Lightweight and energy saving autoclaved aerated concrete(AAC) acting as a newbuilding material were prepared by using magnetite tailings from iron ore as main rawmaterials,and the purpose of comprehensive utilization...Lightweight and energy saving autoclaved aerated concrete(AAC) acting as a newbuilding material were prepared by using magnetite tailings from iron ore as main rawmaterials,and the purpose of comprehensive utilization of tailings resources was to improve their utilization efficiency.The effects of curing system on AAC product performance were discussed.The autoclave curing reaction kinetics was studied as well as the generated amount of hydration product trends over autoclave curing temperature and time were analyzed.The results indicated that the properties of AAC was in accordance with Chinese national standard the A3.5 B06 class of GB/T11968-2006 by prepared from magnetite tailing as the main rawmaterials.Meanwhile,autoclave curing process was controlled by the diffusion velocity through the products ' layers of reactants,and the apparent activation energy of autoclave curing process was 19.269 k J/mol.Compressive strength of aerated concrete is improved by mutual cementation between the appropriate amount of calcium silicate hydrate and tobermorite crystal.展开更多
基金National 12th Five-Year Science and Technology Planning Project,China(No.2013BAB03B03)
文摘Lightweight and energy saving autoclaved aerated concrete(AAC) acting as a newbuilding material were prepared by using magnetite tailings from iron ore as main rawmaterials,and the purpose of comprehensive utilization of tailings resources was to improve their utilization efficiency.The effects of curing system on AAC product performance were discussed.The autoclave curing reaction kinetics was studied as well as the generated amount of hydration product trends over autoclave curing temperature and time were analyzed.The results indicated that the properties of AAC was in accordance with Chinese national standard the A3.5 B06 class of GB/T11968-2006 by prepared from magnetite tailing as the main rawmaterials.Meanwhile,autoclave curing process was controlled by the diffusion velocity through the products ' layers of reactants,and the apparent activation energy of autoclave curing process was 19.269 k J/mol.Compressive strength of aerated concrete is improved by mutual cementation between the appropriate amount of calcium silicate hydrate and tobermorite crystal.