Compared with the undeformed TiNi film, the martensite-austenite transformation (M-A) of the deformed one is elevated to a higher temperature on the first heating, but it nearly returns back to the original temperatur...Compared with the undeformed TiNi film, the martensite-austenite transformation (M-A) of the deformed one is elevated to a higher temperature on the first heating, but it nearly returns back to the original temperature on the second heating. An incomplete M-A transformation of the deformed TiNi film on the first heating divides the total martensite population into the self-accommodating martensite M2 and the oriented martensite M1. Thus, two transformations corresponding to M1-A and M2-A transition occur on the second heating. However, the forward transformation is not affected by the incomplete thermal cycle.展开更多
基金The authors are grateful to the National Natural Science Foundation of China for support under grant No. 59681004 and 59731030.
文摘Compared with the undeformed TiNi film, the martensite-austenite transformation (M-A) of the deformed one is elevated to a higher temperature on the first heating, but it nearly returns back to the original temperature on the second heating. An incomplete M-A transformation of the deformed TiNi film on the first heating divides the total martensite population into the self-accommodating martensite M2 and the oriented martensite M1. Thus, two transformations corresponding to M1-A and M2-A transition occur on the second heating. However, the forward transformation is not affected by the incomplete thermal cycle.