Recovery of Tungsten Surface with Fiber-Form Nanostructure by Plasmas Exposures

One of the serious concerns for tungsten materials in fusion devices is the radiation defects caused by helium plasma irradiation since helium is a fusion product. The fiber-formed nanostructure is thought to have a possible weakness against the plasma heat flux on the plasma- facing component and also may destroy the reflectivity of optical mirrors. In this paper an inter- esting method for the recovery of such tungsten surfaces is shown. The recovery process depends on the grade and manufacturing process of tungsten materials.

TiO_2/浮石复合材料降解有机污染物亚甲基蓝的实验研究

利用天然浮石的孔隙结构和小比重等特点,以浮石为原料、TiOSO4为TiO2前驱体,采用水热合成法,在200 C、15 h条件下,制备出可漂浮的TiO2/浮石复合材料。采用10×10 mol/L严甲基蓝水溶液,在紫外光下进行光催化实验。并用紫外可见分光光度计检测亚甲基蓝浓度变化。实验结果表明,TiO2/浮石复合材料能够降解亚甲基蓝。该材料的孔隙结构对亚甲基蓝有聚集怍用,促进了负载的TiO2的光催化性能的发挥。因为成本低廉, 性能优越,TiO2/浮石复合材料在有机污染物治理方面具有很大的应用潜力。

用于空气中水蒸气吸-脱附的微孔泡沫炭制备研究(英文)

以蜜胺泡沫体为模板,采用氟化聚酰亚胺制备了微孔泡沫炭。测定了其对环境中水气的吸附/脱附行为,发现:泡沫炭在空气中400℃活化1h,可以提高其对水气的吸附能力。与活化前相比,对水气的吸附量几乎高达3倍,尽管其微孔容积仅增大了1.5倍。对环境水气中的可逆吸附率与微孔容积成线性关系,微孔容积为0.75mL/g的泡沫炭,其水气吸附率约为质量分数40%。

由柏木制备纳米孔结构炭材料Ⅰ. 制备与孔结构(英文)

柏木条经过热蒸气处理,成功地制备了纳米孔炭,无需另行活化,比表面积就可达1000m2/g以上。如果在800℃～870℃炭化,柏木炭外表面积可达400m2/g以上,与同样温度在氩气中炭化得到的柏木炭相比,后者微孔面积仅为30m2/g～40m2/g。在900℃以上炭化得到的柏木炭,微孔表面积高达800m2/g以上,外表面积约为150m2/g。柏木炭的孔结构可以通过调节过热蒸气的温度得到控制。

由柏木制备纳米孔结构炭材料 Ⅱ.电双层电容器中的应用(英文)

通过过热蒸气活化法制备的柏木炭中含有大量的中孔,可用于制备以1mol/L硫酸为电解液的双电层电容器(EDLCs)。在50mA/g电流密度下,柏木炭的质量比电容(C50)为190F/g;在1000mA/g电流密度下,其质量比电容(C1000)为140F/g。按C1000/C50定义的性能倍率约为0.72。测得的高电容量可归因于微孔和大孔所造成表面的贡献。以简易浸泡法负载少量NiO粒子后,柏木炭的质量比电容可以提高约13%,体积比电容提高约27%,而其性能倍率保持不变。

日本预拌混凝土的质量控制

为保证预拌混凝土的质量,在日本采取了三种措施,一是根据日本工业标准对预拌混凝土搅拌站进行监测;二是除了常规检测外,还要现场测试新拌混凝土中氯离子和水分的含量,因为这两项指标可能会对混凝土结构的强度和耐久性产生影响;三是建立全国统一的预拌混凝土质量控制的核查系统。本文对这三种保证预拌混凝土质量的手段进行简单的介绍。