Recycled PET (R-PET) is well known to exhibit brittle behavior in the presence of notches and indicated the low heat distortion temperature. In addition, it is hard to prevent some impurities such as cap or label of t...Recycled PET (R-PET) is well known to exhibit brittle behavior in the presence of notches and indicated the low heat distortion temperature. In addition, it is hard to prevent some impurities such as cap or label of the bottle that mixed into R-PET during the recycling process. In this paper, the effect of the amounts and kinds of compatibilizers on the morphological characteristics and mechanical performance of recycled poly(ethylene terephthalate) (R-PET) compounded with polyethylene (PE), polypropylene (PP), and polystyrene (PS) was investigated. From the results, with an increase in the glycidyl methacrylate modified PE (EGMA) additive contents, in the increment of the Izod impact strength of Composite-G was obtained. In addition, it was found that the miscibility of Composite-G was improved with increasing the amount of EGMA, which indicated from the result of SEM images.展开更多
Cu-Zn-S (CZS) films were deposited by the spray pyrolysis method. As-deposited CZS film showed a low crystallinity. The resistivity of CZS film with Cu/(Cu+Zn) ratio of 50% is around 10-2Ω﹒cm. The CZS film elements ...Cu-Zn-S (CZS) films were deposited by the spray pyrolysis method. As-deposited CZS film showed a low crystallinity. The resistivity of CZS film with Cu/(Cu+Zn) ratio of 50% is around 10-2Ω﹒cm. The CZS film elements using spray Cu-Zn (=1:1) solution with thiourea was confirmed as? Cu:Zn:Sn=2:2:3 by ICP-MS and EDX. The band gap of CZS films was varied in the range of 1.8 - 3.5 ev when the? Cu/(Cu+Zn)ratio was increased from 0 to 67%;CZS film with Cu/(Cu+Zn)ratio of 50 % showed an wide band gap of 2 eV. The photovoltaic characteristics were confirmed with cell structure of . The best cell was observed at the CZS films with Cu/(Cu+Zn)ratio of 50%;these cells depicted a conversion efficiency of 1.7%.展开更多
Polymethylmethacrylate (PMMA) is highly regarded for its transparency, and is used in such products as cameras and Video Tape Recorders as plastic lenses to take advantage of its excellent optical properties. Also, it...Polymethylmethacrylate (PMMA) is highly regarded for its transparency, and is used in such products as cameras and Video Tape Recorders as plastic lenses to take advantage of its excellent optical properties. Also, it is used in numerous other industrial fields like automobile lamp lenses, billboards, and lighting equipment. The phenomenon of environmental stress cracking is known to occur in PMMA due to ethanol, and there are cases when this may become a factor which causes damage of molded products. In the present paper, upon close observation by using the method of chemiluminescence in order to elucidate the mechanism by which this environmental stress cracking occurs, we report that we are able to capture the formation of a radical at the moment of cracking.展开更多
文摘Recycled PET (R-PET) is well known to exhibit brittle behavior in the presence of notches and indicated the low heat distortion temperature. In addition, it is hard to prevent some impurities such as cap or label of the bottle that mixed into R-PET during the recycling process. In this paper, the effect of the amounts and kinds of compatibilizers on the morphological characteristics and mechanical performance of recycled poly(ethylene terephthalate) (R-PET) compounded with polyethylene (PE), polypropylene (PP), and polystyrene (PS) was investigated. From the results, with an increase in the glycidyl methacrylate modified PE (EGMA) additive contents, in the increment of the Izod impact strength of Composite-G was obtained. In addition, it was found that the miscibility of Composite-G was improved with increasing the amount of EGMA, which indicated from the result of SEM images.
文摘Cu-Zn-S (CZS) films were deposited by the spray pyrolysis method. As-deposited CZS film showed a low crystallinity. The resistivity of CZS film with Cu/(Cu+Zn) ratio of 50% is around 10-2Ω﹒cm. The CZS film elements using spray Cu-Zn (=1:1) solution with thiourea was confirmed as? Cu:Zn:Sn=2:2:3 by ICP-MS and EDX. The band gap of CZS films was varied in the range of 1.8 - 3.5 ev when the? Cu/(Cu+Zn)ratio was increased from 0 to 67%;CZS film with Cu/(Cu+Zn)ratio of 50 % showed an wide band gap of 2 eV. The photovoltaic characteristics were confirmed with cell structure of . The best cell was observed at the CZS films with Cu/(Cu+Zn)ratio of 50%;these cells depicted a conversion efficiency of 1.7%.
文摘Polymethylmethacrylate (PMMA) is highly regarded for its transparency, and is used in such products as cameras and Video Tape Recorders as plastic lenses to take advantage of its excellent optical properties. Also, it is used in numerous other industrial fields like automobile lamp lenses, billboards, and lighting equipment. The phenomenon of environmental stress cracking is known to occur in PMMA due to ethanol, and there are cases when this may become a factor which causes damage of molded products. In the present paper, upon close observation by using the method of chemiluminescence in order to elucidate the mechanism by which this environmental stress cracking occurs, we report that we are able to capture the formation of a radical at the moment of cracking.