In the present study, an aero pneumatic fatigue testing machine for complete dentures was designed, fabricated, and tested for the evaluation of the fatigue life of reinforced complete upper denture (CUD). On completi...In the present study, an aero pneumatic fatigue testing machine for complete dentures was designed, fabricated, and tested for the evaluation of the fatigue life of reinforced complete upper denture (CUD). On completion and testing, it was observed that the machine has the potential of generating reliable number of cyclic data. The machine’s performance was evaluated using test specimens of identical CUDs that were machined in conformity with standard procedures. The fatigue machine compressed the lower dental arch over the upper denture-specimen in centric occlusion, in the same way that the two masticatory muscles pull the lower jaw over the upper jaw during chewing. The incorporation of glass fibres into the CUD using a sandwich technique quadruples the lifespan of the denture (<em>P</em> = 0.004). The low standard deviation, along with the low coefficient of variation (CV) of the group of unreinforced dentures shows the repeatability of the results and the reliability of the machine. The high standard deviation and coefficient of variation of reinforced dentures was expected, since a high variation of results is usually recorded in fibre reinforcement cases. This research confirmed the view that the crack during denture fracture initiates in the anterior palatal area and propagates to the posterior.展开更多
The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A...The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A total of 36 specimens were manufactured (18 of Ni-Cr alloy and 18 of Co-Cr alloy). The specimens were then divided into 3 subgroups (6 specimens each): control;argon-welded;and non-Argon welded. The specimens were cut, laser welded, radiographed and finally tested under tensile strength testing, followed by examination using Scanning Electron Microscopy. The tensile strength of welded specimens was lower than the strength of non-welded specimens, however this difference was not found to be statistically significant. The material factor (Co-Cr alloy or Ni-Cr alloy) has a statistically significant effect on the tensile strength, while the presence or not of the inert gas, as well as the combination of the two factors do not have a statistically significant effect. The laser welding process applied in daily practice (separation of specimen, formation of two cones in contact, aggregation of two cones, filling of the remaining gap by welding) is considered satisfactory in terms of weld strength. The factor of the material, as an independent factor, affects the tensile strength to a statistically significant degree, in contrast to the factor of the presence of inert gas which does not affect to a statistically significant degree.展开更多
The most commonly used material for constructing complete dentures is polymethyl methacrylate (PMMA). However, the strength characteristics of PMMA, such as impact strength and fatigue strength, are poor, and fracturi...The most commonly used material for constructing complete dentures is polymethyl methacrylate (PMMA). However, the strength characteristics of PMMA, such as impact strength and fatigue strength, are poor, and fracturing of PMMA dentures is a common problem in prosthodontic practice. Reinforcing PMMA with various materials, such as carbon fibers, glass fibers (fiberglass), and ultrahigh modulus polyethylene fibers, has been suggested to strengthen the denture-base material. A common problem encountered when packing the resin on these specimens is fiber slippage beyond the denture edges. The present study proposes an alternative method of incorporating fiber meshes into complete dentures, whereby a thin filament of self-polymerizing resin at the perimeter of the fiber mesh is produced, giving a clear and stable shape to the mesh that fits the upper jaw cast. During placement of the shaped mesh on the cast, a positive-negative relationship is created between the mesh and cast, which immobilizes the mesh during the incorporation process.展开更多
文摘In the present study, an aero pneumatic fatigue testing machine for complete dentures was designed, fabricated, and tested for the evaluation of the fatigue life of reinforced complete upper denture (CUD). On completion and testing, it was observed that the machine has the potential of generating reliable number of cyclic data. The machine’s performance was evaluated using test specimens of identical CUDs that were machined in conformity with standard procedures. The fatigue machine compressed the lower dental arch over the upper denture-specimen in centric occlusion, in the same way that the two masticatory muscles pull the lower jaw over the upper jaw during chewing. The incorporation of glass fibres into the CUD using a sandwich technique quadruples the lifespan of the denture (<em>P</em> = 0.004). The low standard deviation, along with the low coefficient of variation (CV) of the group of unreinforced dentures shows the repeatability of the results and the reliability of the machine. The high standard deviation and coefficient of variation of reinforced dentures was expected, since a high variation of results is usually recorded in fibre reinforcement cases. This research confirmed the view that the crack during denture fracture initiates in the anterior palatal area and propagates to the posterior.
文摘The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A total of 36 specimens were manufactured (18 of Ni-Cr alloy and 18 of Co-Cr alloy). The specimens were then divided into 3 subgroups (6 specimens each): control;argon-welded;and non-Argon welded. The specimens were cut, laser welded, radiographed and finally tested under tensile strength testing, followed by examination using Scanning Electron Microscopy. The tensile strength of welded specimens was lower than the strength of non-welded specimens, however this difference was not found to be statistically significant. The material factor (Co-Cr alloy or Ni-Cr alloy) has a statistically significant effect on the tensile strength, while the presence or not of the inert gas, as well as the combination of the two factors do not have a statistically significant effect. The laser welding process applied in daily practice (separation of specimen, formation of two cones in contact, aggregation of two cones, filling of the remaining gap by welding) is considered satisfactory in terms of weld strength. The factor of the material, as an independent factor, affects the tensile strength to a statistically significant degree, in contrast to the factor of the presence of inert gas which does not affect to a statistically significant degree.
文摘The most commonly used material for constructing complete dentures is polymethyl methacrylate (PMMA). However, the strength characteristics of PMMA, such as impact strength and fatigue strength, are poor, and fracturing of PMMA dentures is a common problem in prosthodontic practice. Reinforcing PMMA with various materials, such as carbon fibers, glass fibers (fiberglass), and ultrahigh modulus polyethylene fibers, has been suggested to strengthen the denture-base material. A common problem encountered when packing the resin on these specimens is fiber slippage beyond the denture edges. The present study proposes an alternative method of incorporating fiber meshes into complete dentures, whereby a thin filament of self-polymerizing resin at the perimeter of the fiber mesh is produced, giving a clear and stable shape to the mesh that fits the upper jaw cast. During placement of the shaped mesh on the cast, a positive-negative relationship is created between the mesh and cast, which immobilizes the mesh during the incorporation process.