The thermodynamic stability of sulfate ions on synthesized calcium aluminosilicate hydrate（C-A-S-H） microstructure with different Ca/Si ratios and Al/Si ratios was investigated by XRD, SEM-EDS, 29 Si and 27 Al nucle...The thermodynamic stability of sulfate ions on synthesized calcium aluminosilicate hydrate（C-A-S-H） microstructure with different Ca/Si ratios and Al/Si ratios was investigated by XRD, SEM-EDS, 29 Si and 27 Al nuclear magnetic resonance（NMR） and thermodynamic modeling. The results indicate that sulfate attack leads to both decalcification and dealumination for C-A-S-H gels, and the amount of corrosion products（gypsum and ettringite） decreased gradually with decreasing Ca/Si ratios of C-A-S-H. Sulfate ions can also promote the polymerization degree of C-A-S-H gels, improving its resistance to sulfate attack. Moreover, the 4-coordination aluminum（Al[4]） in C-A-S-H, 5-coordination aluminum（Al[5]）, 6-ccordination aluminum（Al[6]） in TAH（third aluminum hydrate） and Al[6] in monosulfate or C-A-H（calcium aluminate hydrate） can be transformed into Al[6] in ettringite by sulfate attack. Furthermore, through thermodynamic calculation, the decrease of Ca/Si ratios and increase of Al/Si ratios can improve the thermodynamic stability of C-A-S-H gels under sulfate attack, which agrees well with the experiment results.展开更多
基金Funded by Anhui Key Laboratory of Advanced Building Materials,Anhui Jianzhu University(No.JZCL201602KF)Major State Basic Research Development Program of China(973 Program)(No.2015CB655101)+2 种基金State Key Laboratory of High Performance Civil Engineering Materials(No.2015CEM005)Natural Science Foundation of Hebei Province(No.E2016209283)Hubei Key Laboratory of Roadway Bridge and Structure Engineering(Wuhan University of Technology)(No.DQZDJJ201504)
文摘The thermodynamic stability of sulfate ions on synthesized calcium aluminosilicate hydrate（C-A-S-H） microstructure with different Ca/Si ratios and Al/Si ratios was investigated by XRD, SEM-EDS, 29 Si and 27 Al nuclear magnetic resonance（NMR） and thermodynamic modeling. The results indicate that sulfate attack leads to both decalcification and dealumination for C-A-S-H gels, and the amount of corrosion products（gypsum and ettringite） decreased gradually with decreasing Ca/Si ratios of C-A-S-H. Sulfate ions can also promote the polymerization degree of C-A-S-H gels, improving its resistance to sulfate attack. Moreover, the 4-coordination aluminum（Al[4]） in C-A-S-H, 5-coordination aluminum（Al[5]）, 6-ccordination aluminum（Al[6]） in TAH（third aluminum hydrate） and Al[6] in monosulfate or C-A-H（calcium aluminate hydrate） can be transformed into Al[6] in ettringite by sulfate attack. Furthermore, through thermodynamic calculation, the decrease of Ca/Si ratios and increase of Al/Si ratios can improve the thermodynamic stability of C-A-S-H gels under sulfate attack, which agrees well with the experiment results.