s Ba_4Zn_zCo_(2-z)Fe_(36)O_(60) hexaferrites with Z = 2.0, 1.5, 1.0, 0.5, and0.0 were prepared by a citrate Sol-gel process. The complex dielectric constant and complexpermeability of hexaferrite-paraffin wax composit...s Ba_4Zn_zCo_(2-z)Fe_(36)O_(60) hexaferrites with Z = 2.0, 1.5, 1.0, 0.5, and0.0 were prepared by a citrate Sol-gel process. The complex dielectric constant and complexpermeability of hexaferrite-paraffin wax composites were measured in the range from 0.1 to 6.0 GHz.Measured results showed that both the complex dielectric constant and the dielectric loss exhibitedno significant change as the measuring frequency increasing except for the sample with Z = 0.0. Thereal part of permeability decreased with increasing frequency for all samples in the whole measuringfrequency range, and the natural resonance phenomena were observed in all μ″ spectrum but Co_2U.The results also indicate that the content of zinc closely affects the microwave properties ofBa_4Zn_zCo_(2-z)Fe_(36)O_(60) ferrites, and the greater the zinc content, the lower the naturalresonance frequency is.展开更多
BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics with Z=0.0, 0.5, 0.8 and 1.1 were prepared at temperature 1200℃ for 5h by citrate sol-gel process. The complex dielectric constant and complex permeability of Ba...BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics with Z=0.0, 0.5, 0.8 and 1.1 were prepared at temperature 1200℃ for 5h by citrate sol-gel process. The complex dielectric constant and complex permeability of BaZnzCo2-zFe16 O27/SiO2-paraffin wax composites had been measured. Both the complex dielectric constant and dielectric loss exhibit almost no variation with frequency in 0.1-6.0GHz. The real part of permeability decreases with increasing frequency for all samples, and the imaginary part of permeability exhibits a clear resonance peak at 1.44GHz for Co2 W/SiO2, 1.32GHz for Zn0.5Co1.5 W/SiO2, 1.20GHz for Zn0.8Co1.2W/SiO2, and 1.08GHz for Zn1.1 Co0.9 W/SiO2. It is also showed that the content of zinc has a close effect on the magnetic properties of BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics, the greater the zinc content, the higher the values of imaginary part of permeability and magnetic loss.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No. 59995320.4).
文摘s Ba_4Zn_zCo_(2-z)Fe_(36)O_(60) hexaferrites with Z = 2.0, 1.5, 1.0, 0.5, and0.0 were prepared by a citrate Sol-gel process. The complex dielectric constant and complexpermeability of hexaferrite-paraffin wax composites were measured in the range from 0.1 to 6.0 GHz.Measured results showed that both the complex dielectric constant and the dielectric loss exhibitedno significant change as the measuring frequency increasing except for the sample with Z = 0.0. Thereal part of permeability decreased with increasing frequency for all samples in the whole measuringfrequency range, and the natural resonance phenomena were observed in all μ″ spectrum but Co_2U.The results also indicate that the content of zinc closely affects the microwave properties ofBa_4Zn_zCo_(2-z)Fe_(36)O_(60) ferrites, and the greater the zinc content, the lower the naturalresonance frequency is.
基金supported by the National Natural Science Foundation of China (No.59995320.4).
文摘BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics with Z=0.0, 0.5, 0.8 and 1.1 were prepared at temperature 1200℃ for 5h by citrate sol-gel process. The complex dielectric constant and complex permeability of BaZnzCo2-zFe16 O27/SiO2-paraffin wax composites had been measured. Both the complex dielectric constant and dielectric loss exhibit almost no variation with frequency in 0.1-6.0GHz. The real part of permeability decreases with increasing frequency for all samples, and the imaginary part of permeability exhibits a clear resonance peak at 1.44GHz for Co2 W/SiO2, 1.32GHz for Zn0.5Co1.5 W/SiO2, 1.20GHz for Zn0.8Co1.2W/SiO2, and 1.08GHz for Zn1.1 Co0.9 W/SiO2. It is also showed that the content of zinc has a close effect on the magnetic properties of BaZnzCo2-zFe16O27/SiO2 microcrystalline glass ceramics, the greater the zinc content, the higher the values of imaginary part of permeability and magnetic loss.