The poor stability of halide perovskite nanocrystals(NCs)has severely hindered future practical application.Herein,we proposed a facile and effective ligand modification route to synthesize stable CsPbBr_(3) nanocryst...The poor stability of halide perovskite nanocrystals(NCs)has severely hindered future practical application.Herein,we proposed a facile and effective ligand modification route to synthesize stable CsPbBr_(3) nanocrystals by introducing a double-terminal ligand,namely 4,4'-Azobis(4-cyanovalericacid)(CA),to replace the conventional oleic acid(OA)ligand at room temperature.The as-synthesized CsPbBr_(3)-CA not only possesses high photoluminescence quantum yield(72%)related to the reduced trap defects,but also shows significantly improved stability exposure to water,ethanol,light,and/or heat benefiting from the CA ligand anchored to NC surfaces tightly.The photoluminescence intensity of CsPbBr_(3)-CA maintains about 80%and 75%of its initial emission intensity after immersed in water or ethanol for 360 min,respectively,whereas that of the CsPbBr_(3)-OA was quenched completely within a few minutes.Moreover,an all-inorganic white light-emitting diode(LED)covered 126%National Television System Committee(NTSC)standard and 92%Rec.2020 standard was fabricated by combining the green CsPbBr_(3)-CA and commercial red-emitting K2SiF6:Mn4+(KSF)phosphors onto a blue LED chip.Thus,the presented work initiates the development of the room temperature preparation of high quality CsPbBr_(3) and shows prospect for next-generation displays.展开更多
基金supported by the National Natural Science Foundation of China(Nos.61775060,61275100,61761136006,61790583,and 61874043).
文摘The poor stability of halide perovskite nanocrystals(NCs)has severely hindered future practical application.Herein,we proposed a facile and effective ligand modification route to synthesize stable CsPbBr_(3) nanocrystals by introducing a double-terminal ligand,namely 4,4'-Azobis(4-cyanovalericacid)(CA),to replace the conventional oleic acid(OA)ligand at room temperature.The as-synthesized CsPbBr_(3)-CA not only possesses high photoluminescence quantum yield(72%)related to the reduced trap defects,but also shows significantly improved stability exposure to water,ethanol,light,and/or heat benefiting from the CA ligand anchored to NC surfaces tightly.The photoluminescence intensity of CsPbBr_(3)-CA maintains about 80%and 75%of its initial emission intensity after immersed in water or ethanol for 360 min,respectively,whereas that of the CsPbBr_(3)-OA was quenched completely within a few minutes.Moreover,an all-inorganic white light-emitting diode(LED)covered 126%National Television System Committee(NTSC)standard and 92%Rec.2020 standard was fabricated by combining the green CsPbBr_(3)-CA and commercial red-emitting K2SiF6:Mn4+(KSF)phosphors onto a blue LED chip.Thus,the presented work initiates the development of the room temperature preparation of high quality CsPbBr_(3) and shows prospect for next-generation displays.