An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractorie...An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractories by ZnO-containing fayalite slag, the corrosion behavior of magnesia-chromite refractories in lead smelting slags with different funnel glass additions from 0wt% to 40wt% was tested. Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) was used to acquire the microstructural information of the worn refractory samples. Experimental results showed that the corrosion of magnesia-chromite refractory consisted predominantly of the dissolution of MgO into slag. ZnO and FeO reacted with periclase and chromite to form (Zn,Fe,Mg)O solid solution and (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel, respectively. With the addition of funnel glass, the solubility of MgO increased whereas ZnO levels remained stable, thereby resulting in a reduced Mg content and an elevated Zn and Fe content in the (Zn,Fe,Mg)O solid solution and the (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel. Considering the stability of the (Zn,Fe,Mg)O solid solution layer and the penetration depth of the slag, the optimal funnel glass addition for lead smelting was found to be 20wt%.展开更多
基金financially supported by the National Key R&D Program of China (No. 2018YFC1902004)the National Natural Science Foundation of China (No. U1608254)+1 种基金the Project for Guangdong Collaborative Innovation and Platform Environment Building (No. 2017B090904035)the Special Project for Key Laboratory of Guangdong Science and Technology Department, China (No. 2017B030314046)
文摘An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractories by ZnO-containing fayalite slag, the corrosion behavior of magnesia-chromite refractories in lead smelting slags with different funnel glass additions from 0wt% to 40wt% was tested. Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) was used to acquire the microstructural information of the worn refractory samples. Experimental results showed that the corrosion of magnesia-chromite refractory consisted predominantly of the dissolution of MgO into slag. ZnO and FeO reacted with periclase and chromite to form (Zn,Fe,Mg)O solid solution and (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel, respectively. With the addition of funnel glass, the solubility of MgO increased whereas ZnO levels remained stable, thereby resulting in a reduced Mg content and an elevated Zn and Fe content in the (Zn,Fe,Mg)O solid solution and the (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel. Considering the stability of the (Zn,Fe,Mg)O solid solution layer and the penetration depth of the slag, the optimal funnel glass addition for lead smelting was found to be 20wt%.