Static and Dynamic Leaching Experiments of Heavy Metals from Fly Ash-Based Geopolymers

The feasibility of high calcium fly ash （CFA）-based geopolymers to fix heavy metals were studied. The CFA-based geopolymers were prepared from CFA, flue gas desulfurization gypsum （FGDG）, and water treatment residual （WTR）. The static leaching showed that heavy metals concentrations from CFA- based geopolymers were lower than their maximum concentration limits according to the U.S. environmental protection law. And the encapsulated and fixed ratios of heavy metals by the CFA-based geopolymers were 96.02%-99.88%. The dynamic real-time leaching experiment showed that concentration of Pb （II） was less than 1.μg / L, Cr （VI） less than 3.25 mg / L, while Hg （II） less than 4.0 μg / L. Additionally, dynamic accumulated leaching concentrations were increased at the beginning of leaching process then kept stable. During the dynamic leaching process, heavy metals migrated and accumulated in an area near to the solid-solution interface. When small part of heavy metals in ＂the accumulated area＂ breached through the threshold value of physical encapsulation and chemical fixation they migrated into solution. The dynamic leaching ratios and effective diffusion coefficients of heavy metals from CFA-based geopolymer were very low and the long-term security of heavy metals in CFA-based geopolymer was safe.

Influence of Thermally Treated Flue Gas Desulfurization(FGD) Gypsum on Performance of the Slag Powder Concrete

The feasibility of flue gas desulphurization （FGD） as concrete admixture was studied. A combined concrete admixture of the thermally-treated FGD gypsum and slag powder was explored. The FGD gypsum was roasted at 200℃ for 60 min and then mixed with the slag powder to form FGD gypsum-slag powder combined admixture in which the SO3 content was 3.5wt%. Cement was partially and equivalently replaced by slag powder alone or FGD gypsum-slag powder, at concentration of 25wt%, 40wt%, and 50wt%, respectively. The setting times, hydration products, total porosity and pore size distributions of the paste were determined. The compressive strength and drying shrinkage of cement mortar and concrete were also tested. The experimental results show that, in the presence of FGD gypsum, the setting times are much slower than those of pastes in the absence of FGD gypsum. The combination of FGD gypsum and slag powder provides synergistic benefits above that of slag powder alone. The addition of FGD gypsum provides benefit by promoting ettringite formation and forms a compact microstructure, increasing the compressive strength and reduces the drying shrinkage of cement mortar and concrete.

Effects of Steel Slag Powder on Workability and Durability of Concrete

The workability and durability of a type of sustainable concrete made with steel slag powder were investigated. The hydrated products of cement paste with ground granulated blast furnace slag（GGBFS） alone or with a combined admixture of GGBFS-steel slag powder were investigated by X-ray diffraction（XRD）. Furthermore, the mechanism of chemically activated steel slag powder was also studied. The experimental results showed that when steel slag powder was added to concrete, the slumps through the same time were lower. The initial and fi nal setting times were slightly retarded. The dry shrinkages were lower, and the abrasion resistance was better. The chemically activated steel slag powder could improve compressive strengths, resistance to chloride permeation and water permeation, as well as carbonization resistance. XRD patterns indicated that the activators enhanced the formation of calcium silicate hydrate（C-S-H） gel and ettringite（AFt）. This research contributes to sustainable disposal of wastes and has the potential to provide several important environmental benefi ts.

Rapid Hydrogen Transportation Along Grain Boundary in Nickel

The permeability and diffusivity of hydrogen in directionally solidified polycrystalline and single crystal nickel foils were measured by gas permeation method.The results showed that both hydrogen diffusivity and permeability were higher in directionally solidified nickel specimen than those in single crystal one at the temperature ranging from 300 to480 °C,and confirmed the existence of short-circuit diffusion along the grain boundaries（GBs） in the directionally solidified nickel.The results suggested that the rapid diffusion along GBs was more obviously characterized in terms of higher permeability rather than higher diffusivity.The contribution of grain boundary to hydrogen transportation was represented by the differences of diffusivity（and permeability） in single crystal nickel and directionally solidified nickel.By modifying the Fick＇s first diffusion law and counting the grain boundary density,the hydrogen diffusivity and permeability of rapid diffusion along GBs were calculated.The results suggested both the diffusivity and permeability fit the Arrhenius relationship well at different temperature.