This study aims at investigating the impact of ionic liquid extraction on lignin structure by studying the mechanism of lignin depolymerization in 1-ethyl-3-methylimidazolium acetate EMIM[OAc]) and comparing it with t...This study aims at investigating the impact of ionic liquid extraction on lignin structure by studying the mechanism of lignin depolymerization in 1-ethyl-3-methylimidazolium acetate EMIM[OAc]) and comparing it with that of organosolv and milled wood methods. Ionic liquid mediated lignin (ILL) using EMIM[OAc]), ethanol organosolv lignin (EOL) and milled wood lignin (MWL) were isolated from Typha capensis (TC) and subjected to several analytical characterizations. Experimental data shows that ILL exhibited a relatively lower degree of condensation, lower aromatic C-C structures and a higher aliphatic OH with values of 0.42/Ar, 1.94/Ar and 1.33/Ar moieties compared with EOL values of 0.92/Ar, 2.22/Ar and 0.51/Ar moieties respectively. The ILL was depolymerized under mild conditions giving relatively higher β-aryl ether linkages content, higher molecular mass, and exhibited closer structures and reactivity to native lignin than EOL. These insights on TC lignin depolymerization in EMIM[OAc]) acetate may contribute to better value-addition of lignocellulosic biomass.展开更多
In this work, activated carbons (ACs) prepared by chemical activation of garcinia cola nut shell impregnated with H3PO4 (CBH2/1) and KOH (CBK1/1) were used to study the kinetics, equilibrium and thermodynamics of the ...In this work, activated carbons (ACs) prepared by chemical activation of garcinia cola nut shell impregnated with H3PO4 (CBH2/1) and KOH (CBK1/1) were used to study the kinetics, equilibrium and thermodynamics of the adsorption of thymol blue from aqueous solution. The characterization of ACs showed the BET measurements gave surface area and total pore volume respectively of 328.407 m2·g-1 and 0.1032 cm3·g-1 for CBH2/1 and 25.962 m2·g-1 and 0.03 cm3·g-1for CBK1/1;elemental analysis showed a high percentage of carbon in both ACs. Influence of parameters such as initial pH, contact time, adsorbent mass, initial concentration, ionic strength and the effect of temperature on the removal of thymol blue from aqueous solution were studied in batch mode. The studies showed that equilibrium adsorption was attained after 60 minutes for the two ACs, adsorption capacity increased with increasing concentration of thymol blue, and maximum adsorption capacity was obtained at an acidic environment with pH 2. Avrami’s non-linear kinetic expression was the best suited for describing the adsorption kinetics of thymol blue onto ACs, while equilibrium data showed that the three-parameter isotherms better described the adsorption process since R2 > 0.96, and the error functions were lowest for all of them. Maximum adsorption capacity values obtained using the three-parameter Fritz-Schlunder equation were 32.147 mg·g-1 for CBH2/1 and 67.494 mg·g-1 for CBK1/1. The values of the model parameters g and mFS respectively, obtained using the Redlich-Peterson and Fritz-Schlunder III isotherms below 1, showed that the adsorption of thymol blue by the ACs occurred on heterogeneous surfaces. Thermodynamic analyses of the data of the adsorption of thymol blue onto ACs revealed that the adsorption process was temperature dependent, endothermic and spontaneous.展开更多
文摘This study aims at investigating the impact of ionic liquid extraction on lignin structure by studying the mechanism of lignin depolymerization in 1-ethyl-3-methylimidazolium acetate EMIM[OAc]) and comparing it with that of organosolv and milled wood methods. Ionic liquid mediated lignin (ILL) using EMIM[OAc]), ethanol organosolv lignin (EOL) and milled wood lignin (MWL) were isolated from Typha capensis (TC) and subjected to several analytical characterizations. Experimental data shows that ILL exhibited a relatively lower degree of condensation, lower aromatic C-C structures and a higher aliphatic OH with values of 0.42/Ar, 1.94/Ar and 1.33/Ar moieties compared with EOL values of 0.92/Ar, 2.22/Ar and 0.51/Ar moieties respectively. The ILL was depolymerized under mild conditions giving relatively higher β-aryl ether linkages content, higher molecular mass, and exhibited closer structures and reactivity to native lignin than EOL. These insights on TC lignin depolymerization in EMIM[OAc]) acetate may contribute to better value-addition of lignocellulosic biomass.
文摘In this work, activated carbons (ACs) prepared by chemical activation of garcinia cola nut shell impregnated with H3PO4 (CBH2/1) and KOH (CBK1/1) were used to study the kinetics, equilibrium and thermodynamics of the adsorption of thymol blue from aqueous solution. The characterization of ACs showed the BET measurements gave surface area and total pore volume respectively of 328.407 m2·g-1 and 0.1032 cm3·g-1 for CBH2/1 and 25.962 m2·g-1 and 0.03 cm3·g-1for CBK1/1;elemental analysis showed a high percentage of carbon in both ACs. Influence of parameters such as initial pH, contact time, adsorbent mass, initial concentration, ionic strength and the effect of temperature on the removal of thymol blue from aqueous solution were studied in batch mode. The studies showed that equilibrium adsorption was attained after 60 minutes for the two ACs, adsorption capacity increased with increasing concentration of thymol blue, and maximum adsorption capacity was obtained at an acidic environment with pH 2. Avrami’s non-linear kinetic expression was the best suited for describing the adsorption kinetics of thymol blue onto ACs, while equilibrium data showed that the three-parameter isotherms better described the adsorption process since R2 > 0.96, and the error functions were lowest for all of them. Maximum adsorption capacity values obtained using the three-parameter Fritz-Schlunder equation were 32.147 mg·g-1 for CBH2/1 and 67.494 mg·g-1 for CBK1/1. The values of the model parameters g and mFS respectively, obtained using the Redlich-Peterson and Fritz-Schlunder III isotherms below 1, showed that the adsorption of thymol blue by the ACs occurred on heterogeneous surfaces. Thermodynamic analyses of the data of the adsorption of thymol blue onto ACs revealed that the adsorption process was temperature dependent, endothermic and spontaneous.