The fabrication process of Sm2O3 doped CeO2 reinforced Ti3AlC2 nano composites including the nano particle dispersion process by a hetero-coagulation process was developed using in-situ synthesis and densification pro...The fabrication process of Sm2O3 doped CeO2 reinforced Ti3AlC2 nano composites including the nano particle dispersion process by a hetero-coagulation process was developed using in-situ synthesis and densification process of Ti3AlC2. The effects of Sm2O2 doped CeO2 nano particles on mechanical properties of Ti3AlC2 were investigated. It was found that the presence of 20SDC nano particles in Ti3AlC2 was very effective to improve the mechanical properties of Ti3AlC2 without spoiling the unique characteristics of Ti3AlC2temary carbide.展开更多
We investigated the structural and magnetic properties of Sm（Co0.7Fe0.1Ni0.12Zr0.04B0.04）7.5 melt spun ribbons. Samples were arc melted then melt spun at 37 m/s up to 55 m/s to obtain ribbon for powdering. Annealing...We investigated the structural and magnetic properties of Sm（Co0.7Fe0.1Ni0.12Zr0.04B0.04）7.5 melt spun ribbons. Samples were arc melted then melt spun at 37 m/s up to 55 m/s to obtain ribbon for powdering. Annealing was performed in argon atmosphere for 30- 75 min at 600-870 oC. In as-spun ribbons the hexagonal SmCo7 （TbCu7-type of structure） of crystal structure was determined from x-ray diffraction patterns, while fcc-Co has been identified as a secondary phase. After annealing, the 1：7 phase of the as-spun ribbons transformed into 2：17 and 1：5 phases. X-ray patterns for as-milled powders exhibited very broad peaks making it difficult to identify a precise structure but repre-sented the 1：7 structure after annealing at low temperature （650 oC）. TEM analysis showed a homogeneous nanocrystalline microstructure with average grain size of 30-80 nm. Coercivity values of 15-27 kOe were obtained from hysteresis loops traced up to a field of 5 T. The co-ercivity decreased as temperature increases, but it maintained values higher than 5 kOe at 380 oC. The maximum energy product at room temperature increased, as high as 7.2 MGOe, for melt-spun isotropic ribbons produced at higher wheel speeds. Anisotropic ribbons had a maximum energy product close to 12 MGOe.展开更多
文摘The fabrication process of Sm2O3 doped CeO2 reinforced Ti3AlC2 nano composites including the nano particle dispersion process by a hetero-coagulation process was developed using in-situ synthesis and densification process of Ti3AlC2. The effects of Sm2O2 doped CeO2 nano particles on mechanical properties of Ti3AlC2 were investigated. It was found that the presence of 20SDC nano particles in Ti3AlC2 was very effective to improve the mechanical properties of Ti3AlC2 without spoiling the unique characteristics of Ti3AlC2temary carbide.
基金Project supported by HITEMAG European project (G5RD-CT-2000-002B)DARPA Metamaterials program (ADA458377)
文摘We investigated the structural and magnetic properties of Sm（Co0.7Fe0.1Ni0.12Zr0.04B0.04）7.5 melt spun ribbons. Samples were arc melted then melt spun at 37 m/s up to 55 m/s to obtain ribbon for powdering. Annealing was performed in argon atmosphere for 30- 75 min at 600-870 oC. In as-spun ribbons the hexagonal SmCo7 （TbCu7-type of structure） of crystal structure was determined from x-ray diffraction patterns, while fcc-Co has been identified as a secondary phase. After annealing, the 1：7 phase of the as-spun ribbons transformed into 2：17 and 1：5 phases. X-ray patterns for as-milled powders exhibited very broad peaks making it difficult to identify a precise structure but repre-sented the 1：7 structure after annealing at low temperature （650 oC）. TEM analysis showed a homogeneous nanocrystalline microstructure with average grain size of 30-80 nm. Coercivity values of 15-27 kOe were obtained from hysteresis loops traced up to a field of 5 T. The co-ercivity decreased as temperature increases, but it maintained values higher than 5 kOe at 380 oC. The maximum energy product at room temperature increased, as high as 7.2 MGOe, for melt-spun isotropic ribbons produced at higher wheel speeds. Anisotropic ribbons had a maximum energy product close to 12 MGOe.