In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses o...In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses of the composite cladding layers. Iron liquid–solid-phase zones were formed at copper/steel and iron interfaces because of the melting of the steel substrate and iron. Iron concentrated in the copper cladding layer was observed to exhibit belt, globule, and dendrite morphologies. The appearance of iron-rich globules indicated the occurrence of liquid phase separation（LPS） prior to solidification, and iron-rich dendrites crystallized without the occurrence of LPS. The maximum microhardness of the iron/steel interface was lower than that of the copper/steel interface because of the diffusion of elemental carbon. All samples fractured in the cladding layers. Because of a relatively lower strength of the copper layer, a short plateau region appeared when shear movement was from copper to iron.展开更多
In this paper,6 mm thick 2219-T6 aluminum alloy was joined by means of variable polarity tungsten-arc welding( VP-TIG) and the influence of gradient mismatches on VP-TIG joints is investigated. The average tensile str...In this paper,6 mm thick 2219-T6 aluminum alloy was joined by means of variable polarity tungsten-arc welding( VP-TIG) and the influence of gradient mismatches on VP-TIG joints is investigated. The average tensile strength of the joints reduces 32%,53% and 59%,when the mismatch of the joint was 0. 635 mm,1. 44 mm,1. 83 mm,respectively.Incomplete penetration,additional bending moment( Ma) and decrease of effective load region area are considered to explain this phenomenon. The fracture location of tensile specimens occurred at the weld zone( WZ) close to partial melt zone( PMZ),corresponding to a sharp decline of microhardness from PMZ to WZ. The original position of fracture is found at weld toe,where incomplete penetration forms due to the introduction of gradient mismatches.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51575132)
文摘In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses of the composite cladding layers. Iron liquid–solid-phase zones were formed at copper/steel and iron interfaces because of the melting of the steel substrate and iron. Iron concentrated in the copper cladding layer was observed to exhibit belt, globule, and dendrite morphologies. The appearance of iron-rich globules indicated the occurrence of liquid phase separation（LPS） prior to solidification, and iron-rich dendrites crystallized without the occurrence of LPS. The maximum microhardness of the iron/steel interface was lower than that of the copper/steel interface because of the diffusion of elemental carbon. All samples fractured in the cladding layers. Because of a relatively lower strength of the copper layer, a short plateau region appeared when shear movement was from copper to iron.
基金supported by the National Natural Science Foundation of China(No.50904020)the Fundamental Research Funds for the Central Universities(No.HIT.NSRIF.2012007)
文摘In this paper,6 mm thick 2219-T6 aluminum alloy was joined by means of variable polarity tungsten-arc welding( VP-TIG) and the influence of gradient mismatches on VP-TIG joints is investigated. The average tensile strength of the joints reduces 32%,53% and 59%,when the mismatch of the joint was 0. 635 mm,1. 44 mm,1. 83 mm,respectively.Incomplete penetration,additional bending moment( Ma) and decrease of effective load region area are considered to explain this phenomenon. The fracture location of tensile specimens occurred at the weld zone( WZ) close to partial melt zone( PMZ),corresponding to a sharp decline of microhardness from PMZ to WZ. The original position of fracture is found at weld toe,where incomplete penetration forms due to the introduction of gradient mismatches.