding. Welds made with triangular tool in alloy 2014-T4 Alclad and bare sheets showed very similar lap-shear failure loads. The present work provides some useful insights into the use of friction stir welding for joining Al alloys in lap configuration.展开更多
The present work deals with thermodynamic modeling of oxide systems, in the context of slags and inclusions in steelmaking. The work has emphasis on oxides encountered during the production of tire – cord steel. Cont...The present work deals with thermodynamic modeling of oxide systems, in the context of slags and inclusions in steelmaking. The work has emphasis on oxides encountered during the production of tire – cord steel. Control of inclusion chemistry and variation in eutectic temperature and eutectic composition of MnO-Al2O3-SiO2 slag system have been studied, using Thermo-CalcR software. Relatively low liquidus temperatures are obtained for ratio of MnO / SiO2 = 0.5 - 1.5 and Al2O3 content from 10 - 20 mass%. It has been observed that the addition of Alumina leads to further increase in the liquidus temperature. The stability of inclusions is analyzed in terms of free energy values of related slag systems; and an appropriate minimum of Gibbs free energy value of slag phase observed at around 50 ppm of Oxygen. The observations could not be verified using thermodynamic experiments, but have been compared with findings in the open literature.展开更多
文摘In this study, Inconel 738 alloy was diffusion bonded to a ferritic stainless steel. The effect of bonding temperature on the microstructural development across the joint region was investigated. Following the diffusion bonding, conventional characterization techniques such as scanning electron microscopy （SEM）, energy dispersive X-ray （EDX） and microhardness were used to examine the interracial microstructure. It was seen that bonding temperature was effective on the diffusion of Ni from Inconel 738 to ferritic stainless steel that affected the microstructure of the interface. Austenite phase was formed at the interface as a result of Ni diffusion from the Inconel 738 to the interface.
基金Funded by the Research Projects Unit of Karadeniz Technical(Number:12040)TUBITAK(Number:213M276)
文摘In order to understand the influence of nano-sized B4C additive on ZA27 alloy, mechanical and physical properties of ZA27-B4C nanocomposites were investigated in terms of B4C content. While physical properties were determined in terms of microstructural studies, density and porosity tests, mechanical properties were determined in terms of ultimate tensile strength（UTS） and hardness experiments. Morphological and microstructural studies were carried out with scanning electron microscopy（SEM）. The experimental results indicate that nano-sized B4C can be used to enhance the mechanical properties of ZA27 alloy effectively. The highest mechanical performance can be obtained at ZA27-0.5% B4C（in weight） nanocomposite with values of tensile strength（247 MPa） and hardness（141,18 BH） and low partial porosity（0.5%）. After a pick point, increasing B4C ratio may cause the formation of agglomeration in grain boundaries, that＇s why density, tensile strength, and hardness values are declined.
基金the Indian Space Research Organization (ISRO) for providing financial support forcarrying out this work
文摘Friction stir lap welds were produced in 3 mm thick Alclad sheets of Al alloy 2014-T4 using two different tools （with triangular and threaded taper cylindrical pins）. The effects of tool geometry on weld microstructure, lap-shear performance and failure mode were investigated. The pin profile was found to significantly influence the hook geometry, which in turn strongly influenced the joint strength and the failure mode. Welds produced in alloy 2014-T4 Alclad sheets by using triangular and threaded taper cylindrical tools exhibited an average lap-shear failure load of 16.5 and 19.5 kN, respectively, while the average failure load for standard riveted joints was only 3.4 kN. Welds produced in alloy 2014-T6 Alclad sheets and in alloy 2014-T4 bare sheets （i.e., no Alclad） were comparatively evaluated with those produced in alloy 2014-T4 Alclad sheets. While the welds made （with threaded taper cylindrical tool） in T6 and T4 conditions showed very similar lap-shear failure loads, the joint efficiency of the welds made in T6 condition （43%） was considerably lower （because of the higher base material strength） than those made in T4 condition （51%）. The Alclad layers were found to present no special problems in friction stir lap welding. Welds made with triangular tool in alloy 2014-T4 Alclad and bare sheets showed very similar lap-shear failure loads. The present work provides some useful insights into the use of friction stir welding for joining Al alloys in lap configuration.
文摘The present work deals with thermodynamic modeling of oxide systems, in the context of slags and inclusions in steelmaking. The work has emphasis on oxides encountered during the production of tire – cord steel. Control of inclusion chemistry and variation in eutectic temperature and eutectic composition of MnO-Al2O3-SiO2 slag system have been studied, using Thermo-CalcR software. Relatively low liquidus temperatures are obtained for ratio of MnO / SiO2 = 0.5 - 1.5 and Al2O3 content from 10 - 20 mass%. It has been observed that the addition of Alumina leads to further increase in the liquidus temperature. The stability of inclusions is analyzed in terms of free energy values of related slag systems; and an appropriate minimum of Gibbs free energy value of slag phase observed at around 50 ppm of Oxygen. The observations could not be verified using thermodynamic experiments, but have been compared with findings in the open literature.