The Ni-Cr alloy electrodepositing technology on iron substrate in the chlorid-sulfate solution and the impacts of main processing parameters on coating composition were studied. The optimal Ni-Cr alloy electrodepositi...The Ni-Cr alloy electrodepositing technology on iron substrate in the chlorid-sulfate solution and the impacts of main processing parameters on coating composition were studied. The optimal Ni-Cr alloy electrodepositing conditions are that the cathode current density is 16 A/dm^2,the plating solution temperature is 30℃ and the pH value is 2.5. The bright, compact coating gained under the optimal conditions has good cohesion and 24.1% Cr content. The results show that the coating is composed of crystalline, the average grain size is 82 nm and the higher the Cr content of coating, the larger the rigidity, and the higher the corrosion resistance. The rigidity of coating reaches 78.6(HR30T) and the passivation area broadens to 1.4 V when the Cr content of coating is 24.1%.展开更多
The assembling of a coating of time-resolved fluorescent chelator BSPDA （ abbreviated for 4, 7-bis （ sulfhydrylphenyl）-1, 10-phenanthroline-2, 9-dicarboxylic acid） onto a nano-gold layer was demonstrated. First, B...The assembling of a coating of time-resolved fluorescent chelator BSPDA （ abbreviated for 4, 7-bis （ sulfhydrylphenyl）-1, 10-phenanthroline-2, 9-dicarboxylic acid） onto a nano-gold layer was demonstrated. First, BSPDA was synthesized by simple procedures, and then an approach was developed to immobilize BSPDA onto the nano-gold layer deposited on a silane modified glass substrate, whereby europium ion （Ⅲ, Eu^3＋ ） was captured and released owing to the interactive process of complexation and dissociation between BSPDA functionalized coating and Eu^3＋ solution. The fluorescence spectra and related lifetimes were determined. Also, the BSPDA functionalized coating＇s specific complexation with Eu^3＋ on the BSPDA assembly layer and the nonspecific adsorption of Eu^3＋ on the nano-gold layer were compared. These results allowed a selective complexation of Eu^3＋ by assembling a BSPDA chelating layer on the nano-gold layer; thus, a tunable time-resolved fluorescent layer was covalently attached, The results of the nanoparticle assembling and probing （or labeling） processes to specific bio-systems were very interesting and had significant implications to time-resolved-fluorescence-based detection on biosensor surfaces such as DNA chip and to arrayed light display devices.展开更多
基金Project (59674025) supported by the National Natural Science Foundation of China
文摘The Ni-Cr alloy electrodepositing technology on iron substrate in the chlorid-sulfate solution and the impacts of main processing parameters on coating composition were studied. The optimal Ni-Cr alloy electrodepositing conditions are that the cathode current density is 16 A/dm^2,the plating solution temperature is 30℃ and the pH value is 2.5. The bright, compact coating gained under the optimal conditions has good cohesion and 24.1% Cr content. The results show that the coating is composed of crystalline, the average grain size is 82 nm and the higher the Cr content of coating, the larger the rigidity, and the higher the corrosion resistance. The rigidity of coating reaches 78.6(HR30T) and the passivation area broadens to 1.4 V when the Cr content of coating is 24.1%.
基金Project supported by the National Natural Science Foundation of China (20505020) the Natural Science Foundation ofGuangdong Province (06300086) +2 种基金 China Postdoctoral Science Foundation (20060390202) Scientific Research Fund ofHunan Provincial Education Department (05C508) Skeleton Youth Faculty Programof Hunan Higher Educational School
文摘The assembling of a coating of time-resolved fluorescent chelator BSPDA （ abbreviated for 4, 7-bis （ sulfhydrylphenyl）-1, 10-phenanthroline-2, 9-dicarboxylic acid） onto a nano-gold layer was demonstrated. First, BSPDA was synthesized by simple procedures, and then an approach was developed to immobilize BSPDA onto the nano-gold layer deposited on a silane modified glass substrate, whereby europium ion （Ⅲ, Eu^3＋ ） was captured and released owing to the interactive process of complexation and dissociation between BSPDA functionalized coating and Eu^3＋ solution. The fluorescence spectra and related lifetimes were determined. Also, the BSPDA functionalized coating＇s specific complexation with Eu^3＋ on the BSPDA assembly layer and the nonspecific adsorption of Eu^3＋ on the nano-gold layer were compared. These results allowed a selective complexation of Eu^3＋ by assembling a BSPDA chelating layer on the nano-gold layer; thus, a tunable time-resolved fluorescent layer was covalently attached, The results of the nanoparticle assembling and probing （or labeling） processes to specific bio-systems were very interesting and had significant implications to time-resolved-fluorescence-based detection on biosensor surfaces such as DNA chip and to arrayed light display devices.